Anti-aging rubber belt rubber material

A rubber material and anti-aging technology, applied in the field of packaging materials, can solve the problems of poor anti-aging and flame retardant properties, and achieve good anti-aging and good chemical stability.

Inactive Publication Date: 2018-02-27
安徽微威环保科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing adhesive tapes generally have disadvantages such as poor aging resistance and flame retardancy, so they are not suitable for the needs of modern industrial production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] An anti-aging tape rubber material is made of the following raw materials in parts by weight: 32 parts of butyl rubber, 18 parts of acrylate rubber, 9 parts of carboxylated polybutadiene, 14 parts of tributyl citrate, polyethylene glycol 6 parts, 6 parts of carbon fiber, 5 parts of lamellar talc, 3 parts of titanium dioxide, 5 parts of sulfur, 3 parts of flame retardant, 8 parts of diacetyl peroxide, 6 parts of silicon micropowder, 2 parts of anti-aging agent, 2 parts of heat stabilizer, 7 parts of chlorinated paraffin, 4 parts of calcium hydroxide.

[0019] The preparation method of described anti-aging tape rubber material, comprises the following steps:

[0020] (1) Take each raw material component according to the ratio in parts by weight;

[0021] (2) butyl rubber, acrylate rubber, carboxylated polybutadiene and tributyl citrate are added in the rubber mixer and mixed;

[0022] (3) Add polyethylene glycol, carbon fiber, lamellar talc, titanium dioxide, silicon mi...

Embodiment 2

[0025] An anti-aging tape rubber material is made of the following raw materials in parts by weight: 24 parts of butyl rubber, 28 parts of acrylate rubber, 10 parts of carboxylated polybutadiene, 16 parts of tributyl citrate, polyethylene glycol 7 parts, carbon fiber 5 parts, lamella talc 7 parts, titanium dioxide 5 parts, sulfur 5 parts, flame retardant 2 parts, diacetyl peroxide 10 parts, silicon micropowder 7 parts, anti-aging agent 3 parts, heat stabilizer 3 parts, 12 parts of chlorinated paraffin, 5 parts of calcium hydroxide.

[0026] The preparation method of described anti-aging tape rubber material, comprises the following steps:

[0027] (1) Take each raw material component according to the ratio in parts by weight;

[0028] (2) butyl rubber, acrylate rubber, carboxylated polybutadiene and tributyl citrate are added in the rubber mixer and mixed;

[0029] (3) Add polyethylene glycol, carbon fiber, lamellar talc, titanium dioxide, silicon micropowder, chlorinated pa...

Embodiment 3

[0032] An anti-aging tape rubber material is made of the following raw materials in parts by weight: 32 parts of butyl rubber, 27 parts of acrylate rubber, 8 parts of carboxylated polybutadiene, 23 parts of tributyl citrate, polyethylene glycol 6 parts, 6 parts of carbon fiber, 3 parts of plate crystal talc, 1 part of titanium dioxide, 4 parts of sulfur, 4 parts of flame retardant, 6 parts of diacetyl peroxide, 6 parts of silicon micropowder, 2 parts of anti-aging agent, 4 parts of heat stabilizer, 9 parts of chlorinated paraffin, 3 parts of calcium hydroxide.

[0033] The preparation method of described anti-aging tape rubber material, comprises the following steps:

[0034] (1) Take each raw material component according to the ratio in parts by weight;

[0035] (2) butyl rubber, acrylate rubber, carboxylated polybutadiene and tributyl citrate are added in the rubber mixer and mixed;

[0036] (3) Add polyethylene glycol, carbon fiber, lamellar talc, titanium dioxide, silico...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-aging rubber belt rubber material. The anti-aging rubber belt rubber material is prepared from the following raw materials in parts by weight: 20 to 35 parts of butyl rubber, 15 to 30 parts of acrylate rubber, 5 to 12 parts of carboxylated polybutadiene, 10 to 25 parts of tributyl citrate, 3 to 10 parts of polyethylene glycol, 3 to 8 parts of carbon fiber, 3 to 9 parts of wafer talc, 1 to 5 parts of titanium dioxide, 3 to 6 parts of sulfur, 1 to 5 parts of flame retardant, 5 to 10 parts of diacetyl peroxide, 2 to 7 parts of silica powder, 1 to 3 parts of antiaging agent, 1 to 5 parts of thermal stabilizer, 5 to 13 parts of chlorinated paraffin and 2 to 5 parts of calcium hydroxide. Compared with the prior art, the anti-aging rubber belt rubber material has the advantages that the butyl rubber and the acrylate rubber are taken as major raw materials, and meanwhile the carbon fiber, flame retardant, silica powder and antiaging agent are added, so that theanti-aging rubber belt rubber material has high antiaging property, high flame retardancy and high chemical stability.

Description

technical field [0001] The invention belongs to the technical field of packaging materials, and in particular relates to an anti-aging tape rubber material. Background technique [0002] As we all know, the surface of the tape is coated with a layer of adhesive, and it is widely used in various fields of industrial production. According to its function, the tape can be divided into: high temperature tape, double-sided tape, insulating tape, special tape, pressure sensitive tape, die-cut tape, Different functions are suitable for different industry needs. However, the existing adhesive tapes generally have disadvantages such as poor aging resistance and flame retardancy, so they are not suitable for the needs of modern industrial production. Contents of the invention [0003] The object of the present invention is to provide an anti-aging tape rubber material, which can effectively solve the technical problems mentioned in the background art. [0004] To achieve the above...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/22C08L33/04C08L47/00C08L71/02C08L91/06C08K13/04C08K7/06C08K3/22C08K3/06C08K3/36C08K5/11
CPCC08L23/22C08K2003/2206C08K2003/2241C08L2201/08C08L2205/035C08L33/04C08L47/00C08L71/02C08L91/06C08K13/04C08K7/06C08K3/22C08K3/06C08K3/36C08K5/11
Inventor 李季戴宇辉魏巍李俊李志远梁天也
Owner 安徽微威环保科技有限公司