Insulating fireproof coating for appliances and preparation method thereof

A technology for insulating fireproofing and coatings, applied in the direction of fireproofing coatings, epoxy resin coatings, coatings, etc., can solve problems such as high temperature resistance, poor water resistance, easy cracking, etc. performance effect

Inactive Publication Date: 2017-10-10
HEFEI DONGHENGRUI ELECTRONICS TECH CO LTD
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing coatings have poor high temperature resistance and water resistance, and are prone to cracking after long-term use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] An insulating fireproof coating for electrical appliances, comprising the following raw materials: 55 parts of modified acrylic resin, 40 parts of organosilicon modified epoxy resin, 30 parts of acrylic emulsion, 30 parts of insulating additives, and modified hollow glass microspheres 20 parts, 10 parts of additives and 65 parts of water;

[0034] The modified acrylic resin includes the following raw materials: 18 parts of methyl methacrylate, 14 parts of styrene, 9 parts of isooctyl acrylate, 6 parts of butyl acrylate, γ-methacryloyloxypropyl trimeth 5 parts of oxysilane, 3 parts of xylene and 1 part of azobisisobutyronitrile;

[0035] The modified hollow glass microspheres include the following raw materials: 10 parts of hollow glass microspheres, 8 parts of hydrofluoric acid solution and 8 parts of chromium aluminum phosphate solution;

[0036] The auxiliary agent includes the following raw materials in parts: 3 parts of flame retardant, 2 parts of dispersant, 1 par...

Embodiment 2

[0052] An insulating fireproof coating for electrical appliances, comprising the following raw materials: 65 parts of modified acrylic resin, 45 parts of silicone modified epoxy resin, 40 parts of acrylic emulsion, 40 parts of insulating additive, modified hollow glass microspheres 25 parts, 20 parts of additives and 75 parts of water;

[0053] The modified acrylic resin includes the following raw materials: 20 parts of methyl methacrylate, 16 parts of styrene, 12 parts of isooctyl acrylate, 8 parts of butyl acrylate, γ-methacryloxypropyl trimethyl 7 parts of oxysilane, 5 parts of xylene and 2 parts of azobisisobutyronitrile;

[0054] The modified hollow glass microspheres include the following raw materials: 15 parts of hollow glass microspheres, 10 parts of hydrofluoric acid solution and 10 parts of chromium aluminum phosphate solution;

[0055] The auxiliary agent includes the following raw materials: 5 parts of flame retardant, 3 parts of dispersant, 2 parts of film-formi...

Embodiment 3

[0071] An insulating fireproof coating for electrical appliances, comprising the following raw materials: 60 parts of modified acrylic resin, 42.5 parts of silicone modified epoxy resin, 35 parts of acrylic emulsion, 35 parts of insulating additive, modified hollow glass microspheres 22.5 parts, 15 parts of additives and 70 parts of water;

[0072] The modified acrylic resin includes the following raw materials: 19 parts of methyl methacrylate, 15 parts of styrene, 10 parts of isooctyl acrylate, 7 parts of butyl acrylate, γ-methacryloxypropyl trimethyl 6 parts of oxysilane, 4 parts of xylene and 1.5 parts of azobisisobutyronitrile;

[0073] The modified hollow glass microspheres include the following raw materials: 12 parts of hollow glass microspheres, 9 parts of hydrofluoric acid solution and 9 parts of chromium aluminum phosphate solution;

[0074] The auxiliary agent includes the following raw materials: 4 parts of flame retardant, 2.5 parts of dispersant, 1.5 parts of fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an insulating fireproof coating for appliances and a preparation method thereof, and relates to the technical field of coating. The coating is prepared from the following raw materials in parts by weight: 55-65 parts of modified acrylic resin, 40-45 parts of organic silicon modified epoxy resin, 30-40 parts of acrylic emulsion, 30-40 parts of insulating additive, 20-25 parts of modified hollow glass beads, 10-20 parts of adjuvant and 65-75 parts of water. After being used on an appliance surface, the coating has strong binding performance, cannot be cracked in long-term use, can form a hydrophobic molecular layer on the appliance surface, and has the effects of preventing water and fire, insulating and resisting abrasion.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an insulating fireproof coating for electrical appliances and a preparation method thereof. Background technique [0002] Applying insulating paint on the surface of electrical appliances is a safety measure that uses non-conductive substances to isolate or wrap the charged body to protect against electric shock. Good insulation is the most basic and most reliable means to ensure the safe operation of household appliances and lines and prevent personal electric shock accidents. However, the existing coatings have poor high temperature resistance and water resistance, and are prone to cracking after long-term use. SUMMARY OF THE INVENTION [0003] The purpose of the present invention is to provide an insulating fireproof coating for electrical appliances and a preparation method thereof. After the coating is used on the surface of the electrical appliance, it has strong bindin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/12C09D163/00C09D183/08C09D133/00C09D5/18C09D7/12
CPCC09D143/04C08K2003/2224C08K2003/2227C08L2201/02C08L2203/20C08L2205/02C08L2205/035C09D5/18C08L63/00C08L83/08C08L33/00C08L27/18C08L91/06C08L23/34C08L93/04C08K13/06C08K9/02C08K7/28C08K3/22C08K3/34C08K7/12C08K7/14
Inventor 齐慧
Owner HEFEI DONGHENGRUI ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com