Molten-blown composite plant fiber non-woven whitening facial mask and preparation method thereof

A plant fiber and whitening mask technology, applied in melt spinning, non-woven fabrics, pharmaceutical formulations, etc., can solve the problems of insignificant skin care effects and poor whitening effects, so as to inhibit melanin production, promote metabolism, and improve immunity Effect

Inactive Publication Date: 2018-01-09
ANHUI YICAINI FIBER MATERIALS TECH
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the defects of poor whitening effect and inconspicuous skin care effect in the prior art, and provide a kind of melt-blown composite plant fiber non-woven fabric whitening mask and its preparation method to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Molten-blown composite plant fiber non-woven whitening facial mask and preparation method thereof
  • Molten-blown composite plant fiber non-woven whitening facial mask and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] As a preference, the present invention also discloses a method for preparing the above-mentioned melt-blown composite plant fiber non-woven fabric whitening mask, the steps are as follows:

[0036] (1), according to the above-mentioned parts by weight, mix and stir the plant fiber and polyester evenly to obtain a mixture;

[0037] (2), using a screw extruder to melt the mixture into a melt;

[0038] (3), using a melt filter to filter the melt;

[0039] (4) The melt is extruded from the spinneret through the spinning die, and under the action of the cooling wind, the melt stream is cooled and drafted to form fibers through the drafting air duct;

[0040] (5) Pass the fibers through the diffusion air duct, so that the fibers are evenly adsorbed on the web-forming conveyor belt, forming a continuous mesh fiber layer;

[0041] (6), adopt hot-rolling mill to prepare non-woven fabric with continuous reticular fiber layer;

[0042] (7), soak the prepared non-woven fabric in...

Embodiment 1

[0049] The invention discloses a whitening facial mask of melt-blown composite plant fiber non-woven fabric, which is prepared from the following components in terms of mass percentage: 40 parts of plant fiber and 30 parts of polyester.

[0050] The plant fiber adopts honeysuckle.

[0051]As a preference, the present invention also discloses a method for preparing the above-mentioned melt-blown composite plant fiber non-woven fabric whitening mask, the steps are as follows:

[0052] (1), according to the above-mentioned parts by weight, mix and stir the plant fiber and polyester evenly to obtain a mixture;

[0053] (2), using a screw extruder to melt the mixture into a melt;

[0054] (3), using a melt filter to filter the melt;

[0055] (4) The melt is extruded from the spinneret through the spinning die, and under the action of the cooling wind, the melt stream is cooled and drafted to form fibers through the drafting air duct;

[0056] (5) Pass the fibers through the diff...

Embodiment 2

[0064] The invention discloses a whitening facial mask of melt-blown composite plant fiber non-woven fabric, which is prepared from the following components in terms of mass percentage: 35 parts of plant fiber and 35 parts of polyester.

[0065] The plant fiber adopts mint leaves.

[0066] The present invention also discloses a preparation method of the above-mentioned melt-blown composite plant fiber non-woven fabric whitening mask, the steps are as follows:

[0067] (1), according to the above-mentioned parts by weight, mix and stir the plant fiber and polyester evenly to obtain a mixture;

[0068] (2), using a screw extruder to melt the mixture into a melt;

[0069] (3), using a melt filter to filter the melt;

[0070] (4) The melt is extruded from the spinneret through the spinning die, and under the action of the cooling wind, the melt stream is cooled and drafted to form fibers through the drafting air duct;

[0071] (5) Pass the fibers through the diffusion air duct,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a molten-blown composite plant fiber non-woven whitening facial mask and a preparation method thereof. The facial mask is prepared from the following components in parts by weight: 35-45 parts of a plant fiber and 25-35 parts of polyester. The preparation method comprises the following steps: uniformly mixing and stirring the plant fiber and the polyester according to the parts by weight so as to obtain a mixed material; melting the mixed material into a melt by using a screw extruder; filtering the melt by using a melt filter; extruding the melt from spinneret orificesby using a spinning mold, and under the action of cooling air, performing cooling tension molding on the fine melt flow through a tension channel so as to form a fiber; uniformly sucking the fiber toa reticular conveyer belt through a diffusion air channel so as to form a continuous reticular fiber layer; preparing non-woven cloth from the continuous reticular fiber layer by using a hot-pressingmachine; soaking the prepared non-woven cloth in fibroin fluid; preparing a paste from a nutrient solution, coating the non-woven cloth with the nutrient solution, and performing sealing packaging. The facial mask has the advantages of a remarkable skin-caring function, an excellent whitening effect, and the like.

Description

technical field [0001] The invention relates to the field of non-woven facial mask preparation, in particular to a melt-blown composite plant fiber non-woven whitening facial mask and a preparation method thereof. Background technique [0002] Mask, the principle of the mask is to use the short time covered on the face to temporarily isolate the outside air and pollution, increase the temperature of the skin, expand the pores of the skin, promote the secretion and metabolism of the sweat glands, and increase the oxygen content of the skin. The mask is beneficial The skin eliminates the products of epidermal cell metabolism and accumulated oily substances. The moisture in the mask penetrates into the stratum corneum of the skin’s epidermis, making the skin soft and elastic. If you want the mask to have whitening and moisturizing effects, you must choose a professional skin care mask. Professional products do not irritate or harm the skin, so you can use them safely and safely...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/98A61K8/9789A61K8/9794A61K8/92A61K8/64A61K8/02A61Q19/00A61Q19/02D01D5/08D04H3/00D04H3/147
Inventor 章云张贝尼张娃妮柯模松
Owner ANHUI YICAINI FIBER MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com