Environment-friendly brick and production method thereof

A production method and technology for environmentally friendly bricks, applied in the field of building materials, can solve the problem that clay resources can no longer meet the needs of brick making, and achieve the effects of low cost, high compressive strength and broad market prospects.

Inactive Publication Date: 2018-03-09
GUILIN CHUNXIAO ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with the continuous development of the construction industry, the demand for bricks is gradually increasing, and the existing clay resources can no longer meet the needs of brick making. In addition, my country's continuous strengthening of environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The environmental protection brick of this embodiment is made of the following raw materials: slag 6kg, river sand 10kg, construction waste 3kg, coal gangue powder 15kg, andalusite powder 4kg, granite tailings 9kg, zirconia powder 8kg and kaolin tailings powder 9kg, wherein, the particle size of the slag is 80-100 mesh, the particle size of the construction waste is 60-100 mesh, the particle size of the gangue powder is 40-80 mesh, and the kaolin tailings powder is The particle size is 40-60 mesh.

[0019] The production method of the above-mentioned environmental protection brick comprises the following process steps: take the following raw materials: 6kg of slag, 10kg of river sand, 3kg of construction waste, 15kg of coal gangue powder, 4kg of andalusite powder, 9kg of granite tailings, 8kg of zirconia powder and kaolin 9 kg of tailings powder, wherein the particle diameter of the slag is 80-100 mesh, the particle diameter of the construction waste is 60-100 mesh, the...

Embodiment 2

[0022] The environmental protection brick of this embodiment is made of the following raw materials: slag 9kg, river sand 7kg, construction waste 6kg, coal gangue powder 10kg, andalusite powder 7kg, granite tailings 7kg, zirconia powder 12kg and kaolin tailings powder 6kg, wherein, the particle size of the slag is 80-100 mesh, the particle size of the construction waste is 40-60 mesh, the particle size of the gangue powder is 40-60 mesh, and the kaolin tailings powder is The particle size is 40-60 mesh.

[0023] The production method of the above-mentioned environmental protection brick comprises the following process steps: take the raw materials of the following weight: 9kg of slag, 7kg of river sand, 6kg of construction waste, 10kg of coal gangue powder, 7kg of andalusite powder, 7kg of granite tailings, 12kg of zirconia powder and kaolin 6 kg of tailings powder, wherein the particle diameter of the slag is 80-100 mesh, the particle diameter of the construction waste is 40-...

Embodiment 3

[0026] The environmental protection brick of the present embodiment is made of the following raw materials: slag 12kg, river sand 4kg, construction waste 9kg, coal gangue powder 5kg, andalusite powder 10kg, granite tailings 5kg, zirconia powder 16kg and kaolin tailings powder 3kg, wherein, the particle size of the slag is 80-100 mesh, the particle size of the construction waste is 40-60 mesh, the particle size of the gangue powder is 40-60 mesh, and the kaolin tailings powder is The particle size is 40-60 mesh.

[0027] The production method of the above-mentioned environmental protection brick comprises the following process steps: take the following raw materials: 12kg of slag, 4kg of river sand, 9kg of construction waste, 5kg of coal gangue powder, 10kg of andalusite powder, 5kg of granite tailings, 16kg of zirconia powder and kaolin 3 kg of tailings powder, wherein the particle diameter of the slag is 80-100 mesh, the particle diameter of the construction waste is 40-60 me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly brick and a production method thereof, and belongs to the technical field of building materials. The environment-friendly brick comprises, by weight, 6-12 parts of slags, 4-10 parts of river sand, 3-9 parts of building rubbish, 5-15 parts of coal gangue powder, 4-10 parts of andalusite powder, 5-9 parts of granite tailings, 8-16 parts of zirconium oxide powder and 3-9 parts of kaolin tailing powder. The environment-friendly brick has high compressive strength, high breaking resistance and low cost, resources are saved effectively, and secondary pollution to the environment is avoided.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular, it provides an environment-friendly brick and a production method thereof. Background technique [0002] Traditional fired bricks mainly use clay as raw material. However, with the continuous development of the construction industry, the demand for bricks is gradually increasing, and the existing clay resources can no longer meet the needs of brick making, coupled with the continuous strengthening of environmental protection in our country. Therefore, developing a kind of environment-friendly brick that uses other raw materials instead of clay and has higher performance has become an urgent problem to be solved. Contents of the invention [0003] One of the objectives of the present invention is to provide an environmentally friendly brick. The environmental protection brick of the invention has high compressive strength, good flexural resistance and low cost, effect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B40/02
CPCC04B28/00C04B2111/00017C04B2201/50C04B18/10C04B14/06C04B18/16C04B14/041C04B18/12C04B14/306C04B40/024C04B20/0076
Inventor 黄云鸿李力
Owner GUILIN CHUNXIAO ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com