Organosilicone connecting coating suitable for various substrates and preparation and use method thereof
A silicone and coating technology, applied in the coating field, can solve problems such as poor recoatability, poor substrate adhesion, and inconvenient actual use, and achieve the effects of increasing system toughness, expanding molecular weight, and excellent connection
Active Publication Date: 2017-09-19
XIAMEN SUNRUI SHIP COATING
View PDF9 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
This antifouling mechanism brings the following defects in low surface energy silicone antifouling coatings: poor adhesion to the substrate, poor recoatability
[0005] Invention patent CN201410550964.3 discloses a silicone intermediate connecting paint, which is composed of hydroxyl silicone oil, silane coupling agent, silane crosslinking agent and organotin catalyst, and consists of three parts, A, B, and C, which is inconvenient for actual use; And the adhesion strength on the anti-rust primer is only 1.18MPa
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0029] In order to make the purpose, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions in the embodiments of the present invention are clearly and completely described below. Obviously, the described embodiments are part of the embodiments of the present invention, not all Example. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.
[0030] The present invention is further described by the following examples. Table 1 and Table 2 are respectively the A component and the B component of the three preferred embodiments provided by the present invention.
[0031] Table 1
[0032]
[0033] Table 2
[0034]
[0035] Preparation method of component A: disperse hydroxyl polysiloxane resin, cyanuric acid epoxy resin and solvent at 2500rpm, stir evenly; add defoamer,...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| viscosity | aaaaa | aaaaa |
Login to View More
Abstract
The invention provides an organosilicone connecting coating suitable for various substrates and a preparation and use method thereof. The organosilicone connecting coating suitable for the various substrates is mainly prepared from the following raw materials in parts by weight: a component A and a component B, wherein the component A comprises 40 to 44 parts of hydroxy terminated polydimethylsiloxane, 4 to 8 parts of cyanuric acid epoxy resin, 1.6 to 2 parts of thixotropic agent, 0.4 to 0.8 part of defoaming agent, 0.3 to 0.5 part of dispersant, 8 to 10 parts of pigment, 16 to 20 parts of filler and 6 to 7.2 parts of solvent; the component B comprises 2 to 2.2 parts of crosslinking agent, 0.5 to 1 part of adhesion force accelerant, 3.2 to 6.4 parts of curing agent, 0.3 to 0.5 part of catalyst, and 7.4 to 7.9 parts of solvent. The organosilicone connecting coating suitable for the various substrates has the advantages that after curing, the adhesion strength of a coating layer to the substrate is 2.2MPa or above; after curing, the connecting strength to the dirt-release type anti-pollution paint is higher than 1.0MPa, or is greater than the cohesion force of the anti-pollution coating.
Description
technical field [0001] The invention relates to coating technology, in particular to an organic silicon connection coating suitable for various substrates and a preparation and application method. Background technique [0002] Fouling-release antifouling paint is a non-release antifouling agent and environmentally friendly paint. It uses the low surface energy characteristics of the paint surface itself to make it difficult for marine organisms to adhere; even if marine organisms adhere, the low elastic modulus The attachments are easily removed under the shear force of water or high-pressure water washing when the ship is sailing. This antifouling mechanism brings the following defects in low surface energy silicone antifouling coatings: poor adhesion to the substrate and poor recoatability. [0003] Due to the above-mentioned defects of the fouling-release antifouling paint, if it is directly coated on the epoxy antirust coating or metal substrate, the antifouling coating...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/06C09D163/00C09D7/12C09D5/16
CPCC08K2003/2241C08K2003/2272C08L2205/03C09D5/16C09D183/06C08L63/00C08L77/00C08K13/02C08K3/22C08K3/346C08K3/34C08K5/544C08K3/36C08K13/06
Inventor 王胜龙刘轶龙方大庆苏雅丽吴堃
Owner XIAMEN SUNRUI SHIP COATING