The method that compound template agent synthesizes zsm-35 molecular sieve

A ZSM-35, composite template technology, applied in molecular sieves and alkali exchange compounds, chemical instruments and methods, crystalline aluminosilicate zeolite, etc. Small, moderate particle size effect

Active Publication Date: 2019-11-08
PETROCHINA CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

high production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041]Dissolve 10kg of sodium metaaluminate and 3kg of sodium hydroxide completely in 60kg of desalted water to prepare sodium metaaluminate-sodium hydroxide aqueous solution; add 10kg of hexamethyleneimine to 50kg of cyclohexylamine and stir thoroughly to obtain Hexamethyleneimine-cyclohexylamine composite template. Add 100 kg of silica sol with a mass content of 30% into the gel forming tank, start stirring, add hexamethyleneimine-cyclohexylamine composite template agent, stir evenly, add sodium metaaluminate-sodium hydroxide aqueous solution dropwise to "thick After clicking ", increase the stirring speed, open the gel, and slowly add the remaining sodium metaaluminate-sodium hydroxide aqueous solution; then add 0.6kg NaZSM-35 molecular sieve, stir for 2 hours, and proceed to gelation.

[0042] Put the gelled slurry into a 500L crystallization kettle, start stirring at a stirring speed of 40r.p.m, and press the feeding port tightly; turn on the heat-conducting oil circulati...

Embodiment 2

[0044] 10kg of sodium metaaluminate and 1.2kg of sodium hydroxide are completely dissolved in 120kg of desalted water to prepare sodium metaaluminate-sodium hydroxide aqueous solution; 10kg of hexamethyleneimine is added to 20kg of cyclohexylamine and fully stirred to prepare A hexamethyleneimine-cyclohexylamine composite template was obtained. Add 100 kg of silica sol with a mass content of 30% into the gel forming tank, start stirring, add hexamethyleneimine-cyclohexylamine composite template agent, stir evenly, add sodium metaaluminate-sodium hydroxide aqueous solution dropwise to "thick After clicking ", increase the stirring speed, open the gel, and slowly add the remaining sodium metaaluminate-sodium hydroxide aqueous solution; then add 0.5kg NaZSM-35 molecular sieve, stir for 2 hours, and proceed to gelation.

[0045] Put the gelled slurry into a 500L crystallization kettle, start stirring at a stirring speed of 70r.p.m, and press the feeding port tightly; turn on the h...

Embodiment 3

[0047] 10kg of sodium metaaluminate and 1.2kg of sodium hydroxide are completely dissolved in 120kg of desalted water to prepare sodium metaaluminate-sodium hydroxide aqueous solution; 30kg of hexamethyleneimine is added to 80kg of cyclohexylamine and fully stirred to prepare A hexamethyleneimine-cyclohexylamine composite template was obtained. Add 100 kg of silica sol with a mass content of 30% into the gel forming tank, start stirring, add hexamethyleneimine-cyclohexylamine composite template agent, stir evenly, add sodium metaaluminate-sodium hydroxide aqueous solution dropwise to "thick After clicking ", increase the stirring speed, open the gel, and slowly add the remaining sodium metaaluminate-sodium hydroxide aqueous solution; then add 0.4kg NaZSM-35 molecular sieve, stir for 4 hours, and proceed to gelation.

[0048] Put the gelled slurry into a 500L crystallization kettle, start stirring at a stirring speed of 80r.p.m, and press the feeding port tightly; turn on the h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for synthesizing a ZSM-35 molecular sieve by a composite template agent. The method comprises the following steps: dissolving sodium metaaluminate or sodium aluminateand alkali into desalted water to prepare a sodium metaaluminate-alkali aqueous solution or a sodium aluminate-alkali aqueous solution; adding hexamethylene imine into cyclohexane to prepare a composite template agent, adding the composite template agent into silicon sol, completely stirring, dropwise adding the sodium metaaluminate-alkali aqueous solution or the sodium aluminate-alkali aqueous solution until reaching a thick point, increasing the stirring speed, opening gel and slowly adding the residual sodium metaaluminate-alkali aqueous solution or the sodium aluminate-alkali aqueous solution; adding the ZSM-35 molecular sieve, stirring, gelatinizing and crystallizing, and synthesizing a high-nanoscale ZSM-35 molecular sieve.

Description

technical field [0001] The invention relates to a method for synthesizing ZSM-35 molecular sieves, in particular to a method for synthesizing ZSM-35 molecular sieves with a composite template. Background technique [0002] The structure of ZSM-35 molecular sieve is that the eight-membered ring channel and the six-membered ring channel intersect to form a spherical cage of 0.6nm to 0.7nm, which has good adsorption performance and good shape-selective catalytic performance; due to the molecular sieve structure, it is resistant to carbon deposition and loss With strong activity and large specific surface area, it can be used for alkylation of aromatic hydrocarbons, oligomerization of olefins, isomerization of xylene, isomerization of olefins, etc. The high-purity, nano-scale ZSM-35 molecular sieve has a larger specific surface area and better shape-selective catalytic performance. [0003] At present, the synthesis method of ZSM-35 molecular sieve mainly adopts hydrothermal st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/44B82Y40/00
CPCC01B39/445C01P2004/03C01P2004/62C01P2004/64
Inventor 赵胤邓广金李正侯立波崔龙李菁
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com