Adhesive for white and transparent OPP (Oriented Polypropylene) adhesive tape and processing technology thereof

A technology of adhesives and tapes, applied in the direction of adhesives, polymer adhesive additives, film/sheet adhesives, etc., can solve the problems of increasing research and development costs and complicated processes, so as to save research and development and production costs and simplify synthesis Craftsmanship, the effect of meeting market demand

Inactive Publication Date: 2018-02-16
福建友谊胶粘带集团有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In aerospace, transportation, medical and industrial equipment, automobiles, home appliances, and electronics markets, it can be used for bonding nameplates and labels; currently, the general OPP tape on the market is slightly yellowish, in order to meet some markets The needs, especially in Southeast Asia, need some white OPP tapes. For this reason, many OPP tapes add chemical pigments to the original adhesive to make the adhesive white, but this increases the research and development costs. The synthesis process is complicated. For example, the patent CN101805577A discloses a transparent epoxy resin encapsulation adhesive. A transparent blue-violet dye paste is added to the glue, thereby neutralizing the yellow color produced by the epoxy resin.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive for white and transparent OPP (Oriented Polypropylene) adhesive tape and processing technology thereof
  • Adhesive for white and transparent OPP (Oriented Polypropylene) adhesive tape and processing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of processing technology for the adhesive of white transparent OPP adhesive tape, comprises the steps:

[0035] (1) Add 3.0 parts by weight of ethoxyethanol sulfosuccinate disodium salt, 1.0 parts by weight of polyethoxylated fatty alcohol and 100 parts by weight of deionized water into the emulsification tank and stir for 20 minute;

[0036] (2) 280 parts by weight of butyl acrylate, 60 parts by weight of isooctyl acrylate, 4 parts by weight of acrylic acid, 7.0 parts by weight of hydroxyethyl acrylate, 0.1 parts by weight of n-dodecyl mercaptan, 12 parts by weight of acrylic acid Methyl methyl ester, 0.1 parts by weight of OT-75 and 0.1 parts by weight of polydimethylsiloxane are added to the container and mixed thoroughly, then added to the emulsification tank containing the solution of step (1), and stirred for 10 minutes to form a pre-emulsion ;

[0037] (3) when the temperature is 60 DEG C, adding the concentration of 75 parts by weight to the reactor is ...

Embodiment 2

[0049] A kind of processing technology for the adhesive of white transparent OPP adhesive tape, comprises the steps:

[0050](1) Add 3.5 parts by weight of ethoxyethanol sulfosuccinate disodium salt, 1.5 parts by weight of polyethoxylated fatty alcohol and 120 parts by weight of deionized water into the emulsification tank and stir for 25 minute;

[0051] (2) 330 parts by weight of butyl acrylate, 70 parts by weight of isooctyl acrylate, 5 parts by weight of acrylic acid, 7.4 parts by weight of hydroxyethyl acrylate, 0.2 parts by weight of n-dodecyl mercaptan, 13 parts by weight of acrylic acid Methyl methyl ester, 0.2 parts by weight of OT-75 and 0.2 parts by weight of polydimethylsiloxane are added to the container and mixed thoroughly, then added to the emulsification tank containing the solution of step (1), and stirred for 10 minutes to form a pre-emulsion ;

[0052] (3) when temperature is 65 ℃, adding the concentration of 90 parts by weight to the reactor is an aqueou...

Embodiment 3

[0064] A kind of processing technology for the adhesive of white transparent OPP adhesive tape, comprises the steps:

[0065] (1) Add 4.0 parts by weight of ethoxyethanol sulfosuccinate disodium salt, 1.7 parts by weight of polyethoxylated fatty alcohol and 110 parts by weight of deionized water into the emulsification tank and stir for 25 minute;

[0066] (2) 310 parts by weight of butyl acrylate, 75 parts by weight of isooctyl acrylate, 4 parts by weight of acrylic acid, 8.2 parts by weight of hydroxyethyl acrylate, 0.2 parts by weight of n-dodecyl mercaptan, 13 parts by weight of acrylic acid Methyl methyl ester, 0.2 parts by weight of OT-75 wetting agent and 0.1 parts by weight of polydimethylsiloxane are added to the container and mixed thoroughly, then added to the emulsification tank containing the solution of step (1), and stirred for 14 minutes. Form a pre-emulsion;

[0067] (3) when the temperature is 63 DEG C, adding the concentration of 85 parts by weight to the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an adhesive for a white and transparent OPP (Oriented Polypropylene) adhesive tape and a processing technology thereof. The adhesive is mainly prepared from the following raw materials: butyl acrylate, isooctyl acrylate, acrylic acid, hydroxyethyl acrylate, dodecanethiol, methyl methacrylate, an emulsifier, a wetting agent, a de-foaming agent, an initiator and a preservative. According to the adhesive disclosed by the invention, other raw materials do not need to be added and the adhesive tape can have a white and transparent effect; the research and development cost isreduced; meanwhile, a synthesis technology is simplified.

Description

technical field [0001] The invention relates to an adhesive used for white transparent OPP tape and a processing technology thereof, belonging to the technical field of adhesives. Background technique [0002] With the rapid development of society, all kinds of tapes have become indispensable items in electronics, hardware, electrical appliances and other industries. In aerospace, transportation, medical and industrial equipment, automobiles, home appliances, and electronics markets, it can be used for bonding nameplates and labels; currently, the general OPP tape on the market is slightly yellowish, in order to meet some markets The needs, especially in Southeast Asia, need some white OPP tapes. For this reason, many OPP tapes add chemical pigments to the original adhesive to make the adhesive white, but this increases the research and development costs. The synthesis process is complicated. For example, patent CN101805577A discloses a transparent epoxy resin encapsulation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/08C09J129/04C09J11/08C09J7/30C08F220/18C08F220/06C08F220/20C08F220/14C08F2/30C08F2/26C08F2/38
CPCC08F2/26C08F2/30C08F2/38C08F220/18C08F220/1804C08L2205/035C09J7/00C09J11/08C09J133/066C08L29/04C08L83/04C08L71/02C08F220/1808C08F220/06C08F220/20C08F220/14
Inventor 李文森林子清林克波林克品林克兴
Owner 福建友谊胶粘带集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com