Preparation method of early-warning and temperature-resistant material, and early-warning and temperature-resistant material based on method

A temperature-resistant material and intelligent technology, applied in fabrics, textiles, textiles and papermaking, etc., can solve problems such as poor strength, and achieve the effects of increased tear strength, reduced length of bending parts, and good tear strength

Inactive Publication Date: 2017-11-10
WUXI FIRST SPECIAL TYPE FIBERGLASS
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the traditional high silica fiber has the disadvantage of poor strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of early-warning and temperature-resistant material, and early-warning and temperature-resistant material based on method
  • Preparation method of early-warning and temperature-resistant material, and early-warning and temperature-resistant material based on method
  • Preparation method of early-warning and temperature-resistant material, and early-warning and temperature-resistant material based on method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] This embodiment discloses a method for preparing an intelligent early-warning temperature-resistant material, which includes the following steps:

[0036] Step 1, mixing silicone resin (with a hydroxyl content of 1%, MQ ratio of 0.5) and vinyl acetate at a mass ratio of 1: 1.5;

[0037] Step 2, add dispersant to the mixture of step 1, the mass ratio of dispersant and silicone resin is 18: 1, after stirring for 5 minutes; add temperature-changing powder, the mass ratio of temperature-changing powder and silicone resin is 45:1, after stirring for 10 minutes , to obtain coating slurry;

[0038] Step 3: Coat the coating slurry in Step 2 on the plain weave fabric of silicate fiber, using one-knife coating, the coating thickness is 2 filaments, and the amount of glue is 30g / m 2 ;

[0039] Step 4: Curing the coated silicate fiber plain weave fabric at 170° C. for 2 minutes to obtain an intelligent early-warning temperature-resistant material.

Embodiment 2

[0041] This embodiment discloses a method for preparing an intelligent early-warning temperature-resistant material, which includes the following steps:

[0042] Step 1, mixing silicone resin (with a hydroxyl content of 3%, MQ ratio of 1) and toluene at a mass ratio of 3:5;

[0043] Step 2, add dispersant to the mixture in step 1, the mass ratio of dispersant to silicone resin is 95:2, after stirring for 8 minutes; add temperature-changing powder, the mass ratio of temperature-changing powder to silicone resin is 95:1, and stir for 20 minutes , to obtain coating slurry;

[0044] Step 3: Coat the coating slurry in Step 2 on the silicate fiber twill fabric (one upper and two lower), using one knife coating, the coating thickness is 10 filaments, and the glue amount is 100g / m 2 ;

[0045] Step 4: Curing the coated silicate fiber twill fabric at 180° C. for 2 minutes to obtain an intelligent early-warning temperature-resistant material.

Embodiment 3

[0047] This embodiment discloses a method for preparing an intelligent early-warning temperature-resistant material, which includes the following steps:

[0048] Step 1, silicone resin (the content of hydroxyl group is 2%, the MQ ratio is 0.7) and xylene are mixed according to the mass ratio of 3: 7;

[0049] Step 2, add dispersant to the mixture in step 1, the mass ratio of dispersant to silicone resin is 92:3, after stirring for 5 minutes; add temperature-changing powder, the mass ratio of temperature-changing powder to silicone resin is 92:1.3, after stirring for 15 minutes , to obtain coating slurry;

[0050] Step 3: Coat the coating slurry in Step 2 on the silicate fiber twill fabric (one upper and two lower), using one knife coating, the coating thickness is 15 filaments, and the glue amount is 160g / m 2 ;

[0051] Step 4: Curing the coated silicate fiber twill fabric at 170° C. for 2 minutes to obtain an intelligent early-warning temperature-resistant material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an intelligent early-warning and temperature-resistant material. The preparation method comprises the following steps: 1, mixing silicon resin and a solvent according to the mass ratio being (10-30):(50-70); 2, adding a dispersing agent into the mixture in the step 1 and stirring, and adding temperature-changing powder and stirring uniformly to obtain coating slurry, wherein the mass ratio of the dispersing agent to the silicon resin is (90-95):(2-5), and the mass ratio of the temperature-changing powder to the silicon resin is (90-95):(1-1.5); 3, coating a silicate fiber layer with the coating slurry in the step 2, wherein the coating thickness is 2 to 20 silk, and the gluing quantity is 30 to 220 g / m<2>; and 4, performing curing treatment on the coated silicate fiber layer to obtain the intelligent early-warning and temperature-resistant material. The preparation method of the intelligent early-warning and temperature-resistant material has the following advantages of actively performing early warning, reducing skin allergy probability, improving wearing comfort, having high material internal combining firmness and facilitating postprocessing cutting to make any models.

Description

technical field [0001] The invention relates to the technical field of functional textiles, in particular to a preparation method of an early warning temperature-resistant material and an early warning temperature-resistant material based on the method. Background technique [0002] Heat-resistant materials in the prior art, such as glass fiber-coated PTFE resin high-temperature cloth, glass fiber-coated resin temperature-resistant cloth, aramid fabric, carbon fiber finishing fabric, polyimide fabric, glass limit fabric, etc., are mostly passive. Heat-resistant protective material. That is, effective heat insulation, flame retardancy, and protection are carried out within the allowable temperature range of the material. However, when the external temperature changes or exceeds the limit temperature of the material, since the material itself cannot provide an active warning function, the material will be burned, lose its protective function, and cause burns and other situati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06N3/12D06N3/00D03D15/00
Inventor 王少伟邵亚国
Owner WUXI FIRST SPECIAL TYPE FIBERGLASS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com