A kind of self-adhesive wide-width foamed carpet floor film and preparation method thereof

A carpet type and floor membrane technology, applied in the field of building decoration materials, can solve the problems of non-self-adhesive cost, floor membrane width and narrowness, etc., and achieve the effects of prolonging service life, high authenticity rate, and reducing workload

Active Publication Date: 2020-01-07
QUZHOU LONGWEI PLASTIC
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problems of narrow width, non-self-adhesive and high cost of traditional carpet floor membranes, and provide a preparation method and application of self-adhesive wide-width foamed carpet floor membranes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of self-adhesive wide-width foamed carpet floor film and preparation method thereof
  • A kind of self-adhesive wide-width foamed carpet floor film and preparation method thereof
  • A kind of self-adhesive wide-width foamed carpet floor film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] (1) Put the raw material PVC resin powder, azodicarbonamide (AC), calcium-zinc composite stabilizer, and dioctyl phthalate (DOP) into a high-speed mixer and mix evenly for 20 minutes until the solid particles are mixed evenly Finally, add plasticizer and other liquid additives, and mix for 20 minutes until the plasticizer and other liquid additives are all absorbed by solid particles;

[0048] (2) Place the homogeneously mixed raw materials in the above step (1) to dry in a dryer at a temperature of 80°C, and promote resin mixing while drying until the water is completely volatilized;

[0049] (3) Put the uniformly mixed and fully dried raw materials in the above step (2) into a screw extruder to melt and extrude, the screw speed is 15r / min, and the temperature of each zone of the screw is 150-180°C;

[0050] (4) Press the PVC resin mixture extruded in the above step (3) and the needle felt through a 4.5m roller machine and a laminating machine for 20s, and the pressing...

Embodiment 2

[0054] Compared with Example 1, the mixing time of raw material PVC resin powder, azodicarbonamide (AC), calcium-zinc composite stabilizer, dioctyl phthalate (DOP) in the first step becomes 15min, other Conditions remain the same.

Embodiment 3

[0056] Compared with Example 1, the mixing time of PVC resin powder, azodicarbonamide (AC), calcium-zinc composite stabilizer, dioctyl phthalate (DOP) in the first step becomes 15min, other conditions constant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
decomposition temperatureaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a self-adhesion wide foamed carpet-type floor membrane comprising an adhesive layer, a PVC composite layer, a needled felt layer and an ink layer which are arranged sequentially. The PVC composite layer is obtained by laminating of by weight, 90-120 parts of PVC resin powder, 0.2-1.0 part of azodicarbonamide, 2.5-5.0 parts of calcium-zincum composite heat stabilizers and 30-45 parts of dioctyl phthalate with needled felt through a calender and a laminating machine. The self-adhesion wide foamed carpet-type floor membrane is clear in pattern and attractive in appearance, has the self-adhesion property and is simple in laying process, and self-leveling is not needed; the decorated space is warmer and sweeter; and the processing size and the product width are both 3.6-5.0 m, so that the self-adhesion wide foamed carpet-type floor membrane is suitable for the using occasion with the large decorating area, connecting seams can be avoided or the number of the connecting seams can be reduced in the laying process, and sweeping and maintenance in the future using process are facilitated.

Description

technical field [0001] The invention relates to the field of building decoration materials, in particular to a preparation method and application of a self-adhesive wide-width foamed carpet floor film. Background technique [0002] With the rapid development of my country's economy, people's living conditions and economic income have been further improved. At the same time, people have put forward higher requirements for interior decoration materials. For floor covering materials, compared with the cold "hard decoration materials" such as ceramic floors or wooden floors in the past, the carpet floor film "soft decoration materials" can not only significantly improve the comfort, but also have richer fabric varieties and more colorful colors. It is also more colorful and can match different interior decoration styles, which further improves the integrity and aesthetics of the living room and makes the living and working environment more comfortable and warm. [0003] However...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04F15/16C08L27/06C08K5/12C08J9/10
CPCC08J9/103C08J2203/04C08K5/12C08L2203/14E04F15/163C08L27/06
Inventor 郑耀波
Owner QUZHOU LONGWEI PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com