Compounded rubber reinforcing agent and preparation method and application thereof
A technology of compounding rubber and reinforcing agent, applied in the field of rubber filling materials, can solve the problems of unfavorable energy saving and emission reduction, high design requirements, large energy consumption, etc., and achieve the effects of low density, good compatibility, and increased specific surface area
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0034] (1) Weigh the composite complexing agent (by Al(H 2 PO 4 ) 3 、Na 2 S and sodium tripolyphosphate compounded at a mass ratio of 1:1:1) 1 part was dissolved in 4 parts of water to form an aqueous solution, added to 20 parts of waste incineration fly ash, stirred and mixed in a high-speed mixer, and obtained Complex waste incineration fly ash;
[0035] (2) Place the complexed waste incineration fly ash obtained in step (1) in a drying box and dry at 100° C. for 6 hours, then place it in a pulverizer and pulverize it to 400 mesh to obtain 400 mesh complexed waste incineration fly ash;
[0036] (3) Place the 400-mesh complexed waste incineration fly ash prepared in step (2) with 10 parts of halloysite and 10 parts of activated carbon in a high-speed mixer, mix at a high speed for 0.5h, and then pulverize to 1250 mesh through a pulverizer Left and right, a composite rubber reinforcing agent based on waste incineration fly ash is obtained.
Embodiment 2
[0038] (1) take by weighing composite complexing agent (by Na 2 S, sodium hexametaphosphate and sodium tripolyphosphate compounded at a mass ratio of 1:0.8:1) 4 parts were dissolved in 20 parts of water to make an aqueous solution, added to 80 parts of waste incineration fly ash, and placed in a high-speed mixer Stirring and mixing to obtain complex waste incineration fly ash;
[0039] (2) Place the complexed waste incineration fly ash obtained in step (1) in a drying oven at 120°C and dry for 10 hours, then place it in a pulverizer and pulverize it to 600 mesh to obtain 600 mesh complexed waste incineration fly ash;
[0040] (3) Put the 600-mesh complexed waste incineration fly ash prepared in step (2), 40 parts of halloysite, and 40 parts of activated carbon in a high-speed mixer, mix at high speed for 2 hours, and then pulverize to about 1250 mesh by a pulverizer , to obtain a waste incineration fly ash-based composite rubber reinforcing agent.
Embodiment 3
[0042] (1) Weigh the composite complexing agent (by Al(H 2 PO 4 ) 3 、Na 2 S and sodium hexametaphosphate are compounded at a mass ratio of 1:0.9:0.6) 2 parts are dissolved in 10 parts of water to form an aqueous solution, then added to 50 parts of waste incineration fly ash, placed in a high-speed mixer and stirred and mixed to obtain Complex waste incineration fly ash;
[0043] (2) Place the complexed waste incineration fly ash obtained in step (1) in a drying box and dry at 110° C. for 8 hours, then place it in a pulverizer and pulverize it to 400 mesh to obtain 400 mesh complexed waste incineration fly ash;
[0044](3) Put the 400-mesh complex waste incineration fly ash prepared in step (2), 30 parts of halloysite, and 30 parts of activated carbon in a high-speed mixer, mix at high speed for 1 hour, and then pulverize it to about 1250 mesh by a pulverizer , to obtain a waste incineration fly ash-based composite rubber reinforcing agent.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap