A method for synthesizing metal organic framework material co-mof-71

A metal-organic framework, co-mof-71 technology, applied in the field of synthesis of organic framework materials, can solve the problems of few reports and achieve the effects of high selectivity, short process flow and low environmental pollution

Inactive Publication Date: 2020-06-19
NINGXIA UNIVERSITY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are few reports on the preparation methods and applications of Co-MOF-71 materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for synthesizing metal organic framework material co-mof-71

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Mix the raw materials cobalt nitrate, terephthalic acid, solvent N,N-dimethylformamide, and absolute ethanol in a molar ratio of 1:1.5:95.5:31.3, place it in a Shrek tube, seal it and raise the temperature to 120°C to keep 10h, then filtered while hot, washed three times with anhydrous methanol solution with the same volume as the solvent in the ingredients, and finally dried in air at 100°C for 6h to obtain Co-MOF-71 metal organic framework material. The XRD pattern of the sample is shown as figure 1 As shown in (1), the specific surface area, micropore pore volume, and cobalt mass percentage are listed in Table 1, respectively.

Embodiment 2

[0020] Mix the raw materials cobalt nitrate, terephthalic acid, solvent N,N-dimethylformamide, and absolute ethanol in a molar ratio of 1:1.5:191.0:62.6, place it in a Shrek tube, seal it and raise the temperature to 110°C to keep 15h, then filtered while hot, washed three times with anhydrous methanol solution with the same volume as the solvent in the ingredients, and finally dried in air at 80°C for 10h to obtain Co-MOF-71 metal organic framework material. The XRD pattern of the sample is shown as figure 1 As shown in (1), the specific surface area, micropore pore volume, and cobalt mass percentage are listed in Table 1, respectively.

Embodiment 3

[0022] Mix the raw materials cobalt nitrate, terephthalic acid, solvent N,N-dimethylformamide, and absolute ethanol in a molar ratio of 1:1.5:191.0:31.3, place it in a Shrek tube, seal it and raise the temperature to 110°C to keep 15h, then filtered while hot, washed three times with anhydrous methanol solution with the same volume as the solvent in the ingredients, and finally dried in air at 100°C for 6h to obtain Co-MOF-71 metal organic framework material. The XRD pattern of the sample is shown as figure 1 As shown in (1), the specific surface area, micropore pore volume, and cobalt mass percentage are listed in Table 1, respectively.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention successfully prepares Co-MOF-71 nanomaterials, optimizes the preparation process conditions, and prepares materials with uniform grain size and good stability. When the element Co uses the acidic catalytic reaction of metal ions in the MOF skeleton, the metal ions are both active sites and support points of the skeleton. During the catalytic process, the metal ions coordinate. The prepared Co‑MOF‑71 material has a high metal content and fully exposed metal sites, which can provide more Lewis acidic sites. The Co‑MOF‑71 material is conducive to the activation of all reactant molecules and has good catalytic activity. .

Description

technical field [0001] The invention relates to a synthesis method of an organic framework material. Background technique [0002] Metal-Organic Frameworks (MOF for short) is a new type of porous network structure material formed by the coordination of metal ions and organic ligands. MOF has the following unique and potential advantages: ① Large specific surface area; ② No dead volume, large porosity; ③ Strong and flexible framework; ④ Compared with existing heterogeneous catalysts, the metal sites of MOF are completely exposed; ⑤ Pores have Regularity, so the transfer rate of guest molecules is high. Based on the above advantages, MOFs have been used in gas adsorption, separation and storage, catalysis, drug delivery, optics, electronics, sensing and nanoreactors, etc. [0003] As a heterogeneous catalyst, MOF has attracted more and more researchers' attention in recent years. This is mainly due to the flexible and adjustable MOF framework structure, which can generate a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G83/00B01J31/22B01J35/10C10G2/00
CPCC10G2/332C08G83/008B01J31/1691B01J2531/845B01J2531/0213B01J35/612B01J35/638
Inventor 裴彦鹏郭庆杰胡修德
Owner NINGXIA UNIVERSITY