Adsorptive environment-friendly type waterborne synthetic leather base and preparation method thereof

A synthetic leather bass, environmentally friendly technology, applied in the field of synthetic leather, to achieve the effects of low cost, good air permeability and fine texture

Inactive Publication Date: 2018-01-09
遂昌玄乐炭复合材料有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] "Nanchang University" 2011 master's thesis "Exploration of Aqueous Polyurethane Acid Bath Coagulation Film Formation" paper discloses the use of acetic acid to foam water-based polyurethane emulsion to prepare synthetic leather, but also discloses that the surface and cross-section of WPU acid bath demulsification method have There are ma

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adsorptive environment-friendly type waterborne synthetic leather base and preparation method thereof
  • Adsorptive environment-friendly type waterborne synthetic leather base and preparation method thereof
  • Adsorptive environment-friendly type waterborne synthetic leather base and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0041] Example 1

[0042] The formula of waterborne polyurethane coating is as follows:

[0043] Waterborne polyurethane emulsion

[0044] A production method of environmentally friendly waterborne polyurethane synthetic leather bass, the method includes the following steps:

[0045] 1) Before squeegee, the base cloth is soaked in bamboo vinegar liquid, the pH of the bamboo vinegar liquid is 3.5, so that the base cloth is soaked in the bamboo vinegar liquid, and then squeezed dry;

[0046] 2) The base fabric is scraped and coated with the above-mentioned water-based polyurethane coating, and the water-based polyurethane layer is solidified on the surface of the base fabric and squeezed out;

[0047] 3) After squeezing dry, enter the bamboo vinegar solution for foaming. The pH of the bamboo vinegar solution is 3.2 and the foaming time is 2 minutes to form a porous polyurethane coating. The coating amount of the water-based polyurethane layer is 40g / m 2 ;

[0048] 4) Wash with water aft...

Example Embodiment

[0094] Example 2

[0095] The formula of waterborne polyurethane coating is as follows:

[0096] Waterborne polyurethane emulsion

[0097] A production method of environmentally friendly waterborne polyurethane synthetic leather bass, the method includes the following steps:

[0098] 1) Before squeegee, the base cloth is soaked in bamboo vinegar liquid, the pH of the bamboo vinegar liquid is 3.5, so that the base cloth is soaked in the bamboo vinegar liquid, and then squeezed dry;

[0099] 2) The base fabric is scraped and coated with the above-mentioned water-based polyurethane coating, and the water-based polyurethane layer is solidified on the surface of the base fabric and squeezed out;

[0100] 3) After squeezing dry, enter the bamboo vinegar solution for foaming. The pH of the bamboo vinegar solution is 3.2 and the foaming time is 2 minutes to form a porous polyurethane coating. The coating amount of the water-based polyurethane layer is 40g / m 2 ;

[0101] 4) Wash with water aft...

Example Embodiment

[0111] Example 3

[0112] The formula of waterborne polyurethane coating is as follows:

[0113] Waterborne polyurethane emulsion

[0114] A production method of environmentally friendly waterborne polyurethane synthetic leather bass, the method includes the following steps:

[0115] 1) Before squeegee, the base cloth is soaked in bamboo vinegar liquid, the pH of the bamboo vinegar liquid is 3.5, so that the base cloth is soaked in the bamboo vinegar liquid, and then squeezed dry;

[0116] 2) The base fabric is scraped and coated with the above-mentioned water-based polyurethane coating, and the water-based polyurethane layer is solidified on the surface of the base fabric and squeezed out;

[0117] 3) After squeezing dry, enter the bamboo vinegar solution for foaming. The pH of the bamboo vinegar solution is 3.2 and the foaming time is 2 minutes to form a porous polyurethane coating. The coating amount of the water-based polyurethane layer is 40g / m 2 ;

[0118] 4) Wash with water aft...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of synthetic leather, and in particular to an adsorptive environment-friendly type waterborne synthetic leather base and a preparation method thereof. The adsorptiveenvironment-friendly type waterborne synthetic leather base is characterized in that waterborne synthetic leather is prepared by foaming base cloth by adopting bamboo vinegar after coating the base cloth by adopting a waterborne polyurethane coating material, wherein the waterborne polyurethane coating material is prepared from the following components in percentage by mass: 20 to 60 percent of waterborne polyurethane emulsion, 5 to 15 percent of wood powder and/or wood pulp, 2.0 to 20 percent of an adsorptive material, 0 to 20 percent of calcium carbonate and 0.1 to 2.0 percent of a processing agent. According to the adsorptive environment-friendly type waterborne synthetic leather base disclosed by the invention, the bamboo vinegar is adopted for foaming, generation of an acetic acid foaming microporous structure is avoided, the tensile strength, the tear strength and the wear resistance can achieve the level of DMF (Dimethyl Formamide) wet foaming, DMF is not used in the whole process, formaldehyde and the DMF in an obtained synthetic leather product are not detected, and requirements of ecological synthetic leather can be met.

Description

technical field [0001] The invention relates to the field of synthetic leather, in particular to an absorbent and environment-friendly water-based synthetic leather base and a preparation method thereof. Background technique [0002] The production method of wet-process polyurethane synthetic leather is to add DMF solvent and other fillers and additives to polyurethane wet-process resin to make a mixed solution. (DMF) has affinity, and the water that is incompatible with polyurethane resin, the solvent (DMF) is replaced by water, and the polyurethane resin gradually solidifies, thus forming a porous film, that is, the microporous polyurethane grain layer, which is customarily called bass (Transliteration of English BASS), which means the base material (semi-finished leather). Bass can only become polyurethane synthetic leather after dry veneer or surface finishing, such as surface printing, embossing, grinding and other processes. finished product. [0003] The typical syn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/00D06N3/14C09D175/04C09D5/14
Inventor 管宁章管玄谢永水
Owner 遂昌玄乐炭复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka