A kind of anti-termite-resistant low-temperature flame-retardant PC/PE alloy material and preparation method thereof

An alloy material and termite prevention technology, applied in the field of alloy materials, can solve the problems of poor fluidity and low temperature resistance of PC resin, and achieve the effects of reducing volatilization loss, satisfying large-scale batch production and simple operation.

Active Publication Date: 2019-12-31
QINGDAO HAIER NEW MATERIAL R&D CO LTD
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The high-density polyethylene resin selected in the present invention as a component of the alloy material not only improves the defects of poor fluidity and low temperature resistance of the PC resin, but also better disperses the effective anti-termite components on the PC base as a carrier. materials, give full play to the role of anti-termites

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-termite-resistant low-temperature flame-retardant PC/PE alloy material and preparation method thereof
  • A kind of anti-termite-resistant low-temperature flame-retardant PC/PE alloy material and preparation method thereof
  • A kind of anti-termite-resistant low-temperature flame-retardant PC/PE alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The preparation of anti-termite masterbatch specifically comprises the following steps:

[0040] First, add 0.2 parts of initiator DCP, 2 parts of maleic anhydride, 5 parts of bifenthrin and 10 parts of methyl carbamate in a closed stirring pot for pre-mixing at a low speed for 1 minute, then add 82.4 parts of high-density polyethylene HDPE, Stir and mix at high speed for 2 minutes, then add to a twin-screw screw extruder for melting and reaction granulation. The temperature of each section of the twin-screw extruder is 160°C, 180°C, 200°C, 220°C, 220°C, 200°C, 200°C, 180°C, 180°C, the die head temperature is 160°C, and the screw speed is 50r / min . The prepared anti-termite masterbatch is packaged in an aluminum foil packaging bag and vacuum-sealed in time for future use.

Embodiment 2-8

[0042] Weigh a certain amount of PC resin, high-density polyethylene HDPE, low-temperature synergist, phosphorus flame retardant, flame retardant synergist, anti-dripping agent, anti-termite masterbatch, antioxidant and add it to the high-speed mixer In the middle, the mixed material after stirring for 3 minutes is added from the main feeding port of the twin-screw extruder; the anti-termite masterbatch is added from the ninth zone by using a weight loss scale, and melted and granulated by the twin-screw extruder. In the twin-screw extruder, the temperature of each section from the feed section to the machine head is 200°C, 220°C, 230°C, 230°C, 245°C, 245°C, 235°C, 235°C, 230°C, 230°C, 230°C °C, 230 °C, the die temperature is 230 °C. The prepared anti-termite, low-temperature and flame-retardant PC / PE alloy pellets were placed in a vacuum oven at 80°C for 3 hours, and then the test specimens were prepared by injection molding machine.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention discloses a termite-proof low-temprature-resisting and flame-retarding PC / PE (Polycarbonate / Polyethylene) alloy material and a preparation method thereof. The termite-proof low-temprature-resisting and flame-retarding PC / PE alloy material is prepared from the following components in parts by weight: 50 to 80 parts of PC resin, 5 to 20 parts of PE resin, 3 to 8 parts of a low-temperature synergist, 10 to 20 parts of a phosphorus-based flame retardant, 0.2 to 2.0 parts of a flame-retarding synergist, 0.4 to 1.0 part of an anti-dropping agent, 1 to 10 parts of termite-proof master batch and 0.4 to 1.0 part of an antioxidant. In a PC / PE alloy system, the PE resin is distributed in the PC resin in a dispersed phase manner; active groups of the PE resin and the PC resin are subjected to grafting reaction in a melting and blending process of the low-temperature synergist, so that a two-phase interface of PC and PE is improved, and the low-temperature toughening effect of the PEresin is sufficiently expressed; the phosphorus-based flame retardant is cooperatively matched with the flame-retarding synergist, so that flame-retarding requirements of large-size thin-wall parts are met. According to the termite-proof low-temprature-resisting and flame-retarding PC / PE alloy material, the termite-proof master batch is prepared firstly and then is used for synthesizing the PC / PEalloy material, so that the obtained termite-proof low-temprature-resisting and flame-retarding PC / PE alloy material keeps relatively good low-temperature-resisting and flame-retarding properties; meanwhile, the termite-proof low-temprature-resisting and flame-retarding PC / PE alloy material also has a long-effect termite-proof effect and is applicable to optical fibers and cable wiring boxes.

Description

technical field [0001] The invention belongs to the technical field of alloy materials, and relates to a termite-proof, low-temperature-resistant and flame-retardant PC / PE alloy material and a preparation method thereof, in particular to a termite-proof, low-temperature-resistant and flame-retardant PC / PE alloy material for junction boxes such as optical fibers and cables, and its preparation method. Background technique [0002] Polycarbonate (PC) material has the characteristics of excellent impact resistance, creep resistance, good dimensional stability, heat resistance, and non-toxicity, and has become an engineering plastic with the fastest growing application volume in recent years. As a general-purpose plastic, a high-density polyethylene copolymer (HDPE) not only has outstanding impact resistance, heat resistance, and low temperature resistance, but also has environmental stress cracking resistance, electrical properties, and processability. [0003] At present, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08L23/06C08L23/36C08K13/04C08K7/10C08K5/101C08K5/39C08K5/205
CPCC08K2201/003C08K2201/004C08L69/00C08L2201/02C08L2203/20C08L2205/03C08L2207/062C08L23/06C08L23/36C08K13/04C08K7/10C08K5/101C08K5/39C08K5/205
Inventor 肖红伟张秀文李建敏谭伟宏李伟刘机关郝雅珍周洋
Owner QINGDAO HAIER NEW MATERIAL R&D CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com