A kind of preparation method of ti3sic2/ag composite conductive powder

A technology of composite conductive powder and powder, which is applied in metal processing equipment, liquid chemical plating, transportation and packaging, etc. It can solve the problems of inability to carry out mass production, complex process, high cost, etc., and achieve good chemical stability and process The process is simple and the effect of reducing density

Active Publication Date: 2019-03-08
XI'AN POLYTECHNIC UNIVERSITY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to the reports in the existing literature, flexible conductive materials mainly use metal nanowires, graphene, CNTs, etc. as conductive fillers. there is still a certain gap

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of ti3sic2/ag composite conductive powder
  • A kind of preparation method of ti3sic2/ag composite conductive powder

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0059] The Ti prepared by the preparation method of the present invention will be 3 SiC 2 / Ag composite conductive powder is mixed with resin, rubber and other insulating matrix in a certain proportion, by adjusting the Ti 3 SiC 2 / Ag composite conductive powder content, can prepare conductive film material with good conductivity; in addition, the Ti 3 SiC 2 / Ag composite conductive powder can also be used as conductive filler of electronic paste.

[0060] figure 1 is Ti 3 SiC 2 / Ag composite conductive powder XRD pattern, from figure 1 It can be seen that: except Ti 3 SiC 2 In addition to the diffraction peaks of Ag, the diffraction peaks of Ag can also be clearly observed, indicating that the Ti3SiC2 / Ag composite conductive powder has been successfully prepared.

[0061] figure 2 is Ti 3 SiC 2 / Ag composite conductive powder SEM image, from figure 2 It can be seen that the nano-Ag particles are attached to the Ti 3 SiC 2 Powder surface, but not completely c...

Embodiment 1

[0063] Take Ti with an average particle size of 2 μm to 20 μm and a purity greater than 93%. 3 SiC 2 powder; the Ti 3 SiC 2 Pour the powder into the ethanol aqueous solution (the ethanol aqueous solution is obtained by mixing ethanol and water at a volume ratio of 1: 1), and make the Ti 3 SiC 2 The powder is completely immersed in the ethanol aqueous solution, and the Ti 3 SiC 2 The powder was washed with alcohol, and the alcohol washing time was 10 minutes; the Ti obtained after alcohol washing 3 SiC 2 Pour the powder into hydrofluoric acid aqueous solution (hydrofluoric acid aqueous solution is obtained by mixing hydrofluoric acid and water at a volume ratio of 1:1), and make Ti 3 SiC 2 The powder is completely submerged in hydrofluoric acid aqueous solution, and the Ti 3 SiC 2 The powder is subjected to coarsening treatment, and the coarsening treatment time is 30 minutes; hydrochloric acid (the concentration of hydrochloric acid is 100ml / L) and SnCl are mixed at ...

Embodiment 2

[0068] Take Ti with an average particle size of 2 μm to 20 μm and a purity greater than 93%. 3 SiC 2 powder; the Ti 3 SiC 2 Pour the powder into the ethanol aqueous solution (the ethanol aqueous solution is obtained by mixing ethanol and water at a volume ratio of 1: 1.5), and make Ti 3 SiC 2 The powder is completely immersed in the ethanol aqueous solution, and the Ti 3 SiC 2 The powder was washed with alcohol, and the alcohol washing time was 15 minutes; the Ti obtained after alcohol washing 3 SiC 2 Pour the powder into hydrofluoric acid aqueous solution (hydrofluoric acid aqueous solution is obtained by mixing hydrofluoric acid and water at a volume ratio of 1:2), and make Ti 3 SiC 2 The powder is completely submerged in hydrofluoric acid aqueous solution, and the Ti 3 SiC 2 The powder is subjected to coarsening treatment, and the coarsening treatment time is 40min; the volume ratio of SnCl is 3:1 2 Aqueous solution (SnCl 2 The concentration of the aqueous solut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

Ti disclosed in the present invention 3 SiC 2 The preparation method of / Ag composite conductive powder, its step is: step 1, to Ti 3 SiC 2 The powder is sequentially washed with alcohol, roughened, sensitized, activated, washed with water and dried to obtain pretreated Ti 3 SiC 2 Powder; step 2, prepare silver ammonia solution and reducing solution respectively; Step 3, utilize the silver ammonia solution and reducing solution that step 2 obtains to the pretreatment Ti that obtains through step 1 3 SiC 2 The powder is subjected to silver-ammonia plating; step 4, filtering the remaining material after plating in step 3, and drying the remaining part after filtering off the liquid to obtain Ti 3 SiC 2 / Ag composite conductive powder. The preparation method of the present invention can prepare Ti with lower density, good stability and high conductivity. 3 SiC 2 / Ag composite conductive powder.

Description

technical field [0001] The invention belongs to the technical field of conductive materials or electronic paste preparation methods, in particular to a Ti 3 SiC 2 A preparation method of Ag / Ag composite conductive powder. Background technique [0002] With the development of electronic technology, more and more electronic devices are developing in the direction of flexibility, such as: smart clothing, robot skin, rollable e-books, strain sensors, stretchable solar cells, etc. At present, the conductive films that have been widely used are mostly prepared on hard substrate materials such as glass ceramics, but hard substrate materials have many shortcomings such as brittleness, fragility, and difficulty in deformation, which largely limits their use. Applications, can no longer meet the needs of the new generation of electronic equipment, so the development of new flexible conductive materials is urgently needed. [0003] Conductive fillers play a decisive role in the cond...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F1/02C23C18/44
CPCC23C18/44B22F1/17
Inventor 刘毅苏晓磊徐洁王俊勃贺辛亥屈银虎
Owner XI'AN POLYTECHNIC UNIVERSITY