Organic tanning agent for leather and preparing method of organic tanning agent

An organic and leather technology, applied in the field of organic tanning agents for leather and its preparation, can solve environmental pollution and other problems

Active Publication Date: 2018-05-29
WENZHOU UNIVERSITY
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The tanning agents in the prior art all need to be pickled, which has great pollution to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic tanning agent for leather and preparing method of organic tanning agent
  • Organic tanning agent for leather and preparing method of organic tanning agent
  • Organic tanning agent for leather and preparing method of organic tanning agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Embodiment one: the experimental procedure of H acid and cyanuric chloride reaction

[0037] 5.59g of cyanuric chloride (TCT) was added into a 100mL three-necked flask, and 17.46g of water was added at room temperature. Put it into a pre-prepared constant temperature water bath with a temperature controlled at 0-5°C, and stir with a stirring bar for 20 minutes to cool the solution to 0-5°C. Add 11.26g of lysine to 26.53g of 12.23% sodium carbonate aqueous solution, mix evenly and place it in a beaker, and use a peristaltic pump to drop it into a three-necked flask at a speed of 0.5mL / min. 19.9 g of 12.23% sodium carbonate aqueous solution was added dropwise into the funnel, and the addition was completed in 60 minutes. The pH value was measured every 30 minutes to monitor the reaction progress, and the reaction was kept at 0-5° C. for 5 hours. After the reaction, an aqueous dispersion with a solid content of 25% was obtained, ready for use.

Embodiment 2

[0038] Embodiment two: the experimental procedure of taurine and cyanuric chloride reaction

[0039] 5.59g of cyanuric chloride (TCT) was added into a 100mL three-necked flask, and 27.94g of acetone was added at room temperature to dissolve the cyanuric chloride. Put it into a pre-prepared constant temperature water bath pot with a temperature controlled at 0-5°C, and stir for 20 minutes with a stirring bar, so that the temperature of the solution is lowered to 0-5°C to form a saturated solution. 3.99g taurine was added into 33.69g mass fraction of 10% sodium carbonate aqueous solution, mixed uniformly and placed in a beaker, and was added dropwise to a three-necked flask at a speed of 0.5mL / min by a peristaltic pump, and the addition was completed in 60 minutes. The pH value was measured every 30 minutes in order to monitor the progress of the reaction, and the reaction was incubated at 0-5°C for 5 hours. A reaction solution with a solid content of 15.7% was obtained and was...

Embodiment 3

[0040] Embodiment three: the reaction of lysine and cyanuric chloride

[0041] 5.59g of cyanuric chloride (TCT) was added into a 100mL three-necked flask, and 38.4g of acetone was added at room temperature to dissolve the cyanuric chloride. Put it into a pre-prepared constant temperature water bath pot with a temperature controlled at 0-5°C, and stir for 20 minutes with a stirring bar, so that the temperature of the solution is lowered to 0-5°C to form a saturated solution. Add 2.84g of lysine to 12.96g of 20% sodium hydroxide aqueous solution, mix evenly and place it in a beaker, and drop it into a three-necked flask with a peristaltic pump at a speed of 0.5mL / min. After 30 minutes, the addition is complete. The pH value was measured every 30 minutes in order to monitor the progress of the reaction, and the reaction was incubated at 0-5°C for 5 hours. A reaction solution with a solid content of 18% was obtained and was ready for use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an organic tanning agent for leather. The organic tanning agent comprises the following components of, by weight, 20-40 parts of cyanuric chloride and 10-20 parts of multiaminocompounds. When discharging of the organic tanning agent is completed, the appearance of the active chlorine organic tanning agent is yellow emulsion at normal temperature. The organic tanning agenthas stable shrinkage stability and is suitable for demands of most of tanning processes in the prior art.

Description

technical field [0001] The invention belongs to the field of leather tanning, in particular to an organic tanning agent for leather and a preparation method thereof. Background technique [0002] At present, leather tanning agents at home and abroad are mainly divided into two categories: inorganic tanning agents and organic tanning agents; among them, inorganic tanning agents are represented by chrome tanning agents, and there are many kinds of organic tanning agents. Chrome tanning is widely used due to its high shrinkage temperature, strong washing resistance, softness, fullness, elasticity and extensibility. However, the utilization rate of Cr3+ in the chrome tanning agent cannot reach 100%, and the part remaining in the waste liquid is precipitated to form chromium-containing sludge together with lime, other inorganic substances and organic substances. Chromium-containing sludge is included in the hazardous waste catalogue, and it is very difficult to dispose of. It ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C14C3/08
CPCC14C3/08
Inventor 柴玉叶兰云军邹祥龙柴玉枝
Owner WENZHOU UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap