A technology for epoxidizing hydroxyl-terminated polybutadiene and hydroxyl-terminated polybutadiene is applied in the rubber field, which can solve the problems of poor mechanical properties of liquid rubber and achieve the effect of excellent mechanical properties
Inactive Publication Date: 2018-06-01
CHENGDU JINHUI TECH
View PDF1 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0006] The present invention aims to solve the problem of poor mechanical properties of liquid rubber in the prior art, and provides an epoxidized hydroxyl-terminated polybutadiene liquid rubber, which has excellent mechanical properties
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0035] An epoxidized hydroxyl-terminated polybutadiene liquid rubber, comprising the following raw materials in parts by weight:
[0036] 50 parts of hydroxyl-terminated polybutadiene
[0037] 150 parts hydrogen peroxide
[0038] 30 parts of formic acid
[0039] 50 parts of methyl ethyl ketone
[0040] Sodium sulfamate 3 parts
[0041] 800 parts of deionized water.
Embodiment 2
[0043] An epoxidized hydroxyl-terminated polybutadiene liquid rubber, comprising the following raw materials in parts by weight:
[0044] 60 parts of hydroxyl-terminated polybutadiene
[0045] 200 parts hydrogen peroxide
[0046] 50 parts of formic acid
[0047] 60 parts of methyl ethyl ketone
[0048] Sodium sulfamate 5 parts
[0049] 1000 parts of deionized water.
Embodiment 3
[0051] An epoxidized hydroxyl-terminated polybutadiene liquid rubber, comprising the following raw materials in parts by weight:
[0052] 55 parts of hydroxyl-terminated polybutadiene
[0053] 175 parts hydrogen peroxide
[0054] 40 parts of formic acid
[0055] 55 parts of methyl ethyl ketone
[0056] Sodium sulfamate 4 parts
[0057] 900 parts of deionized water.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to epoxidized hydroxyl-terminated polybutadiene liquid rubber and belongs to the technical field of rubber. The epoxidized hydroxyl-terminated polybutadiene liquid rubber is prepared from the following raw materials in parts by weight: 50-60 parts of hydroxyl-terminated polybutadiene, 150-200 parts of hydrogen peroxide, 30-50 parts of formic acid, 50-60 parts of methyl ethylketone, 3-5 parts of sodium sulfamate and 800-1000 parts of deionized water. The epoxidized hydroxyl-terminated polybutadiene liquid rubber has the beneficial effects that epoxidizing modification canbe carried out on hydroxyl-terminated polybutadiene liquid rubber (HTPB) by adopting a peroxyformic acid in-situ method for all the raw materials so as to prepare the epoxidized hydroxyl-terminated polybutadiene liquid rubber with excellent mechanical property.
Description
technical field [0001] The invention relates to a liquid rubber, more specifically, the invention relates to an epoxidized hydroxyl-terminated polybutadiene liquid rubber, which belongs to the technical field of rubber. Background technique [0002] Hydroxyl-terminated polybutadiene (HTPB for short) is a liquid telechelic polymer. It reacts with chain extender and crosslinking agent to form a cured product with one-dimensional network structure, which has excellent mechanical properties and good hydrolysis resistance, acid and alkali resistance, wear resistance, low temperature resistance and electrical insulation properties. [0003] Epoxidized hydroxyl-terminated polybutadiene (EHTPB) is the product of introducing epoxy groups into the macromolecular chain of HTPB, which can not only effectively improve the polarity, but also introduce epoxy groups as reactive functional groups, which can be combined with polyurethane The amino active hydrogen produced during the cross-li...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.