Preparation method of bi-color artificial quartz stone slate

A quartz stone plate, artificial technology, applied in the field of architectural decoration, can solve the problems of surface bacterial pollution, bacteria not inhibited or killed, etc., and achieve the effects of good flatness, long-lasting photocatalysis, and excellent wettability

Inactive Publication Date: 2018-01-19
佛山市欧泊石业有限公司
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the artificial quartz stone in the prior art also has its inherent disadvantages, such as (1) the surface of the artificial quartz stone will inevitably be contaminated by bacteria when used, but ordinary artificial quartz stone has no effect on inhibiting or killing bacteria (2) People have higher and higher requirements for the pattern and color of artificial quartz stones, and the existing artificial quartz stones can no longer fully meet people's needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A two-color artificial quartz stone plate, which is made of the following raw materials in parts by weight: 35 parts of 9-15 mesh glass particles, 18 parts of artificial quartz particles, 22 parts of natural quartz sand, 18 parts of 160-1200 mesh quartz powder, resin 6 parts, 0.3 parts of curing agent, 0.3 parts of coupling agent, 0.6 parts of pigment, 2 parts of antibacterial agent; wherein, the pigment includes iron red powder and iron black powder.

[0042] The resin is formed by mixing components A and B, and the B component is a brominated epoxy resin, wherein the weight ratio of the A component to the B component is 1:1.3; the A component It is made of the following parts by weight: 30-40 parts of 2-methyl-1,3-propanediol, 40-50 parts of benzoic acid, 25-30 parts of glycerol, 38-42 parts of phthalic acid, cis 20-22 parts of butenedioic acid, 50-60 parts of vinyl acetate, 0.2-0.5 parts of simethicone, and 1-2 parts of hydroquinone.

[0043] The preparation method ...

Embodiment 2

[0062] A two-color artificial quartz stone plate, which is made of the following raw materials in parts by weight: 30 parts of 9-15 mesh glass particles, 24 parts of artificial quartz particles, 15 parts of natural quartz sand, 25 parts of 160-1200 mesh quartz powder, resin 5 parts, 0.1 part of curing agent, 0.1 part of coupling agent, 0.2 part of pigment, 1 part of antibacterial agent; wherein, the pigment includes iron red powder and iron black powder.

[0063] The resin is formed by mixing components A and B, and the B component is a brominated epoxy resin, wherein the weight ratio of the A component to the B component is 1:1.2; the A component It is made of the following parts by weight: 30-40 parts of 2-methyl-1,3-propanediol, 40-50 parts of benzoic acid, 25-30 parts of glycerol, 38-42 parts of phthalic acid, cis 20-22 parts of butenedioic acid, 50-60 parts of vinyl acetate, 0.2-0.5 parts of simethicone, and 1-2 parts of hydroquinone.

[0064] The preparation method of t...

Embodiment 3

[0083] A two-color artificial quartz stone plate, which is made of the following raw materials in parts by weight: 40 parts of 9-15 mesh glass particles, 13 parts of artificial quartz particles, 30 parts of natural quartz sand, 25 parts of 160-1200 mesh quartz powder, resin 7 parts, 0.5 parts of curing agent, 0.5 parts of coupling agent, 1 part of pigment, and 3 parts of antibacterial agent; wherein, the pigment includes iron red powder and iron black powder.

[0084] Described resin is formed by mixing A component and B component, and described B component is brominated epoxy resin, and wherein, the weight ratio of described A component and B component is 1: 1.5; It is made of the following parts by weight: 30-40 parts of 2-methyl-1,3-propanediol, 40-50 parts of benzoic acid, 25-30 parts of glycerol, 38-42 parts of phthalic acid, cis 20-22 parts of butenedioic acid, 50-60 parts of vinyl acetate, 0.2-0.5 parts of simethicone, and 1-2 parts of hydroquinone.

[0085] The prepar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a bi-color artificial quartz stone slate. The method comprises steps as follows: (1) raw materials are weighed in proportion and stored separately; (2)an antibacterial agent is added to resin and stirred and mixed in vacuum; pigments, a coupling agent, glass particles, artificial quartz particles, natural quartz sand and quartz powder are stirred and mixed in vacuum; finally, a curing agent is added and stirred and mixed in vacuum, and a mixture is obtained; (3) the mixture is uniformly spread on a template; (4) the template is sent into a vacuum vibration forming press for vibratory pressing forming; (5) primary curing and secondary curing are performed sequentially after vibratory pressing forming. The mechanical properties such as hardness, toughness and the like of the artificial quartz stone slate are effectively improved through optimization and improvement of a raw material formula, matching of different raw materials and improvement of the preparation method, the artificial quartz stone slate has high anti-bacterial ability and lasting anti-bacterial action, and the comprehensive performance of the artificial quartz stone slate is improved.

Description

technical field [0001] The invention relates to the technical field of architectural decoration, in particular to a preparation method of a two-color artificial quartz stone plate. Background technique [0002] Artificial quartz stone (or diamond / corundum) originated in Spain. It was called Celite when it entered China in 2005. When artificial quartz stone was recognized by more and more consumers, in 2006, some people in China began to develop artificial quartz. Stone, in 2007, many manufacturers have launched domestic artificial quartz stone. As a new type of artificial building material, artificial quartz stone has incomparable advantages of natural stone in terms of moisture resistance, acid resistance, and splicability. Today, as natural stone resources are becoming increasingly depleted, artificial quartz stone is the best substitute. At the same time, artificial quartz stone can use waste glass as raw material, thus realizing resource reuse while protecting the envi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/14B28B1/087B28B3/02B28B11/24C04B111/54C04B111/20
Inventor 陆顺欢
Owner 佛山市欧泊石业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com