Environment-friendly energy-saving brick and production method thereof

A technology of environmental protection, energy saving and production method, which is applied in the field of building materials, can solve the problems that clay resources can no longer meet the needs of brick making, and achieve the effects of low cost, simple production method and high compressive strength

Inactive Publication Date: 2018-03-30
桂林市晟博科技服务有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with the continuous development of the construction industry, the demand for bricks is gradually increasing, and the existing clay resources can no longer meet the needs of brick making. In addition, my country's continuous strengthening of environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The environmental protection and energy-saving brick of the present embodiment is made of the following raw materials: gangue powder 10kg, river sand 20kg, construction waste 10kg, zirconia powder 18kg, andalusite powder 10kg, kaolin tailings powder 18kg and attapulgite 8kg, Wherein, the particle diameter of the gangue powder is 40-60 mesh, the particle diameter of the construction waste is 40-60 mesh, the particle diameter of the zirconia powder is 40-60 mesh, and the particle diameter of the andalusite powder is 40-60 mesh. 40-60 mesh, and the particle size of the kaolin tailings powder is 40-60 mesh.

[0021] The production method of the above-mentioned environmental protection and energy-saving bricks includes the following process steps: take the following raw materials: gangue powder 10kg, river sand 20kg, construction waste 10kg, zirconia powder 18kg, andalusite powder 10kg, kaolin clay tailings powder 18kg and attapulgite 8kg of soil, mixed evenly, fully stirred...

Embodiment 2

[0024] The environmental protection and energy-saving brick of the present embodiment is made of the following raw materials: gangue powder 15kg, river sand 14kg, construction waste 15kg, zirconia powder 14kg, andalusite powder 15kg, kaolin tailings powder 13kg and attapulgite 12kg, Wherein, the particle diameter of the gangue powder is 40-60 mesh, the particle diameter of the construction waste is 40-60 mesh, the particle diameter of the zirconia powder is 40-60 mesh, and the particle diameter of the andalusite powder is 40-60 mesh. 40-60 mesh, and the particle size of the kaolin tailings powder is 40-60 mesh.

[0025] The production method of the above-mentioned environmental protection and energy-saving bricks comprises the following process steps: raw materials of the following weight are taken: gangue powder 15kg, river sand 14kg, construction waste 15kg, zirconia powder 14kg, andalusite powder 15kg, kaolin clay tailings powder 13kg and attapulgite 12kg of soil, mixed eve...

Embodiment 3

[0028] The environmental protection and energy-saving brick of the present embodiment is made of the following raw materials: gangue powder 20kg, river sand 8kg, construction waste 20kg, zirconia powder 10kg, andalusite powder 20kg, kaolin tailings powder 8kg and attapulgite 16kg, Wherein, the particle size of the waste bricks and tiles is 80-100 mesh, the particle size of the construction waste is 40-60 mesh, the particle size of the fly ash is 40-60 mesh, and the kaolin tailings powder is The particle size is 40-60 mesh.

[0029] The production method of the above-mentioned environmental protection and energy-saving bricks includes the following process steps: take the following raw materials: gangue powder 20kg, river sand 8kg, construction waste 20kg, zirconia powder 10kg, andalusite powder 20kg, kaolin clay tailings powder 8kg and attapulgite 16kg of soil, mixed evenly, fully stirred and digested for 8 hours, then pressed into shape, and finally autoclaved and cured under...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly energy-saving brick and a production method thereof, and belongs to the technical field of a building material. The environment-friendly energy-saving brick is prepared from the following raw materials in parts by weight: 10 to 20 parts of gangue powder, 8 to 20 parts of river sand, 10 to 20 parts of building rubbish, 10 to 18 parts of zirconium oxide powder, 10 to 20 parts of andalusite powder, 8 to 18 parts of kaolin tailing powder and 8 to 16 parts of attapulgite. The environment-friendly energy-saving brick has the advantages that the compressive strength is high; the fracture resistance is high; the cost is low; resources are effectively saved; the secondary pollution on environment is avoided.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular, it provides an environment-friendly and energy-saving brick and a production method thereof. Background technique [0002] Traditional fired bricks mainly use clay as raw material. However, with the continuous development of the construction industry, the demand for bricks is gradually increasing, and the existing clay resources can no longer meet the needs of brick making, coupled with the continuous strengthening of environmental protection in our country. Therefore, it is an urgent problem to develop an environmentally friendly and energy-saving brick that uses other raw materials instead of clay and has higher performance. Contents of the invention [0003] One of the purposes of the present invention is to provide an environment-friendly and energy-saving brick. The environmental-friendly and energy-saving brick of the invention has high compressive strength, go...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B18/12C04B18/16B28B3/00
CPCB28B3/00C04B18/12C04B18/16C04B28/001C04B2201/50C04B14/068C04B14/306C04B14/041Y02W30/91
Inventor 王君阳艳华刘谋军
Owner 桂林市晟博科技服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com