Natural inorganic medical stone diatomite calcification system decoration wall material and preparation method and construction method thereof

A technology of stone diatomite and calcined diatomite, which is applied in the field of building decoration materials to achieve the effect of simple and thick texture and beautiful finished product effect

Inactive Publication Date: 2017-08-18
白山和一硅藻科技股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, although diatomite wall materials can be used to make certain textures on the surface of the wall to increase its decoration, there is still room for improvement in this regard.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Inorganic medical stone diatomite calcification system decorative wall material contains the following components by weight: 100-325 mesh medical stone powder: 10 weight parts; 250-500 mesh calcined diatomite: 15 weight parts; 325-600 mesh ash calcium powder 80-100 mesh calcium-based bentonite: 10 weight portions; 400-1000 mesh lithopone: 10 weight portions; 800-1000 mesh titanium dioxide: 10 weight portions; methyl cellulose: 0.3 weight portions; guar Bean gum: 0.6 parts by weight.

Embodiment 2

[0055]Inorganic medical stone diatomite calcification system decorative wall material contains the following components by weight: 100-325 mesh medical stone powder: 30 weight parts; 250-500 mesh calcined diatomite: 30 weight parts; 325-600 mesh ash calcium powder 80-100 mesh calcium bentonite: 48 weight portions; 400-1000 mesh lithopone: 3 weight portions; 800-1000 mesh titanium dioxide: 3 weight portions; methyl cellulose: 1.0 weight portions; guar Bean gum: 8 parts by weight.

Embodiment 3

[0057] Inorganic medical stone diatomite calcification system decorative wall material contains the following components by weight: 100-325 mesh medical stone powder: 15 weight parts; 250-500 mesh calcined diatomite: 28 weight parts; 325-600 mesh ash calcium powder 80-100 mesh calcium bentonite: 12 weight portions; 400-1000 mesh lithopone: 8 weight portions; 800-1000 mesh titanium dioxide: 7 weight portions; methyl cellulose: 0.6 weight portions; guar Bean gum: 4 parts by weight.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a natural inorganic medical stone diatomite calcification system decoration wall material and a preparation method and a construction method thereof, and belongs to the field of building decoration materials. The natural inorganic medical stone diatomite calcification system decoration wall material is prepared from the following components in parts by weight: 10 to 30 parts of 100 to 325 meshes of medical stone powder, 15 to 38 parts of 250 to 500 meshes of calcined diatomite, 28 to 48 parts of 325 to 600 meshes of ash calcium powder, 10 to 48 parts of 80 to 100 meshes of calcium bentonite, 3 to 10 parts of 400 to 100 meshes of lithopone, 3 to 10 parts of titanium dioxide, 0.3 to 1.0 part of methylcellulose and 0.6 to 8 parts of guar gum. By utilizing the natural inorganic medical stone diatomite calcification system decoration wall material and the construction method thereof provided by the invention, construction is carried out on indoor walls without adding any pigment, so that the advantages of the natural inorganic material of the product are guaranteed, the finished product is attractive in result, the texture is simple and decorous, the requirement of people on the decoration of the natural inorganic medical stone diatomite calcification system decoration wall is met, and meanwhile the material has extremely good effects in the aspect of removing hazardous substances such as formaldehyde and bacteria.

Description

technical field [0001] The invention relates to the field of building decoration materials, in particular to a medical stone diatomite wall material and its preparation and construction methods. Background technique [0002] Medical stone, medical stone belongs to volcanic rocks, which is quartz monzonite porphyry of intermediate acid igneous rocks. It has the effects of detoxifying and dispelling stagnation, removing putrefaction and promoting granulation, removing cold and dampness, nourishing the liver and strengthening the stomach, promoting blood circulation and removing blood stasis, diuretic fossils, and prolonging life. The mineral composition is mainly plagioclase (Na, Ca) [(Si, Al) 4 o 8 ], potassium feldspar (K, Na) [Al, Si 3 o 8 ], Quartz SiO 2 , followed by Biotite K(Mg, Fe)[Al, Si 3 o 10 ](OH,F) 2 Or hornblende (mostly common hornblende) HornblendaNaCa 2 (Mg,Fe) 4 [(Si,Al)4O 11 ] 2 (OH) 2 , there are traces of apatite, etc. At the same time, medica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B26/28E04F13/075
CPCC04B26/28C04B26/285C04B2111/00025E04F13/0875C04B14/041C04B14/08C04B22/064C04B14/305C04B24/383C04B14/104C04B24/38C04B22/142C04B22/14
Inventor 于浪曹永科
Owner 白山和一硅藻科技股份有限公司