Novel table tennis racket base plate and preparation method thereof

A table tennis racket and bottom plate technology, applied in the field of table tennis rackets, can solve the problems of high carbon fiber cost, uneven density, and different elasticity, and achieve the effects of low production cost, avoiding fatigue deformation, and uniform density

Inactive Publication Date: 2017-10-24
合肥博创机械制造有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The table tennis rackets currently on the market are mainly solid wood rackets and carbon fiber rackets. The density of solid wood rackets is uneven due to the annual rings of wood, and the force response speed in each direction is slightly different, so that its elasticity is different. It is not determined by the way the athlete hits, there is a certain chance, even if the density of the composite board is as uniform as possible in all directions, there are still differences, and the cost of carbon fiber is too high, and imports are restricted; so a new type is needed Substitute products to meet market demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] This embodiment relates to a new type of table tennis racket bottom plate, including a racket body, the racket body is composed of a core layer and a face plate layer, and the upper and lower parts of the core plate layer are glued together by a modified glutinous rice adhesive layer and the face plate layer respectively. , the core layer is made of a composite material plate, and its thickness is 5mm; the panel layer is made of bamboo board, and its thickness is 0.5mm; the modified glutinous rice adhesive layer is made of modified glutinous rice glue, its The thickness is 0.3mm.

[0033] Wherein, the bamboo board of described panel layer is made by following method:

[0034] (1) Select bamboo that has grown for 5 years, with a bamboo wall thickness of 9mm to 14mm, and saw it into a bamboo tube according to the length of 270mm;

[0035] (2) Dilute the anti-mildew and anti-moth agent into a 1% aqueous solution, first soak the bamboo tube at room temperature for 1 hour, ...

Embodiment 2

[0051] This embodiment relates to a new type of table tennis racket bottom plate, including a racket body, the racket body is composed of a core layer and a face plate layer, and the upper and lower parts of the core plate layer are glued together by a modified glutinous rice adhesive layer and the face plate layer respectively. , the core board layer is made of composite material board, its thickness is 3mm; the face layer is made of bamboo board, its thickness is 1mm; the modified glutinous rice adhesive layer is made of modified glutinous rice glue, its thickness 0.8mm.

[0052] Wherein, the bamboo board of described panel layer is made by following method:

[0053] (1) Select bamboo that has been growing for 7 years, with a bamboo wall thickness of 9mm to 14mm, and saw it into a bamboo tube according to the length of 270mm;

[0054] (2) Dilute the anti-mildew and anti-moth agent into a 1% aqueous solution, first soak the bamboo tube at room temperature for 2 hours, then c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel table tennis racket base plate which comprises a racket body, wherein the racket body comprises a core board layer and a panel layer; the upper surface and the lower surface of the core board layer are glued through a modified glutinous rice glue layer and the panel layer separately; the core board layer is made of a composite material sheet and the thickness is 3-5mm; the panel layer is made of a bamboo board and the thickness is 0.5-1mm; and the modified glutinous rice glue layer is made of modified glutinous rice glue and the thickness is 0.3-0.8mm. The novel table tennis racket base plate is uniform in density and equal in force reaction rates in various directions, has relatively high stability, high strength and sufficient toughness and has multiple excellent properties, such as electrical insulating property, corrosion resistance, combustion resistance and high-temperature resistance, the service life of a table tennis racket is prolonged, and meanwhile, the production cost is relatively low.

Description

technical field [0001] The invention belongs to the field of table tennis rackets, and in particular relates to a novel table tennis racket bottom plate and a preparation method thereof. Background technique [0002] The table tennis rackets currently on the market are mainly solid wood rackets and carbon fiber rackets. The density of solid wood rackets is uneven due to the annual rings of wood, and the force response speed in each direction is slightly different, so that its elasticity is different. It is not determined by the way the athlete hits, there is a certain chance, even if the density of the composite board is as uniform as possible in all directions, there are still differences, and the cost of carbon fiber is too high, and imports are restricted; so a new type is needed Substitute products to meet market demand. Contents of the invention [0003] The present invention provides a novel table tennis racket base plate and a preparation method thereof, which solv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B9/02B32B9/04B32B21/02B32B7/12B32B37/06B32B37/10B32B37/12C08L97/02C08L61/06C08L101/00C08K5/19C08K7/10C08K3/08C08K3/32C09J103/02C09J11/04C09J11/06C09J11/08H01B3/52A63B59/40
CPCA63B2209/00A63B59/40A63B2102/16B32B7/12B32B9/02B32B9/048B32B21/02B32B37/06B32B37/10B32B37/1284B32B2307/206B32B2307/306B32B2307/51B32B2307/558B32B2307/56B32B2307/714B32B2307/7145B32B2307/72B32B2307/764B32B2309/02B32B2309/04B32B2309/12C08K3/08C08K3/32C08K2003/0806C08K2003/085C08K2003/0893C08K2003/325C08L97/02C08L2201/02C08L2201/08C08L2205/03C08L2205/16C09J11/04C09J11/06C09J11/08C09J103/02H01B3/52C08L61/06C08L101/00C08K5/19C08K7/10
Inventor 何飞
Owner 合肥博创机械制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com