Graphene enhanced water permeable brick and preparation method thereof
A graphene and permeable brick technology, applied in the field of permeable brick and its preparation, can solve the problems of increased cost, high energy consumption in the sintering process, and high repair rate, and achieve the effects of reducing cracking, excellent air permeability and low cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0041] Example 1:
[0042] (1) Add 0.34g of polymer surfactant into 1kg of water, add 34g of graphene and 136g of graphene oxide, stir at 240r / min for 10min, then sonicate at 300W for 5min, and add 25.5kg of water under 240r / min of stirring , Continue to stir for 5 min to form a graphene carbon dispersion.
[0043] (2) Add 159.4kg of quartz sand and 30kg of cement to the mixer, premix for 1min at 120r / min, add 5.3kg of graphene carbon dispersion and 5.3kg of water while stirring, continue to mix for 3min, then use the surface layer for processing The mechanism is superficial.
[0044] (3) Add 115.4kg gravel, 40kg fine sand and 34kg cement into the mixer, premix for 1 min at 120r / min, add 2.65kg graphene carbon dispersion and 7.95kg water under stirring, continue stirring for 3min Use the bottom layer processing mechanism to get the bottom layer.
[0045] (4) Put the prepared bottom layer into the mold cavity, put the surface layer on the bottom layer, and then press and shape it wit...
Example Embodiment
[0047] Example 2: The best example
[0048] (1) Add 0.34g of polymer surfactant into 1kg of water, add 34g of graphene and 136g of graphene oxide, stir at 240r / min for 10min, then sonicate at 300W for 5min, and add 25.5kg of water under 240r / min of stirring , Continue to stir for 5 min to form a graphene carbon dispersion.
[0049] (2) Add 155.4kg of quartz sand and 34kg of cement to the mixer, premix for 1 min at 120r / min, add 5.3kg of graphene carbon dispersion and 5.3kg of water under agitation, continue to mix for 3min, then use the surface layer for processing The mechanism is superficial.
[0050] (3) Add 115.4kg gravel, 40kg fine sand and 34kg cement into the mixer, premix for 1 min at 120r / min, add 2.65kg graphene carbon dispersion and 7.95kg water under stirring, continue stirring for 3min Use the bottom layer processing mechanism to get the bottom layer.
[0051] (4) Put the prepared bottom layer into the mold cavity, put the surface layer on the bottom layer, and then pre...
Example Embodiment
[0053] Example 3:
[0054] (1) Add 0.34g of polymer surfactant into 1kg of water, add 34g of graphene and 136g of graphene oxide, stir at 240r / min for 10min, then sonicate at 300W for 5min, and add 25.5kg of water under 240r / min of stirring , Continue to stir for 5 min to form a graphene carbon dispersion.
[0055] (2) Add 149.4kg of quartz sand and 40kg of cement to the mixer, premix for 1min at 120r / min, add 5.3kg of graphene carbon dispersion and 5.3kg of water under stirring, continue to stir for 3min, then use surface layer processing The mechanism is superficial.
[0056] (3) Add 115.4kg gravel, 40kg fine sand and 34kg cement into the mixer, premix for 1 min at 120r / min, add 2.65kg graphene carbon dispersion and 7.95kg water under stirring, continue stirring for 3min Use the bottom layer processing mechanism to get the bottom layer.
[0057] (4) Put the prepared bottom layer into the mold cavity, put the surface layer on the bottom layer, and then press and shape it with a bri...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap