Glutamic acid derivative, preparation method thereof, and preparation method of multi-scale porous structured TiO2 crystalline aerogel

A technology of derivatives and glutamic acid, which is applied in the field of preparing TiO2 crystalline airgel with multi-scale pore structure, can solve the problems of slow mass transfer process, difficult to reuse, easy to condense, etc., and achieves simple and efficient preparation method Ease of operation and mild reaction conditions

Active Publication Date: 2017-09-29
SHAANXI NORMAL UNIV
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Dispersed Nano TiO 2 There are disadvantages such as difficulty in separation, easy aggregation, and difficulty in recycling; supported nano-TiO 2 And because of the slow mass transfer process, the utilization rate of effective nanoparticles is low, which greatly weakens the advantages of large specific surface area of ​​nanoparticles, so the preparation of nano-TiO with novel pore structure 2 Porous blocks become an effective way to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glutamic acid derivative, preparation method thereof, and preparation method of multi-scale porous structured TiO2 crystalline aerogel
  • Glutamic acid derivative, preparation method thereof, and preparation method of multi-scale porous structured TiO2 crystalline aerogel
  • Glutamic acid derivative, preparation method thereof, and preparation method of multi-scale porous structured TiO2 crystalline aerogel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] 1. Synthesis of compounds of formula Ⅰ-1

[0048]12.4g (49.97mmol) Boc-L-glutamic acid, 38.43g (200.61mmol) 1-ethyl-(3-dimethylaminopropyl) carbodiimide hydrochloride, 0.42g (3.34mmol) 4-Dimethylaminopyridine was dissolved in 200mL of dichloromethane, and 18.54g (100.02mmol) of n-dodecylamine was added under ice bath conditions, and the ice bath was removed after stirring for 30 minutes, and the reaction was stirred and reacted at normal temperature for 24 hours, and the reaction Liquid was washed with 0.1mol / L NaOH aqueous solution, 0.1mol / L HCl aqueous solution and distilled water successively, and the organic phase was washed with anhydrous NaOH 2 SO 4 After drying, the solvent was evaporated under reduced pressure, and the obtained crude product was separated and purified by column chromatography with chloroform and methanol in a volume ratio of 20:1 as a mobile phase and silica gel as a stationary phase to obtain the compound of formula Ⅰ-1 (white Solid 22.8g, pr...

Embodiment 2

[0072] Dissolve 0.076g of the glutamic acid derivative of Example 1 in 3mL of benzyl alcohol, and slowly add 0.15mL of TiCl dropwise under nitrogen protection and -15°C 4 And keep stirring, the solution turns reddish brown, after the dropwise addition, seal and age at 80°C for 3 days, then place it in a centrifuge tube, repeat centrifugation with acetone (10mL×7 times), add 100 μL of benzene, and Centrifuge at 1000r / min for 5min, freeze-dry the solid, and anneal at 450°C for 30min to obtain TiO 2 Crystalline airgel.

[0073] The obtained samples were characterized by X-ray diffractometer, scanning electron microscope and transmission electron microscope, the results are shown in Figure 1~4 . Depend on figure 1 It can be seen that the obtained sample is anatase TiO 2 . Depend on Figure 2-4 It can be seen that the anatase TiO 2 Crystalline aerogels have three-dimensional continuous micro- and nano-scale channels, wherein the size of the micro-channel is about 25 μm, and...

Embodiment 3

[0075] In this example, after adding 100 μL of benzene, it was centrifuged at 2000 r / min for 5 minutes, and other steps were the same as in Example 2 to obtain TiO 2 Crystalline airgel. Depend on Figure 5 It can be seen that the obtained TiO 2 The crystalline airgel has three-dimensional continuous micron-scale and nano-scale channels, wherein the size of the micro-channel is about 20 μm, and the size of the nano-channel is 1-10 nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Sizeaaaaaaaaaa
Sizeaaaaaaaaaa
Sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a glutamic acid derivative, a preparation method thereof, and a preparation method of a multi-scale porous structured TiO2 crystalline aerogel. The structural formula of the derivative is shown in the description; and in the formula, and n is an integer in a range of 7-13, m is 0, 1 or 2. The derivative has a self-assembling characteristic, and the preparation method of the derivative has the advantages of simplicity, and mild reaction conditions. The anatase TiO2 crystalline aerogel having three-dimensional continuous nanometer and nanometer pores is prepared through covalent grafting of the surface of TiO2 nano-particles with the above compound, centrifugal concentration, freeze drying and annealing, and the centrifugal rotating speed is adjusted to realize the regulation of the pore dimensions. The crystalline aerogel can be used for photocatalytic degradation of formaldehyde gas.

Description

technical field [0001] The invention belongs to the technical field of preparation of nanomaterials, in particular to a glutamic acid derivative with self-assembly function and a preparation method thereof, and the preparation of TiO with a multi-scale pore structure by using the glutamic acid derivative 2 A method for crystalline aerogels. Background technique [0002] Nano titanium dioxide (TiO 2 ) is an n-type semiconductor with a forbidden band width of 3.2 eV, corresponding to photon energy with a wavelength of 387.5 nm. When the wavelength is less than 387.5nm biophoton irradiates TiO 2 When on the surface of the valence band, the electrons in the valence band are excited to the conduction band, thereby generating highly active photo-generated electrons (e - ) and photogenerated holes (h + ), under the action of an electric field, the negatively charged photogenerated electrons (e - ) and positively charged photogenerated holes (h + ) to separate and migrate to d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C07D249/04B01J31/38B01J21/06
CPCC07D249/04B01J21/063B01J31/0244B01J31/0271B01J31/38B01J35/23
Inventor 严军林杨颖超刘静
Owner SHAANXI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com