Method for manufacturing hollow gold ornaments

A processing method and jewelry technology, which is applied in clothing, jewelry, electrolysis process, etc., can solve the problems of difficult molding, waste of raw materials, and difficulty in restoring the original shape, and achieve the effects of excellent compressive strength, prolonging service life, and reducing repair costs

Inactive Publication Date: 2017-08-11
陈哲
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, most gold ornaments are manufactured by casting, oil pressure and other methods. It is difficult to obtain three-dimensional shapes for gold ornaments processed according to these aspects. Especially when processing hollow ornaments, it is not only diffic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0022] Example 1

[0023] A method for processing hollow gold jewelry, comprising the steps of:

[0024] (1), adopt tablet press machine to press gold bar into the gold flake that thickness is 0.2 millimeter;

[0025] (2), by the method for electrolysis, add potassium cyanide, the gold flake of step (1) is processed into potassium gold cyanide;

[0026] (3), by the method of centrifugal casting, make the low-temperature alloy of the shape of required jewelry;

[0027] (4) Put the low-temperature alloy in the electroforming cylinder, add potassium gold cyanide, and electroplate for 12 hours. After the weight required for the jewelry is electroplated on the outer layer of the alloy jewelry, open 2 small holes;

[0028] (5) Put the electroplated jewelry into the dealloying furnace, the heating temperature is 300°C, and heat until the low-temperature alloy flows out automatically through the small hole;

[0029] (6), put the jewelry that has been de-alloyed in step (5) into a c...

Example Embodiment

[0031] Example 2

[0032] A method for processing hollow gold jewelry, comprising the steps of:

[0033] (1), adopt tablet press machine to press gold bar into the gold flake that thickness is 0.2 millimeter;

[0034] (2), by the method for electrolysis, add potassium cyanide, the gold flake of step (1) is processed into potassium gold cyanide;

[0035] (3), by the method of centrifugal casting, make the low-temperature alloy of the shape of required jewelry;

[0036] (4) Put the low-temperature alloy in the electroforming cylinder, add potassium gold cyanide, and electroplate for 12 hours. After the weight required for the jewelry is electroplated on the outer layer of the alloy jewelry, open 2 small holes;

[0037] (5) Put the electroplated jewelry into the dealloying furnace, the heating temperature is 200°C, and heat until the low-temperature alloy flows out automatically through the small hole;

[0038] (6), put the jewelry that has been de-alloyed in step (5) into a c...

Example Embodiment

[0040] Example 3

[0041] A method for processing hollow gold jewelry, comprising the steps of:

[0042] (1), adopt tablet press machine to press gold bar into the gold flake that thickness is 0.2 millimeter;

[0043] (2), by the method for electrolysis, add potassium cyanide, the gold flake of step (1) is processed into potassium gold cyanide;

[0044] (3), by the method of centrifugal casting, make the low-temperature alloy of the shape of required jewelry;

[0045] (4) Put the low-temperature alloy in the electroforming cylinder, add potassium gold cyanide, and electroplate for 12 hours. After the weight required for the jewelry is electroplated on the outer layer of the alloy jewelry, open 2 small holes;

[0046] (5) Put the electroplated jewelry into the dealloying furnace, the heating temperature is 400°C, and heat until the low-temperature alloy flows out automatically through the small hole;

[0047] (6), put the jewelry that has been de-alloyed in step (5) into a c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for manufacturing hollow gold ornaments. Compared with traditional casting and oil pressing methods, the method has the advantages that the weight of gold ornaments manufactured with the method is reduced by two thirds, the size of manufactured gold ornaments is larger, and a three-dimensional shape can be obtained. Gold ornaments manufactured with the method have excellent compressive strength, can be assembled, worn and used conveniently and have a longer service life, and the gold ornament repair cost is reduced.

Description

technical field [0001] The invention relates to a processing method of jewelry, in particular to a processing method of hollow gold jewelry. Background technique [0002] Gold ornaments are one of the favorite ornaments of people. In order to increase the ornamental value of gold ornaments, it is necessary to process different angles on the surface of gold ornaments or process gold ornaments into different three-dimensional shapes, so that they can present the same color under different angles of light. Effect. [0003] At present, most gold ornaments are manufactured by casting, oil pressure and other methods. It is difficult to obtain three-dimensional shapes for gold ornaments processed according to these aspects. Especially when processing hollow ornaments, it is not only difficult to form, wastes raw materials, but also easy to deform. As a result, when the hollow gold jewelry is worn and used in daily life, it will be deformed under slight pressure, and it is difficul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Owner 陈哲
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap