A packaging material and easy-to-degrade technology, which is applied in the field of preparation of easily-degradable packaging materials, can solve the problems of difficult-to-degrade polymer packaging materials and pollution, and achieve the effects of improving degradable performance, environmental friendliness, and reducing degradation time

Inactive Publication Date: 2018-02-23
周顺花
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional polymer packaging materials are difficult to degrade in nature. While bringing convenience to peopl

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] Example one

[0016] A preparation method of easily degradable packaging material includes the following steps:

[0017] 1) Calcium carbonate and montmorillonite mixed ball milled to an average particle size of 200nm to obtain filler mixed powder; in parts by weight, the distribution ratio of each component is: calcium carbonate 70 parts, montmorillonite 30 parts;

[0018] 2) Take step 1) and mix the prepared filler mixed powder with lignocellulose and iron stearate to obtain modified mixed powder; in parts by weight, the distribution ratio of each component is: 28 parts of filler mixed powder and 12 parts of lignocellulose , 8 parts of iron stearate;

[0019] 3) The modified mixed powder prepared in step 2) is mixed with polypropylene in a weight ratio of 1:3, and placed in a screw extruder for extrusion and granulation. The extruder has an extrusion working temperature of 165℃-260 ℃.

Example Embodiment

[0020] Example two

[0021] A preparation method of easily degradable packaging material includes the following steps:

[0022] 1) Calcium carbonate and montmorillonite mixed ball milled to an average particle size of 500nm to obtain filler mixed powder; in parts by weight, the distribution ratio of each component is: calcium carbonate 70 parts, montmorillonite 30 parts;

[0023] 2) Take step 1) and mix the prepared filler mixed powder with lignocellulose and iron stearate to obtain modified mixed powder; in parts by weight, the distribution ratio of each component is: 25 parts of filler mixed powder and 8 parts of lignocellulose , 6 parts of iron stearate;

[0024] 3) The modified mixed powder prepared in step 2) is mixed with polypropylene in a weight ratio of 1:3-5, and placed in a screw extruder for extrusion granulation. The working temperature of the extruder is 200°C-230 ℃.

Example Embodiment

[0025] Example three

[0026] A preparation method of easily degradable packaging material includes the following steps:

[0027] 1) Calcium carbonate and montmorillonite mixed ball milled to an average particle size of 500nm to obtain filler mixed powder; in parts by weight, the distribution ratio of each component is: calcium carbonate 70 parts, montmorillonite 30 parts;

[0028] 2) Take step 1) and mix the prepared filler mixed powder with lignocellulose and iron stearate to obtain modified mixed powder; in parts by weight, the distribution ratio of each component is: 25 parts of filler mixed powder and 8 parts of lignocellulose , 6 parts of iron stearate;

[0029] 3) The modified mixed powder prepared in step 2) is mixed with polypropylene in a weight ratio of 1:5, and placed in a screw extruder for extrusion granulation, and the working temperature of the extruder is 200°C-230°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of an easily-degradable packing material. The method comprises the following steps: 1) performing mixing and ball milling on 50-70 parts by weight of calcium carbonate and 20-60 parts by weight of montmorillonite until the average particle size is 200-800nm, thus obtaining filler mixing powder; 2) mixing 20-28 parts by weight of filler mixing powder prepared in step 1), 8-12 parts by weight of lignocellulose, and 3-8 parts by weight of iron stearate to obtain modified mixing powder. The packing material prepared by the method has the advantages of being low in environmental pollution, easy to degrade, and short in degrading time.

Description

technical field [0001] The invention relates to a preparation method of an easily degradable packaging material. Background technique [0002] With the rapid development of my country's packaging industry, the role of packaging production in promoting the construction of the national economy and improving the material and cultural life of the people has become increasingly apparent. As an independent industry system, the development of the packaging industry has been included in the national economic and social development plan. [0003] Traditional polymer packaging materials are difficult to degrade in nature. While bringing convenience to people, they also produce huge pollution. Therefore, we urgently need to study an environmentally friendly packaging material. Contents of the invention [0004] The technical problem to be solved by the present invention is to overcome the above disadvantages of the prior art: to provide a method for preparing a packaging material th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08K9/04C08K3/26C08K3/34
CPCC08K9/08C08K3/26C08K3/346C08K9/04C08K2003/265C08K2201/003C08L2201/06C08L23/12
Inventor 周顺花
Owner 周顺花
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap