An aluminum alloy and orange technology, applied in the field of orange aluminum alloy and its preparation, can solve the problems of environmental pollution, affect people's physical and mental health, cannot meet the needs of modern people's life, etc., and achieve a simple production process, easy promotion and low production cost. Effect

Inactive Publication Date: 2017-12-08
苏州飞伦利斯金属科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Non-ferrous metals in the traditional sense are determined by the color of the metal itself. Generally, paint and other materials need to be coated on its surface after processing for rust prevention and decoration. The production and use of paint will cause serious pollution to the environment. And after use, it will continue to release harmful substances, which will affect people's physical and mental health, and cannot meet the needs of modern people's lives. Therefore, an improved technology is urgently needed to solve the above technical defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] An orange aluminum alloy and a preparation method thereof, comprising the following components in parts by weight: aluminum: 50-80 parts; zinc: 20-40 parts; copper: 5-8 parts; titanium: 4-7 parts, orange pigment: 5-10 servings.

[0020] The orange pigment is a mixture of iron oxide and titanium nickel yellow, and the mass ratio of iron oxide and titanium nickel yellow is 2:1.

[0021] Include the following steps:

[0022] a. Make aluminum, zinc, copper, titanium and orange pigments into powder, the powder fineness is 300-500 mesh;

[0023] b. Mix aluminum, zinc and copper powder and heat to 1000°C;

[0024] c. Heating the titanium powder until it melts;

[0025] d. Add the molten titanium obtained in step c to the molten mixture obtained in step b and stir, keep the temperature at 1000-1200°C, and stir for 3-5 minutes;

[0026] e. Add the orange pigment powder to the alloy mixed melt obtained in step d, keep stirring for 10-15min, and keep the temperature at 900-100...

Embodiment 2

[0029] An orange aluminum alloy and a preparation method thereof, comprising the following components in parts by weight: aluminum: 50-80 parts; zinc: 20-40 parts; copper: 5-8 parts; titanium: 4-7 parts, orange pigment: 5-10 servings.

[0030] The orange pigment is a mixture of iron oxide and titanium nickel yellow, and the mass ratio of iron oxide and titanium nickel yellow is 2:1.

[0031] Include the following steps:

[0032] a. Make aluminum, zinc, copper, titanium and orange pigments into powder, the powder fineness is 300-500 mesh;

[0033] b. Mix aluminum, zinc and copper powder and heat to 1000°C;

[0034] c. Heating the titanium powder until it melts;

[0035] d. Add the molten titanium obtained in step c to the molten mixture obtained in step b and stir, keep the temperature at 1000-1200°C, and stir for 3-5 minutes;

[0036] e. Add the orange pigment powder to the alloy mixed melt obtained in step d, keep stirring for 10-15min, and keep the temperature at 900-100...

Embodiment 3

[0039] An orange aluminum alloy and a preparation method thereof, comprising the following components in parts by weight: aluminum: 50-80 parts; zinc: 20-40 parts; copper: 5-8 parts; titanium: 4-7 parts, orange pigment: 5-10 servings.

[0040] The orange pigment is a mixture of iron oxide and titanium nickel yellow, and the mass ratio of iron oxide and titanium nickel yellow is 2:1.

[0041] Include the following steps:

[0042] a. Make aluminum, zinc, copper, titanium and orange pigments into powder, the powder fineness is 300-500 mesh;

[0043] b. Mix aluminum, zinc and copper powder and heat to 1000°C;

[0044] c. Heating the titanium powder until it melts;

[0045] d. Add the molten titanium obtained in step c to the molten mixture obtained in step b and stir, keep the temperature at 1000-1200°C, and stir for 3-5 minutes;

[0046] e. Add the orange pigment powder to the alloy mixed melt obtained in step d, keep stirring for 10-15min, and keep the temperature at 900-100...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an orange aluminum alloy and a preparation method thereof. The yellow aluminum alloy comprises the following components in parts by weight: 50-80 parts of aluminum, 20-40 parts of zinc, 5-8 parts of copper, 4-7 parts of titanium and 5-10 parts of an orange pigment. The preparation method comprises the following steps of: a, preparing aluminum, zinc, copper, titanium and orange pigment into powder, wherein the fineness of the powder is 300-500 meshes; b, mixing and heating the copper, zinc and copper powder to 1000 DEG C; c, heating the titanium powder till the titanium powder is molten; and d, adding the molten titanium obtained in the step c into the molten mixture obtained in the step b and stirring the mixture, keeping the temperature at 1000-1200 DEG and stirring the mixture for 3-5min. The orange aluminum alloy provided by the invention provided by the invention has the beneficial effects that the manufacturing process is simple and the manufacturing cost is relatively low; an anti-rust or decorative coating needs not to be sprayed to the surface of a product, so that no harmful substances are released, the demand of people on health is met, and the orange aluminum alloy is easy to popularize.

Description

technical field [0001] The invention relates to an alloy metal preparation method, in particular to an orange aluminum alloy and a preparation method thereof. Background technique [0002] Non-ferrous metal alloys are widely used, mainly used in automobiles, building materials, home appliances, electric power, 3C, machinery manufacturing and other industries. In recent years, industries such as automobiles, building materials, home appliances, electric power, 3C, and machinery manufacturing have shown a trend of rapid development, while the development of the non-ferrous metal alloy manufacturing industry relies on the pull of downstream industries. With the development of downstream industries, the non-ferrous metal alloy manufacturing industry has also gained Rapid development. Non-ferrous metal alloys are widely used, mainly used in automobiles, building materials, home appliances, electric power, 3C, machinery manufacturing and other industries. In recent years, indust...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/10C22C1/02
CPCC22C1/026C22C21/10
Inventor 王晶
Owner 苏州飞伦利斯金属科技有限公司