Compound coiled material and preparation method thereof

A technology of composite rolls and modified asphalt, which is applied in the field of construction chemical materials, can solve problems such as the difficulty of removing the isolation film, affecting the construction efficiency, and the melting and softening of the roll material, and achieves excellent adhesion, good full adhesion effect, The effect of excellent weather resistance

Inactive Publication Date: 2018-05-04
GUILIN HEXIN WATERPROOF DECORATION MATERIAL
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But as far as the current self-adhesive polymer modified bitumen waterproofing membrane is concerned, its heat resistance is not high, and many problems have appeared in summer construction. Soft, with a tendency to flow; and the isolation film is difficult to uncover, which affects construction efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 1) The penetration of petroleum asphalt is 80, the softening point is 48°C, and the content of asphaltene is 15%. The softening point of natural lake asphalt is 95°C, it contains 33% porous minerals, and the content of asphaltene in natural lake asphalt is 38%. Compound petroleum asphalt and natural lake asphalt, and natural lake asphalt accounts for 50% of the total asphalt;

[0020] 2) The modified asphalt rubber layer is composed of the following raw materials in parts by weight: 50 parts of the above compounded asphalt, 8 parts of pulverized regenerated rubber powder, 15 parts of waste rubber powder, and 1.5 parts of softened oil.

[0021] 3) First raise the temperature of the above compound asphalt to 200°C, add waste engine oil and stir to cool down to 180°C, then add pulverized regenerated rubber powder, heat up to 240°C, add waste rubber powder, keep warm and stir for 2 hours, then add softened oil to continue Stir for 0.5h to obtain the modified asphalt compou...

Embodiment 2

[0024] 1) The softening point of natural lake asphalt is 110°C, it contains 38% porous minerals, and the content of asphaltene in natural lake asphalt is 43%.

[0025] 2) The modified asphalt rubber layer is composed of the following raw materials in parts by weight: 62 parts of natural lake asphalt, 10 parts of pulverized regenerated rubber powder, 25 parts of waste rubber powder, and 2.5 parts of softened oil.

[0026] 3) First raise the temperature of natural lake asphalt to 220°C, add waste engine oil and stir to cool down to 190°C, then add pulverized regenerated rubber powder, heat up to 250°C, add waste rubber powder, keep stirring for 3 hours, then add softened oil and continue stirring 1h, the modified asphalt compound is obtained.

[0027] 4) Glass fiber felt or polyester felt is used as the reinforcement body, and the modified asphalt layer is coated on the top of the reinforcement body. mm, mineral particle layer 2.0mm, thermoplastic polyolefin layer 1.5mm, modifi...

Embodiment 3

[0029] 1) The penetration of petroleum asphalt is 70, the softening point is 50°C, and the content of asphaltene is 16%. The softening point of natural lake asphalt is 105°C, it contains 35% porous minerals, and the content of asphaltene in natural lake asphalt is 40%. Compound petroleum asphalt and natural lake asphalt, and natural lake asphalt accounts for 80% of the total asphalt;

[0030] 2) The modified asphalt rubber layer is composed of the following raw materials in parts by weight: 58 parts of the above-mentioned compound asphalt, 9 parts of pulverized regenerated rubber powder, 20 parts of waste rubber powder, and 2 parts of softened oil.

[0031] 3) First raise the temperature of the above compound asphalt to 210°C, add waste engine oil and stir evenly to cool down to 185°C, then add pulverized regenerated rubber powder, heat up to 245°C, add waste rubber powder, keep stirring for 2.5 hours, then add softening oil Continue stirring for 0.8h to obtain the modified a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a compound coiled material. A glass fiber mat or a polyester felt serves as a reinforcement body, the reinforcement body is coated with a modified asphalt layer, the upper surface of the modified asphalt layer is coated with a mineral particle layer, and a thermoplastic polyolefin layer is coated below the reinforcement body. The modified asphalt rubber layer is arranged between the upper covering layer and an intermediate carcass layer; and the modified asphalt rubber layer is composed of the following raw materials in parts by weight: 50-62 parts of asphalt, 8-10 parts of reclaimed rubber powder, 15-25 parts of waste rubber powder and 1.5-2.5 parts of softening oil. The waterproof roll disclosed by the invention is long in service life and excellent in waterproofproperty, aging resistance and heat resistance.

Description

technical field [0001] The invention belongs to the field of chemical materials for construction, and in particular relates to a composite coil and a preparation method thereof. Background technique [0002] Self-adhesive waterproof membrane is a new type of waterproof material with great development prospects. The self-adhesive roll material has the characteristics of good water impermeability, strong adaptability to low temperature, good deformation resistance and self-healing property, good waterproof effect, and no need for hot melt, cold construction, direct laying and sticking, which not only improves the construction efficiency, It also eliminates fire hazards and has been highly praised by construction, design and construction units. [0003] But as far as the current self-adhesive polymer modified bitumen waterproofing membrane is concerned, its heat resistance is not high, and many problems have appeared in summer construction. Soft, with a tendency to flow; and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B17/02B32B17/06B32B27/02B32B27/14B32B27/36B32B33/00B32B37/06B32B37/10B32B37/24B32B37/02C09J195/00C09J11/08E04B1/66
CPCB32B17/068B32B5/02B32B5/30B32B27/14B32B37/02B32B37/06B32B37/10B32B37/24B32B2037/243B32B2255/02B32B2255/04B32B2255/20B32B2255/26B32B2255/28B32B2262/0276B32B2262/101B32B2264/10B32B2307/306B32B2419/00C08L2205/035C09J11/08C09J195/00E04B1/665C08L17/00C08L19/003C08L91/00
Inventor 黄志强钟圣福王继发
Owner GUILIN HEXIN WATERPROOF DECORATION MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com