Diatom-ooze decorative material and preparation method thereof

A technology of decorative materials and diatom mud, which is applied in the field of diatom mud decorative materials and its preparation, can solve the problems of losing the function of filtration and adsorption, not being environmentally friendly and green, and achieving good wall texture, not easy to chemical changes, and adhesion strong effect

Inactive Publication Date: 2018-03-20
东莞市爱乐居环保科技有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The added chemical adhesive will block all the original micropores of these coatings, causing the coating to solidify and lose its original filtration and adsorption function, and the adhesive itself will release harmful substances such as formaldehyde, which is not a real coating. Environmentally friendly and green products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A diatom mud decoration material, the diatom mud decoration material is composed of the following raw materials in parts by weight: 60 parts of diatomite, 1.5 parts of palygorskite, 3.0 parts of magnesium silicate, 1.5 parts of cellulose, heavy calcium carbonate 50 parts, 25 parts of coarse sand, 4 parts of lime calcium powder, 2.5 parts of nano-titanium dioxide, 1 part of antibacterial agent, and 0.4 part of defoamer.

[0033] The particle diameter of the diatomite selected in this embodiment is 6000 mesh, the particle diameter of the palygorskite is 500 mesh, the length of the cellulose is 2mm, the coarse sand is 7# coarse sand, the antibacterial The agent is copper oxide, and the defoamer is polyoxyethylene polyoxypropanolamine ether.

[0034] The preparation method of the above-mentioned diatom mud decoration material is to weigh and mix each raw material according to its weight ratio, add it to a mixer and stir for 15 minutes, after mixing evenly, put it into a 5 k...

Embodiment 2

[0037] A diatom mud decoration material, the diatom mud decoration material is composed of the following raw materials in parts by weight: 40 parts of diatomite, 1.0 parts of palygorskite, 3.5 parts of magnesium silicate, 1.5 parts of cellulose, heavy calcium carbonate 60 parts, 20 parts of coarse sand, 4 parts of gray calcium powder, 2.0 parts of nano-titanium dioxide, 1 part of antibacterial agent, and 0.2 part of defoamer.

[0038] The particle diameter of the diatomite selected in this embodiment is 8000 mesh, the particle diameter of the palygorskite is 400 mesh, the length of the cellulose is 1mm, the coarse sand is 7# coarse sand, the antibacterial The antifoaming agent is nano-zinc oxide, and the defoaming agent is emulsified silicone oil.

[0039] The preparation method of the above-mentioned diatom mud decoration material is to weigh and mix each raw material according to its weight ratio, add it to a mixer and stir for 15 minutes, after mixing evenly, put it into a ...

Embodiment 3

[0042] A diatom mud decoration material, the diatom mud decoration material is composed of the following raw materials in parts by weight: 45 parts of diatomite, 1.2 parts of palygorskite, 3.2 parts of magnesium silicate, 1.6 parts of cellulose, heavy calcium carbonate 55 parts, 2 parts of coarse sand, 4.5 parts of lime calcium powder, 2.2 parts of nano-titanium dioxide, 2 parts of antibacterial agent, and 0.3 part of defoamer.

[0043] The particle diameter of the selected diatomite used in the present embodiment is 10000 orders, and the particle diameter of palygorskite is 600 orders, and the length of described cellulose is 1mm, and described coarse sand is 7# coarse sand, and described antibacterial agent is Nano Zinc Oxide. The defoamer is a mixture of emulsified silicone oil and polyoxypropylene glyceryl ether in a volume ratio of 1:1.

[0044] The preparation method of the above-mentioned diatom mud decoration material is to weigh and mix each raw material according to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a diatom-ooze decorative material and a preparation method thereof. The diatom-ooze decorative material is prepared from the following raw materials in parts by weight: 40-60 parts of diatomite, 1.0-1.5 parts of palygorskite, 3.0-3.5 parts of magnesium silicate, 1.5-2 parts of cellulose, 50-60 parts of heavy calcium carbonate, 20-25 parts of coarse sand, 4-5 parts of ash calcium powder, 2.0-2.5 parts of nano titanium dioxide, 1-3 parts of antibacterial agent and 0.2-0.4 part of defoaming agent. The diatom-ooze decorative material prepared by the method has the advantages that because of no need of adding chemical adhesive and no-adhesive wall decoration, the environment-friendly effect is achieved; because of better water absorptivity and insulating-oxygenating effects and a better adsorbing effect and wall-surface texture, the environment-friendly effect is achieved and the comprehensive effect is good.

Description

technical field [0001] The invention relates to the technical field of diatom mud decoration materials, in particular to a diatom mud decoration material and a preparation method thereof. Background technique [0002] At present, along with the continuous improvement of economic development and people's living standards, wall decoration coatings have been widely used. Due to the use of a large amount of chemical substances in the wall decoration paint for interior decoration, the "interior decoration pollution syndrome" has been caused, which has seriously affected people's health. Therefore there is a kind of wall decoration coating on the market, and this coating is main component with inorganic porous powder, and its advantage is can not impair people's health. [0003] However, in order to be able to firmly combine these inorganic porous powder coatings with the wall, chemical adhesives are often added to the formula. The added chemical adhesive will block all the orig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B111/28
CPCC04B28/001C04B2111/00025C04B2111/28C04B14/08C04B14/042C04B24/383C04B14/28C04B14/36C04B14/06C04B14/305C04B20/008C04B14/309C04B24/32C04B14/30C04B24/42
Inventor 李绍龙唐世家吴沁
Owner 东莞市爱乐居环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products