High-temperature-resistant packaging material and preparation method thereof

A packaging material and high-temperature-resistant technology, which is applied in the field of packaging materials, can solve problems such as large gaps, and achieve the effects of improving high-temperature resistance, less industrial pollutants, and simple preparation methods

Inactive Publication Date: 2017-12-01
TAISHAN SHIHENG PACKAGING MATERIAL CO LTD
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, for some special purposes, there is a large gap in the packaging materials required in special environments, such as packag

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of preparation method of high temperature resistant packaging material of the present embodiment, comprises the following steps:

[0024] S1: Weigh each raw material component according to the following weight: 20 parts of polyethylene terephthalate, 20 parts of epoxy resin, 8 parts of talcum powder, 5 parts of silicon dioxide, 5 parts of propylene oxide butyl ether, 8 parts of glass fiber powder, 8 parts of aluminum silicate fiber, 10 parts of polyetherimide, 8 parts of diethylenetriaminopropyltrimethylsilane, 8 parts of phenyltriethoxysilane, coupling agent (KH570 ) 3 parts, antioxidant (1010) 3 parts.

[0025] S2: Mix all the components evenly and then add them into the kneader and stir well to obtain the raw material mixture;

[0026] S3: Put the raw material mixture into the extruder, extrude, and then cool to obtain the finished plastic packaging material.

Embodiment 2

[0028] A kind of preparation method of high temperature resistant packaging material of the present embodiment, comprises the following steps:

[0029] S1: Weigh each raw material component according to the following weight: 10 parts of polyethylene terephthalate, 25 parts of epoxy resin, 5 parts of talcum powder, 8 parts of silicon dioxide, 3 parts of propylene oxide butyl ether, 10 parts of glass fiber powder, 5 parts of aluminum silicate fiber, 12 parts of polyetherimide, 5 parts of aminopropyltriethoxysilane, 5 parts of phenylmethyldichlorosilane and phenyltrimethoxysilane, even Joint agent (KH550) 2 parts, antioxidant (168) 2 parts.

[0030] S2: Mix all the components evenly and then add them into the kneader and stir well to obtain the raw material mixture;

[0031] S3: Put the raw material mixture into the extruder, extrude, and then cool to obtain the finished plastic packaging material.

Embodiment 3

[0033] A kind of preparation method of high temperature resistant packaging material of the present embodiment, comprises the following steps:

[0034] S1: Weigh each raw material component according to the following weight: 25 parts of polyethylene terephthalate, 15 parts of epoxy resin, 10 parts of talcum powder, 5 parts of silicon dioxide, 5 parts of propylene oxide butyl ether, 8 parts of glass fiber powder, 10 parts of aluminum silicate fiber, 5 parts of polyetherimide, 10 parts of N-cyclohexyl-γ-aminopropylmethyldimethoxysilane, benzophenone hydrazone as phenylsilane 10 parts, 5 parts of coupling agent (KH560), 3 parts of antioxidant (1098).

[0035] S2: Mix all the components evenly and then add them into the kneader and stir well to obtain the raw material mixture;

[0036] S3: Put the raw material mixture into the extruder, extrude, and then cool to obtain the finished plastic packaging material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-temperature-resistant packaging material and a preparation method thereof. The high-temperature-resistant packaging material is prepared from the following components by weight: 10-25 parts of polyethylene terephthalate, 15-30 parts of epoxy resin, 5-10 parts of talcum powder, 3-8 parts of silicon dioxide, 3-8 parts of glycidyl butyl ether, 5-10 parts of glass fiber powder, 5-10 parts of aluminum silicate fibers, 5-15 parts of polyetherimide, 5-10 parts of aminosilane, 5-10 parts of phenylsilane, 2-5 parts of a coupling agent and 2-5 parts of an antioxidant. Compared with the prior art, the high-temperature-resistant packaging material provided by the invention has the advantages that the high temperature resistance of the packaging material is greatly improved and the application scope of the packaging material is greatly broadened since a variety of environment-friendly high-temperature-resistant raw materials are adopted, a variety of environment-friendly pollution-free industrial additives are used, a coupling agent is employed for improving the interfacial effect of organic substances and inorganic substances and all the components are cooperated with each other.

Description

technical field [0001] The invention relates to the field of packaging materials, in particular to a high-temperature-resistant packaging material and a preparation method thereof. Background technique [0002] Packaging materials refer to materials used in the manufacture of packaging containers, packaging decoration, packaging printing, packaging and transportation to meet product packaging requirements. The packaging of the product is an important part of the product. It not only plays a protective role in the transportation process, but also directly relates to the overall quality of the product. Packaging materials include metal, plastic, glass, ceramics, paper, bamboo, wild mushrooms, natural fibers, chemical fibers, composite materials and other main packaging materials, as well as auxiliary materials such as coatings, adhesives, strapping, decoration and printing materials. Material. [0003] Plastic packaging material is a kind of packaging material that is widely...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08L63/00C08L79/08C08K13/04C08K3/34C08K3/36C08K5/1515C08K7/14C08K7/10C08K5/544C08K5/5415C08K5/5425C08K5/134C08K5/526C08K5/5435
CPCC08L67/02C08K2201/014C08L63/00C08L2201/08C08L2205/03C08L79/08C08K13/04C08K3/34C08K3/36C08K5/1515C08K7/14C08K7/10C08K5/544C08K5/5415C08K5/5425C08K5/1345C08K5/526C08K5/5435C08K5/20
Inventor 甄坤华
Owner TAISHAN SHIHENG PACKAGING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap