Q235B hot-rolled steel plate enamel and preparation method thereof

A Q235B, hot-rolled steel plate technology, applied in the field of steel plate enamel, can solve the problems of high manufacturing cost, and achieve the effects of low manufacturing cost, stable glaze properties and simple process

Inactive Publication Date: 2018-04-06
山东金仓搪瓷制品科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Enamel products need to use special enamelled steel plates with low carbon content, and the manufacturing cost is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] (1) Porcelain powder: 60% to 75%, antiknock agent: 0.5% to 2%, pigment: 1% to 3%, sodium nitrite (content: 98%): 0.15% to 0.35%, borax ( Content: 95%): 0.15% ~ 0.4%, calcium carbonate: 0.1 ~ 0.5%, kaolin: 4% ~ 5%, quartz powder: 3.6% ~ 5.5%, urea (nitrogen content: 46.4%): 0.5% ~ 1.5%, water: 27% ~ 45% mixed into the ball mill, after ball milling for 6 hours, to get the glaze;

[0014] (2) Spray the ball-milled glaze on the rust-removed steel plate, put it in the drying room to dry the glaze, and then fire at 900°C to obtain the enamel product.

Embodiment 2

[0016] (1) Porcelain powder: 65%, antiknock agent: 0.6%, pigment: 1.6%, sodium nitrite (content: 98%): 0.15%, borax (content: 95%): 0.25%, calcium carbonate: 0.1 %, kaolin: 4.6%, quartz powder: 3.6%, urea (nitrogen content: 46.4%): 0.7%, water: 30%, mix and add to the ball mill, after ball milling for 6 hours, the glaze is obtained;

[0017] (2) Spray the ball-milled glaze on the rust-removed steel plate, put it in the drying room to dry the glaze, and then fire at 900°C to obtain the enamel product.

Embodiment 3

[0019] (1) Porcelain powder: 60.9%, antiknock agent: 0.6%, pigment: 1.8%, sodium nitrite (content: 98%): 0.18%, borax (content: 95%): 0.22%, calcium carbonate: 0.3 %, kaolin: 4.3%, quartz powder: 3.6%, urea (nitrogen content: 46.4%): 0.6%, water: 27.5%, mix and add to the ball mill, after ball milling for 6 hours, the glaze is obtained;

[0020] (2) Spray the ball-milled glaze on the rust-removed steel plate, put it in the drying room to dry the glaze, and then fire at 900°C to obtain the enamel product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a Q235B hot-rolled steel plate enamel and a preparation method thereof, which comprises the following raw materials in weight percentage: porcelain powder: 60% to 75%, antiknock agent: 0.5% to 2%, pigment: 1 %~3%, sodium nitrite: 0.15%~0.35%, borax: 0.15%~0.4%, calcium carbonate: 0.1~0.5%, kaolin: 4%~5%, quartz powder: 3.6%~5.5%, urea: 0.5%~1.5%, water: 27%~45%. The present invention uses ordinary Q235B hot-rolled steel plate as the base material of enamel products, and the manufacturing cost is relatively low, which is more conducive to the popularization and use of enamel products; The surface has anti-corrosion ability, and the glaze body has stable properties, low cost and simple process.

Description

technical field [0001] The invention belongs to the technical field of steel plate enamel, and in particular relates to a Q235B hot-rolled steel plate enamel and a preparation method thereof. Background technique [0002] Steel enamel products have a wide range of applications. At present, the base material of enamel products on the market generally adopts enamel special steel plates with a carbon content of ≤0.08%. The enamel is ball milled and sprayed on the special enamel steel plates. After sintering in an enamel furnace, enamel is obtained. product. Enamel products need to use enamel special steel plates with low carbon content, and the manufacturing cost is relatively high. Contents of the invention [0003] In order to overcome the deficiencies of the above technologies, the present invention provides a Q235B hot-rolled steel plate enamel and a preparation method thereof. [0004] The technical solution that the present invention overcomes its technical problem ad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/14C03C1/04C23D5/02
CPCC03C8/14C03C1/04C23D5/02
Inventor 李广生
Owner 山东金仓搪瓷制品科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com