Treatment method for oxygen pressure leaching tailing slag

A treatment method and oxygen pressure leaching technology are applied in the treatment field of oxygen pressure leaching tailings slag, which can solve the problem of high production cost and achieve the effects of increasing utilization rate, reducing pollution and obvious economic effect.

Active Publication Date: 2017-10-17
WESTERN MINING CO LTD +4
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Pyrochemical lead smelting ingredients generally control the lead grade at about 50%, the content of iron and zinc in the mixed ore is generally 6-8%, control FeO:SiO 2 =1.8~2.2, based on the calculat

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Treatment method for oxygen pressure leaching tailing slag

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only a part of the embodiments of the present invention, rather than all the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by those of ordinary skill in the art without creative work shall fall within the protection scope of the present invention.

[0020] See figure 1 , The present invention provides a technical solution: a processing method of oxygen pressure leaching tailings slag, the processing method includes the following steps:

[0021] (1) Transport the collected tailings slag raw materials to the silo, and stack the tailings slag collected in the silo for air-drying treatment;

[0022] (2) The raw material of tailings slag stacked and air-dried is transported to the crushing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a treatment method for oxygen pressure leaching tailing slag. The treatment method comprises the following steps that collected tailing slag raw materials are transported into a bin, and the tailing slag collected into the bin is subjected to stacking and drying treatment; the stacked and dried tailing slag raw materials are transported into a crushing device through a conveyor belt to be crushed, and the crushed materials can increase the speed rate of a subsequent inner-furnace reaction; the crushed tailing slag is mixed with other materials containing little water and then passes through another conveyor belt to conduct material mixing and further dehydration treatment; and the dehydrated tailing slag is subjected to dosing, and the high iron and high sulphur characteristics of the tailing slag approaches that of sulfur-gold sand. According to the treatment method for the oxygen pressure leaching tailing slag, the wasted slag is recycled, the economic effect is obvious, original production is not influenced, the cost is greatly saved, the utilization rate of the waste materials is increased, resource waste is reduced, and environment pollution is relieved.

Description

technical field [0001] The invention relates to the field of industrial technology, in particular to a treatment method for oxygen pressure leaching tailings slag. Background technique [0002] At present, lead smelting mainly adopts the "bottom blowing furnace-reduction furnace-fuming furnace" system. After the reduction furnace replaces the blast furnace, the slag type tends to be a high-iron slag type. The slag is mainly made of sulfur gold sand, and sulfur gold sand needs to be added to supplement iron when making ingredients. and sulfur. Pyrochemical lead smelting ingredients generally control the lead grade at about 50%, the content of iron and zinc in the mixed ore is generally 6-8%, control FeO:SiO 2 =1.8~2.2, based on an annual output of 100,000 tons of crude lead, under the condition of full production per month, the amount of sulfur gold sand is about 500~700 tons, and the production cost is relatively high. The zinc concentrate oxygen pressure leaching tailings...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B7/04
CPCC22B7/001C22B7/04Y02P10/20
Inventor 蔡文陈万群毛成桥秦海斌耿继安石云章郭辉豆连彭靳宝贞刘春胜
Owner WESTERN MINING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap