Anti-aging Co-TiO2 nanometer sol

Abstract

The invention discloses an anti-aging Co-TiO2 nanometer sol. The anti-aging Co-TiO2 nanometer sol is prepared from the following components according to a formula by weight: 40 to 80 parts of Co, 10 to 30 parts of TiO2, 0.5 to 1.5 parts of additive, 4.5 to 5.5 parts of nanometer silicon oxide, 3.5 to 4.5 parts of mildew-proof antibacterial agent, 6.2 to 8.5 parts of anti-aging agent, 8.2 to 12 parts of gelling agent, 0.1 to 0.4 part of coloring agent, 0.2 to 0.75 parts of trace elements, and 30 to 50 parts of water. The anti-aging Co-TiO2 nanometer sol has the advantages that the anti-aging function is better improved, the damage under the conditions of sunlight and adverse weather is avoided, more durability in use is realized, the appearance is more attractive, the influence to the service life by corrosion rust spot is avoided, the problems of easiness in damage and lower strength are solved, the current consumption concept is met, and the anti-aging Co-TiO2 nanometer sol is suitable for popularization and application.

Description

technical field [0001] The invention relates to the technical field of nano sol, in particular to an anti-aging sol Co-TiO2 nano sol. Background technique [0002] In industrial areas, coastal areas or areas with severe smog, due to the action of smoke particles, sulfur dioxide gas or salt in the air, the color coating on the surface of the color-coated board is severely corroded and aged, especially in the case of strong sunlight, rain and air Pollutants such as sulfur dioxide in medium accelerate the aging of color-coated plates, the color fades, becomes dull, and eventually corrosion and rust spots appear, which affect the service life and appearance, are relatively easy to be damaged, have low strength, and do not have the effect of heat insulation. Therefore, it is proposed An anti-aging sol Co-TiO2 nano-sol. Contents of the invention [0003] The object of the present invention is to provide an anti-aging sol Co-TiO2 nano-sol, to solve the problems raised in the abo...

AI Technical Summary

Problems solved by technology

[0002] In industrial areas, coastal areas or areas with severe smog, due to the action of smoke particles, sulfur dioxide gas or salt in the air, the color coating on the surface of the color-coated board is severely corroded and aged, especially in the case of strong sunlight, rain and air Pollutants such as sulfur dioxide in medium accelerate the aging of color-coated plates, the color fades, becomes dull, and eventually corrosion and rust spots appear, which affect the service life and appearance, are relatively easy to be damaged, have low strength, and do not have the effect of heat insulation. Therefore, it is proposed An Antiaging Co-TiO2 Nanosol