Composite desulfurizer for molten iron desulphurization or semisteel desulphurization and process method thereof
A process method and technology for desulfurization of molten iron, which are applied in the field of metallurgical production, can solve the problems of inability to meet the smelting requirements of steel-making steel grades, low desulfurization efficiency, large splash, etc., and achieve high iron loss, low desulfurization efficiency, and reduced iron loss. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0014] Example 1:
[0015] After vanadium-containing titanium molten iron is blown oxygen through a converter to extract vanadium in the molten iron, vanadium-rich vanadium slag and sulfur-containing semi-steel are formed respectively. After the high-sulfur semi-steel enters the desulfurization station, the weight is 139.0 tons, the temperature is 1362℃, and the composition is: C3.54%, Mn0.02%, V0.022%, Si0.02%, S0.095%, P0.053 %, Ti0.004% and the balance of iron and unavoidable impurities. Using the original mixed injection equipment, the target sulfur is set to 0.020%, and 1042 kg of the composite desulfurizer of the present invention is added to perform injection desulfurization. In the blowing process, the spray is small, the flame is small, and there is no smoke and dust overflow. After the desulfurization, the slag scraper is used to remove the desulfurization slag, and the desulfurization slag is removed for 5.5 minutes. After removing the slag, weigh, measure the tempe...
Example Embodiment
[0016] Example 2:
[0017] After vanadium-containing titanium molten iron is blown oxygen through a converter to extract vanadium in the molten iron, vanadium-rich vanadium slag and sulfur-containing semi-steel are formed respectively. After the high-sulfur semi-steel enters the desulfurization station, the weight is 137.0 tons, the temperature is 1345℃, and the composition is: C3.56%, Mn0.02%, V0.031%, Si0.02%, S0.078%, P0.054 %, Ti0.003% and the balance of iron and unavoidable impurities. Using the original composite injection equipment, the target sulfur is set to 0.008%, and 947 kg of the desulfurizing agent of the present invention is added to perform injection desulfurization. In the blowing process, the spray is small, the flame is small, and there is no smoke and dust overflow. After the desulfurization is completed, the desulfurization slag is removed by a slag scraper, and the desulfurization slag is removed in 5.0 minutes. After removing the slag, weigh, measure the...
Example Embodiment
[0018] Example 3:
[0019] The vanadium-containing titanium molten iron weighs 138.5 tons after the tank is assembled, the temperature is 1275°C, and the composition is: C4.28%, Mn0.22%, V0.31%, Si0.15%, S0.072%, P0.053%, Ti is 0.15%, using 924 kg of the desulfurizing agent of the present invention for injection desulfurization. In the blowing process, the spray is small, the flame is small, and there is no smoke and dust overflow. After the desulfurization, the desulfurization slag is removed by a slag scraper, and it takes 5.3 minutes for the desulfurization slag to be exhausted. After removing the slag, weigh, measure temperature and sample and analyze the semi-steel after the desulfurization slag is removed. The weight of the semi-steel after the removal of the desulfurization slag is 134.5 tons, the temperature is 1250°C, and the composition is C4.27%. , Mn0.22%, V0.30%, Si0.15%, S0.007%, P0.53%, Ti0.15%, and the balance of iron and unavoidable impurities. It is calculate...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap