Stone-like coating

A technology of real stone paint and natural colored sand, applied in the field of wall building materials, which can solve the problems of affecting the appearance, the coating becomes soft and white, and whitening when exposed to water, so as to improve water whitening resistance, widen pores, and avoid external moisture the effect of passing

Inactive Publication Date: 2018-01-19
常州杰轩纺织科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The main technical problem to be solved by the present invention is: after the real stone paint coating is dried, it is easy to appear whitening when it encounters water, especially in the early stage of drying, when it encounters rainy weather, the coating will become soft and white after being washed by rain for a long time. Problems that affect the appearance, the invention provides a real stone paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0025]In parts by weight, take 50 parts of lichens, 50 parts of milk, and 100 parts of water successively, pour them into a mortar, grind for 30 minutes, and obtain a homogenate of lichens; add natural colored sand into a pulverizer, pass through a 200-mesh sieve after pulverization, Add the sifted natural colored sand and lichen homogenate into the beaker according to the mass ratio of 1:20, stir and mix with a glass rod for 20 minutes to obtain a mixed mortar, and spread the obtained mixed mortar evenly on the tray, and place the tray Move it into the refrigerator, freeze for 5 hours at -18°C, take out the tray, and culture at a constant temperature and humidity for 5 days under the conditions of light intensity of 400Lx, temperature of 15°C, and humidity of 70%. The constant humidity cultivation cycle is 10 times, and the mixed mortar obtained from the last light constant temperature and humidity cultivation is frozen and pulverized to obtain pulverized wet material, and the...

example 2

[0027] In parts by weight, take 50 parts of lichens, 50 parts of milk, and 100 parts of water successively, pour them into a mortar, grind for 30 minutes, and obtain a homogenate of lichens; add natural colored sand into a pulverizer, pass through a 200-mesh sieve after pulverization, Add the sifted natural colored sand and lichen homogenate into the beaker according to the mass ratio of 1:20, stir and mix with a glass rod for 20 minutes to obtain a mixed mortar, and spread the obtained mixed mortar evenly on the tray, and place the tray Move it into the refrigerator, freeze for 5 hours at -18°C, take out the tray, and culture at a constant temperature and humidity for 5 days under the conditions of light intensity of 400Lx, temperature of 15°C, and humidity of 70%. The constant humidity cultivation cycle is 10 times, and the mixed mortar obtained from the last light constant temperature and humidity cultivation is frozen and pulverized to obtain pulverized wet material, and th...

example 3

[0029] In parts by weight, take 50 parts of lichens, 50 parts of milk, and 100 parts of water successively, pour them into a mortar, grind for 30 minutes, and obtain a homogenate of lichens; add natural colored sand into a pulverizer, pass through a 200-mesh sieve after pulverization, Add the sifted natural colored sand and lichen homogenate into the beaker according to the mass ratio of 1:20, stir and mix with a glass rod for 20 minutes to obtain a mixed mortar, and spread the obtained mixed mortar evenly on the tray, and place the tray Move it into the refrigerator, freeze for 5 hours at -18°C, take out the tray, and culture at a constant temperature and humidity for 5 days under the conditions of light intensity of 400Lx, temperature of 15°C, and humidity of 70%. The constant humidity cultivation cycle is 10 times, and the mixed mortar obtained from the last light constant temperature and humidity cultivation is frozen and pulverized to obtain pulverized wet material, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a stone-like coating and belongs to the technical field of wall building materials. The stone-like coating comprises, by weight, 10 to 20 parts of an emulsion, 10 to 20 parts of water, 60 to 80 parts of modified natural colored sand, 0.3 to 0.5 parts of a film-forming aid, 6 to 10 parts of an agar solution, 0.1 to 0.3 parts of a thickener, 0.1 to 0.2 parts of a defoaming agent, 0.2 to 0.6 parts of a bactericide, 0.8 to 1.5 parts of an antifreezing agent and 0.03 to 0.05 parts of a pH buffer agent. The modified natural colored sand is prepared through homogenizing natural colored sand and lichen, carrying out refrigeration, carrying out illumination constant-temperature constant-humidity culture circulation and carrying out carbonization and quenching. The stone-likecoating can form a compact film on the base surface, prevent permeation of inner water and outer water and effectively improve the water bleaching resistance of the product.

Description

technical field [0001] The invention discloses a real stone paint, which belongs to the technical field of wall surface building materials. Background technique [0002] Natural stone is often used as a building decoration material due to its colorful and natural texture appearance, but its disadvantages are heavy weight, increased load on the wall, complex construction and brittle cracks, and many unsafe factors, which make Its application is subject to certain restrictions. Real stone paint is a synthetic resin emulsion sand-wall architectural coating made of natural granite, crushed stone and stone powder as aggregates, synthetic resin emulsion as the base material and a variety of additives. It not only has a decorative effect similar to marble and granite. , giving people an elegant, harmonious and solemn aesthetic feeling, and has good fire and water resistance, acid and alkali resistance, pollution resistance, strong adhesion, and light fading. It can effectively pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/32C04B20/02C04B20/04
Inventor 王海霞许蘅张琳
Owner 常州杰轩纺织科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com