Imitation marble water-based paint

A water-based paint, imitating marble technology, applied in the coating and other directions, can solve the problems of unclear color particle boundaries, easy photolysis, color particle instability, etc., to solve the problem of color particle instability, improve noise reduction, and reduce production costs Effect

Inactive Publication Date: 2018-05-29
马鞍山市银洁建材科技有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the problems in the prior art that the imitation marble water-based paint has unstable color particles, unclear color particle boundaries, and easy photodecomposition, the present invention provides a marble-like water-based paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Imitation marble water-based paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] An imitation marble water-based paint of this embodiment includes the following materials in parts by weight: deionized water 40, transparent emulsion 40, protective rubber powder 5% solution 40, barium sulfate 5, roll-on diatom mud 6, film-forming aid Agent 0.8, cellulose 1.0, defoamer 0.2, wetting agent 0.05; the roll-on diatom mud includes the following materials in parts by weight: deionized water 30, diatomaceous earth powder 20, rubber powder 10, ice length Stone powder 1 and pattern additives 1.

[0061] Among them, the production process of diatomite is as follows: the diatomite ore in the original diatomite ore bin is fed to the belt conveyor via a feeder, and transferred to a grading screen. The screened material enters the hand-selecting belt, and the branches are manually picked out. After the debris such as broken plastic film, iron wire and large rocks, the diatomite ore is fed into the crusher, and the crushed materials and the under-sieve of the grading sie...

Embodiment 2

[0071] The marble-like water-based paint of this embodiment includes the following materials in parts by weight: deionized water 45, transparent emulsion 45, protective rubber powder 5% solution 45, barium sulfate 6, roll-on diatom mud 8, film-forming aid Agent 1.0, cellulose 1.2 and defoaming agent 0.1; the roll-on diatom mud includes the following materials in parts by weight: deionized water 40, diatomaceous earth dry powder 30, gum powder 20, ice feldspar powder 2 and cellulose 2 .

[0072] The manufacturing steps of the marble-like water-based paint of this embodiment are:

[0073] Step 1. The production process of diatomite dry powder is as follows:

[0074] (1) Classification: The diatomite raw ore is the same as in Example 1. The diatomite ore in the diatomite raw ore bin is transferred to the grading screen by a belt conveyor for classification;

[0075] (2) Picking: The sieve goes into the hand-selected belt, and the impurities are picked out manually;

[0076] (3) Crushing:...

Embodiment 3

[0094] The basic steps of an imitation marble water-based paint of this embodiment are the same as those of embodiment 2, but the difference and improvement lies in that it includes the following materials in parts by weight: deionized water 40, transparent emulsion 40, protective rubber powder 5% solution 40, sulfuric acid Barium 4, roll-on diatom mud 7, film-forming aid 1.0, cellulose 1.2, and defoamer 0.2; the roll-on diatom mud includes the following materials in parts by weight: deionized water 35, diatomaceous earth dry powder 25. Rubber powder 15, feldspar powder 2 and pattern aid 2.

[0095] The manufacturing steps of the marble-like water-based paint of this embodiment are:

[0096] Step 1. The production process of diatomite dry powder is as follows:

[0097] (1) Classification: The diatomite raw ore is the same as in Example 1. The diatomite ore in the diatomite raw ore bin is transferred to the grading screen by a belt conveyor for classification;

[0098] (2) Picking: Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses imitation marble water-based paint, and belongs to the technical field of building materials. The imitation marble water-based paint is prepared from, by weight, 40-45 parts ofdeionized water, 40-45 parts of transparent emulsion, 40-45 parts of solution of 5% protection glue powder, 6-8 parts of roll-coated diatom ooze, 4-6 parts of barium sulfate, 0.8-1.0 part of coalescing agent, 1.0-1.2 parts of cellulose, 0.1-0.2 part of defoaming agent and 0.05-0.1 part of wetting agent. The roll-coated diatom ooze is prepared from, by weight, 30-40 parts of deionized water, 20-30parts of kieselguhr dry powder, 10-20 parts of rubber powder, 1-2 parts of valencianite powder and 1-2 parts of decoration pattern additive. Kieselguhr ores are precipitated and separated after beingscrubbed to obtain fine kieselguhr, and the fine kieselguhr is dryed through a vacuum freeze-drying method to prepare the kieselguhr dry powder. Through the coordinative effect of the kieselguhr drypowder and the valencianite powder, pigments and micro-pores are firmly combined, and the problems that the imitation marble water-based paint is instable in color chip, unclear in color chip boundaryand prone to photolysis are solved.

Description

Technical field [0001] The invention relates to the technical field of building materials, in particular to a marble-like water-based paint. Background technique [0002] Marble is a natural stone, which is widely used in building exterior finishes. However, the cost of marble is relatively expensive, and it is a public hazard to use as a veneer on the exterior wall of a building, and it is not easy to use it on a large area or on the exterior wall of a high-rise building. Therefore, in order for the building to achieve the luxurious appearance of marble, the materials that imitate the marble are constantly pouring out. Due to the heterogeneity of the color of the marble, the imitation process is very complicated. People need a simple and convenient material to simplify the complexity of the imitation process. In this context, marble-like coatings came into being. In my country, the research on marble-like coatings began in the 1980s. At that time, marble-like coatings were mai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/00C09D7/61C09D7/62C09D7/63C09D7/65
Inventor 丁一恒
Owner 马鞍山市银洁建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com