Passivation magnesium powder, passivation aluminum magnesium alloy powder and wet process production process of passivation magnesium powder and passivation aluminum magnesium alloy powder

A kind of aluminum-magnesium alloy powder and production process technology, which is applied in metal material coating process, metal processing equipment, transportation and packaging, etc., can solve the problems of high airtight requirements of equipment, unsatisfactory nitrogen protection effect, large specific surface area, etc., and achieve Excellent anti-oxidation performance, excellent site environment, and high safety factor

Active Publication Date: 2017-08-25
浏阳市科力烟花材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The chemical properties of aluminum and magnesium are active. Due to the large specific surface area of ​​magnesium powder and aluminum-magnesium alloy powder, it is easy to slowly react with oxygen, nitrogen and moisture in the air during production, storage and use, resulting in a decrease in effective activity and affecting the use effect. , it is easy to induce various safety hazards due to the exothermic reaction
[0003] At the same time, the existing dry process for producing magnesium powder and aluminum-magnesium alloy powder has the following defects: 1. The production process needs inert gas protection, and the airtight requirements for equipment are high, otherwise it is easy to cause dust leakage, and even cause safety accidents such as dust combustion and explosion ; 2. The effect of using cheap nitrogen protection is not ideal, while the cost of using other inert gases is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Passivation magnesium powder, passivation aluminum magnesium alloy powder and wet process production process of passivation magnesium powder and passivation aluminum magnesium alloy powder
  • Passivation magnesium powder, passivation aluminum magnesium alloy powder and wet process production process of passivation magnesium powder and passivation aluminum magnesium alloy powder
  • Passivation magnesium powder, passivation aluminum magnesium alloy powder and wet process production process of passivation magnesium powder and passivation aluminum magnesium alloy powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: the wet process production technique of passivated aluminum-magnesium alloy powder, comprises the steps:

[0023] Step 1, preparation of an antioxidant aqueous solution, by weight, phytic acid, boric acid, and potassium dichromate are prepared into an aqueous solution with a total concentration of antioxidants of 5%. The aqueous solution contains 1% of phytic acid, 2% of boric acid, 2% of potassium dichromate and the rest is water.

[0024] Step 2, through crushing, the aluminum-magnesium alloy particles with a total activity of 99.5% are arbitrarily divided into two parts, one part is processed according to the wet process of the present invention as the experimental group; the other part is processed according to the traditional dry process as the control group;

[0025] Experimental group: Al-Mg alloy grains were added to the antioxidant aqueous solution with a total concentration of 5% prepared in step 1, and wet crushed to obtain a solid-liquid mixtur...

Embodiment 2

[0032] Embodiment 2: the wet process production technique of passivated magnesium powder, comprises the steps:

[0033] Step 1, preparation of antioxidant aqueous solution, boric acid and potassium dichromate are prepared by weight into an aqueous solution with a total concentration of antioxidant of 10%. The aqueous solution contains 3% of boric acid, 7% of potassium dichromate, and the rest is water.

[0034] Step 2, broken through milling short-cut method, active total amount is 99.7% flaky metallic magnesium particle and is arbitrarily divided into two parts, one part is processed by wet process of the present invention as experimental group; another part is processed by traditional method as control group dry processing;

[0035] Experimental group: the flaky metal magnesium particles are added to the antioxidant aqueous solution with a total concentration of 10% prepared in step 1, and wet crushed until the 60-mesh sieve passes through to obtain a solid-liquid mixture; ...

Embodiment 3～8

[0046] Embodiments 3-8 are different from Embodiment 1 or 2 in that in the preparation of the antioxidant aqueous solution in step 1, the type, quantity, proportioning of the selected antioxidant and the total antioxidant content in the antioxidant aqueous solution are different, See table (4) below for details.

[0047]

[0048]In each formula of above table, all the other are water. It should be noted that the formulation of the antioxidant aqueous solution of the present invention is not limited to the content listed in each example. According to specific needs (such as different requirements for passivation degree, speed and active content), different types and proportions of antioxidant aqueous solutions can be used, combined with different passivation temperatures and passivation times, to produce passivated magnesium powder and passivated magnesium powder for different purposes. Aluminum-magnesium alloy powder, and each antioxidant used alone or in any combination h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses passivation magnesium powder, passivation aluminum magnesium alloy powder and a wet process production process of the passivation magnesium powder and the passivation aluminum magnesium alloy powder. Magnesium particles, aluminum magnesium alloy particles and an antioxidant aqueous solution are added into wet grinding equipment to be subject to wet grinding; then a solid-liquid mixture is subjected to wet type screening or waterpower classification to complete solid-liquid separation; and the passivation magnesium powder or the passivation aluminum magnesium alloy powder is obtained after drying is carried out. Surfaces of particles of the finished magnesium powder and the aluminum magnesium alloy powder are wrapped with passivation protection films. The powder production process is fully carried out under the antioxidant aqueous solution protection, and is a production method high in safety factor, simple in equipment and excellent in site environment. Passivation, grinding and size grading are completed through one step. Finished products are even in passivation, compact, stable and excellent in anti-oxidation performance. The antioxidant aqueous solution can be used for a long time in a circulated manner, waste water emission is avoided, and the process method is environment-friendly.

Description

technical field [0001] The invention relates to a passivated metal magnesium powder, a passivated aluminum-magnesium alloy powder and a production method thereof, in particular to a passivated magnesium powder and a passivated aluminum-magnesium alloy powder produced by a wet process and a production method thereof. Background technique [0002] The chemical properties of aluminum and magnesium are active. Due to the large specific surface area of ​​magnesium powder and aluminum-magnesium alloy powder, it is easy to slowly react with oxygen, nitrogen and moisture in the air during production, storage and use, resulting in a decrease in effective activity and affecting the use effect. , it is easy to induce various safety hazards due to the exothermic reaction. [0003] At the same time, the existing dry process for producing magnesium powder and aluminum-magnesium alloy powder has the following defects: 1. The production process needs inert gas protection, and the airtight r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F1/02C23C22/27
CPCC23C22/27B22F1/16
Inventor 卜佩璇卜继望
Owner 浏阳市科力烟花材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com