V and Cr-contained microalloy construction steel rod and preparation method thereof

A production method, technology of construction steel

Inactive Publication Date: 2018-04-24
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problems of low nitrogen content and few types of vanadium nitride alloys used in the preparation of nitrogen-containing alloy steels, the present invention provides a new method for preparing nitrogen-containing alloys

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • V and Cr-contained microalloy construction steel rod and preparation method thereof
  • V and Cr-contained microalloy construction steel rod and preparation method thereof
  • V and Cr-contained microalloy construction steel rod and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Embodiment 1 uses the inventive method to prepare containing V, Cr microalloy building steel bar

[0050] A steel plant adopts the technology of the present invention to produce ribbed steel bars for construction in the converter process with a nominal capacity of 120 tons (the actual steel output is in the range of 120 to 140 tons). The production process is converter smelting → blowing inert gas after the furnace + feeding Core-spun wire → 6-machine 6-strand billet continuous casting machine casting into 150mm×150mm billet → billet heating → rolling into continuous bar rolling production line Ribbed steel bars.

[0051] Firstly, 120 tons of molten iron and 20 tons of steel scrap are added into the converter, and the S content of the added molten iron is 0.059%. After the molten iron and steel scrap are added to the converter, the molten iron and steel scrap are initially smelted into molten steel by using the function of the converter to blow oxygen to remove C. Whe...

Embodiment 2

[0062] Embodiment 2 prepares containing V, Cr microalloy construction steel bar with the inventive method

[0063] A steel plant adopts the technology of the present invention to produce ribbed steel bars for construction in the converter process with a nominal capacity of 120 tons (the actual steel output is in the range of 120 to 140 tons). The production process is converter smelting → blowing inert gas after the furnace + feeding Core-spun wire → 6-machine 6-strand billet continuous casting machine casting into 150mm×150mm billet → billet heating → rolling into continuous bar rolling production line Ribbed steel bars.

[0064] Firstly, 120 tons of molten iron and 20 tons of scrap steel are added into the converter, and the S content of the added molten iron is 0.057%. After the molten iron and steel scrap are added to the converter, the molten iron and scrap steel are initially smelted into molten steel by using the function of the converter to blow oxygen and remove C. ...

Embodiment 3

[0077] Embodiment 3 prepares containing V, Cr microalloy construction steel bar with the inventive method

[0078] A steel plant adopts the technology of the present invention to produce ribbed steel bars for construction in the converter process with a nominal capacity of 120 tons (the actual steel output is in the range of 120 to 140 tons). The production process is converter smelting → blowing inert gas after the furnace + feeding Core-spun wire → 6-machine 6-strand billet continuous casting machine casting into 150mm×150mm billet → billet heating → rolling into continuous bar rolling production line Ribbed steel bars.

[0079] Firstly, 120 tons of molten iron and 20 tons of steel scrap are added into the converter, and the S content of the added molten iron is 0.052%. After the molten iron and steel scrap are added to the converter, the molten iron and scrap steel are initially smelted into molten steel by using the function of the converter to blow oxygen and remove C. Wh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
elongationaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of steel and iron metallurgy, and in particular, relates to a V and Cr-contained microalloy construction steel rod and a preparation method thereof. Aiming at the problems of low nitrogen content and few types of vanadium nitride alloys selected for traditional preparation of nitrogen-contained alloy steel, the invention provides the V and Cr-contained microalloyconstruction steel rod and the preparation method thereof. The rod comprises the following components in percentage by weight: 0.15-0.30% of C, 0.30-1.00% of Si, 0.60-1.30% of Mn, 0.0060-0.0180% of N, P not more than 0.040%, S not more than 0.040%, 0.010-0.160% of V, 0.10-0.60% of Cr, and the balance of Fe and inevitable impurities. The preparation method is characterized in that N-contained core-spun yarns are fed in a small platform after a furnace and N is adjusted to a proper level. The method is simple in operation; the nitrogen yield is high and stable; the production cost can be effectively reduced; and the method deserves popularization and application.

Description

technical field [0001] The invention belongs to the field of iron and steel metallurgy, and in particular relates to a V and Cr microalloy building steel bar and a production method thereof. Background technique [0002] Microalloyed steel mainly refers to the steel whose performance can be obviously improved by adding a small amount or a trace amount of certain elements in the steel, especially the strength index of the steel. Under the existing technical conditions, microalloyed steel is mainly obtained by adding a small amount or a small amount of vanadium, niobium and titanium. The mechanism of microalloying is: after adding vanadium, niobium and titanium as trace elements into molten steel, they combine with carbon and nitrogen in molten steel to form carbon and nitrogen compound particles, namely V(C, N), Nb( C, N) and Ti (C, N) particles, these particles have a certain effect of precipitation strengthening and grain refinement, which can significantly improve the str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/24C21C7/00C21D8/08
CPCC21C7/0056C21D8/065C21D8/08C22C38/001C22C38/02C22C38/04C22C38/24Y02P10/20
Inventor 邓通武刘明郭跃华冉准
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com