Double-component ceramic tile back adhesive

A two-component, ceramic tile technology, applied in the direction of adhesives, adhesive types, amide/imide polymer adhesives, etc., can solve the problem that the bonding performance needs to be further improved, achieve convenient and efficient construction, improve physical and chemical The effect of improving performance and bonding performance

Inactive Publication Date: 2018-05-18
苏州启跃新材料科技有限公司
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The two-component tile adhesive in the prior art can make the tiles and cement-based materials bond be

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double-component ceramic tile back adhesive
  • Double-component ceramic tile back adhesive
  • Double-component ceramic tile back adhesive

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0042] The preparation method of the two-component tile adhesive of the present invention includes the following steps:

[0043] 1) Preparation of acrylate emulsion and styrene-acrylate copolymer emulsion;

[0044] 2) Mix 40 to 70 parts of acrylate emulsion prepared in step 1) and 30 to 50 parts of styrene-acrylate copolymer emulsion, stir evenly, add 1-5 parts of preservative and 1-5 parts of antiseptic Foaming agent, 0.5-1 part of thickening agent, and mixing uniformly to obtain the two-component tile adhesive.

Example Embodiment

[0046] Example 1

[0047] The two-component tile adhesive of this embodiment includes the following components in parts by weight:

[0048]

[0049]

[0050] Wherein, in parts by weight, the acrylic emulsion includes the following components:

[0051]

[0052] Wherein, in parts by weight, the solid content of the styrene-acrylate copolymer emulsion is 48%, the viscosity is 500 CP, and the pH value is 7.

Example Embodiment

[0053] Example 2

[0054] The two-component tile adhesive of this embodiment includes the following components in parts by weight:

[0055]

[0056] Wherein, in parts by weight, the acrylic emulsion includes the following components:

[0057]

[0058]

[0059] Wherein, in parts by weight, the solid content of the styrene-acrylate copolymer emulsion is 49%, the viscosity is 600 CP, and the pH value is 7.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention provides a double-component ceramic tile back adhesive. The double-component ceramic tile back adhesive comprises, by weight, 40-70 parts of acrylate emulsion, 30-50 parts of styrene-acrylate copolymer emulsion, 1-5 parts of preservatives, 1-5 parts of defoaming agent and 0.5-1 part of thickening agent. The double-component ceramic tile back adhesive has the advantages that the backadhesive is coordinated with cement mortar during use, a layer of back adhesive is plastered on the back of a ceramic tile, then the cement mortar is directly applied, and the ceramic tile is immediately adhered to a wall; the double-component ceramic tile back adhesive is convenient in construction, simple, efficient, good in adhering effect, capable of increasing bonding strength between the ceramic tile and the cement base material, capable of also increasing bonding strength between the cement base material and the wall, short in drying time, convenient and efficient in construction, and capable of avoiding the hollowing, peeling and falling off problems of ceramic tiles.

Description

technical field [0001] The invention belongs to the technical field of tile back glue, and relates to a two-component tile back glue. Background technique [0002] During the pasting process of tiles, due to the influence of construction conditions, ambient temperature, bonding materials, especially the density and water absorption of tiles, they often fall off; tile adhesive is specially used for the back treatment of wet tiles, and is also suitable It is suitable for stone materials with low water absorption, dense texture and smooth surface, which can effectively improve the bonding strength between ceramic tiles and bonding materials, and solve common problems such as hollowing and falling off in tile wet paste. [0003] CN107083215A discloses a kind of tile adhesive produced by pure acrylic elastic emulsion and styrene-acrylic emulsion and its technology. The ceramic tile adhesive produced by pure acrylic elastic emulsion and styrene-acrylic emulsion of this invention c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J125/14C09J133/10C09J133/12C09J11/04
CPCC08K2003/265C08K2201/011C09J11/04C09J125/14C09J133/068C09J133/10C09J133/24C09J133/26C08L33/14C08K3/36C08K9/06C08K3/26C08L25/14C08K3/346C04B26/04C04B28/02C04B40/065C04B2111/00637
Inventor 李相志刘成纲王婷
Owner 苏州启跃新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap