Preparation method of concrete water-permeable bricks with good water-permeable effect

A technology for concrete and permeable bricks, applied in clay products, ceramic products, applications, etc., can solve problems such as poor mechanical properties, and achieve the effects of enhanced mechanical properties, increased interface strength and bonding properties, and high bonding strength.

Inactive Publication Date: 2018-06-12
DINGYUAN COUNTY MINGYOU WALL MATERIALS
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the existing water-permeable floor tiles have a certain water-permeable function and meet the ecological needs, their mechanical properties are poor, especially the water-permeable effect of the cement paste can not meet the needs, and urgently need to be solved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A method for preparing a concrete permeable brick with good water permeability, comprising the steps of:

[0019] S1. Mix 80kg of construction waste coarse aggregate, 60kg of fast-hardening sulfoaluminate cement, 6kg of polyethylene compound, 60kg of diatomaceous earth, 30kg of construction waste micropowder, 30kg of steel slag, 4kg of asphalt granules, and 8kg of borax, and press them into shape. Molding pressure is 20MPa, natural drying for 45h, hot air drying at 100°C to constant weight, cooling to obtain pre-compressed material;

[0020] The polyethylene compound is prepared by the following process: 8kg of sucrose fatty acid ester, 3kg of lecithin, and 50kg of water are sent into the emulsification tank, and nitrogen gas is continuously fed into the bottom of the emulsification tank at a speed of 25 L / min, and stirred for 8 hours. 2400r / min, add 35kg polyethylene for homogenization treatment for 4h, homogenization pressure is 30MPa, irradiation treatment is 25min, ...

Embodiment 2

[0023] A method for preparing a concrete permeable brick with good water permeability, comprising the steps of:

[0024] S1. Mix 100kg of construction waste coarse aggregate, 40kg of fast-hardening sulfoaluminate cement, 14kg of polyethylene compound, 40kg of diatomaceous earth, 40kg of construction waste micropowder, 20kg of steel slag, 8kg of asphalt granules, and 4kg of borax, and press to form it. Molding pressure is 22MPa, natural drying for 30h, hot air drying at 110°C to constant weight, cooling to obtain pre-compressed material;

[0025] The polyethylene compound is prepared by the following process: 4kg of sucrose fatty acid ester, 5kg of lecithin, and 30kg of water are sent into the emulsification tank, and nitrogen gas is continuously fed into the bottom of the emulsification tank at a rate of 35 L / min, and stirred for 4 hours. 2800r / min, add 25kg polyethylene for homogenization treatment for 8h, homogenization pressure is 25MPa, irradiation treatment is 35min, irra...

Embodiment 3

[0028] A method for preparing a concrete permeable brick with good water permeability, comprising the steps of:

[0029] S1. Mix 85kg of construction waste coarse aggregate, 55kg of fast-hardening sulfoaluminate cement, 8kg of polyethylene compound, 55kg of diatomaceous earth, 33kg of construction waste micropowder, 28kg of steel slag, 5kg of asphalt granules, and 7kg of borax, and press to form it. Molding pressure is 20.5MPa, natural drying for 40h, hot air drying at 102℃ to constant weight, cooling to obtain pre-compressed material;

[0030] Polyethylene composites were prepared using the following process: 7kg of sucrose fatty acid ester, 3.5kg of lecithin, and 45kg of water were sent into the emulsification tank, and nitrogen gas was continuously fed into the bottom of the emulsification tank at a speed of 28 L / min, stirred for 7 hours, and stirred The speed is 2500r / min, add 32kg polyethylene for homogenization treatment for 5h, the homogenization pressure is 28MPa, the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of concrete water-permeable bricks with good water-permeable effect. The preparation method includes following steps: well mixing construction waste coarseaggregate, rapid-hardening sulfate aluminum cement, polyethylene composite, diatomite, construction waste micropowder, slag, asphalt particle and borax, forming under pressure, naturally drying, using hot air to dry to constant weight, and cooling to obtain a pre-pressed material; heating and sintering the pre-pressed material, and heating and sintering again to obtain the concrete water-permeable bricks. A preparation process of the polyethylene composite includes: sending sucrose fatty acid ester, lecithin and water into an emulsifying tank, continuously feeding nitrogen to the bottom of the emulsifying tank, stirring, adding polyethylene, homogenizing, irradiating, adding polyamide, and heating while stirring to obtain the polyethylene composite. Water-permeable gaps inside the concrete water-permeable bricks are uniform, the concrete water-permeable bricks are good in water-permeable effect and excellent in mechanical performance and durability, meet requirements on compressive strength of concrete pavement bricks and have a noise absorbing function.

Description

technical field [0001] The invention relates to the technical field of permeable bricks, in particular to a method for preparing a concrete permeable brick with good water permeable effect. Background technique [0002] Floor tiles are subject to greater pressure and therefore require higher strength. The existing floor tiles have high density, such as concrete floor tiles. These floor tiles are all formed from the same material at one time, and the internal material has fewer pores. Moreover, the pores are not connected and impermeable, which cuts off the communication between the roadbed and the outside world. , destroying the natural ecological environment. Although the existing water-permeable floor tiles have a certain water-permeable function and meet the ecological needs, their mechanical properties are poor, especially the water-permeable effect of the cement paste can not meet the needs, and urgently need to be solved. Contents of the invention [0003] Based on...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B33/138C04B33/13C04B33/32C04B35/634C04B38/08
CPCC04B33/1305C04B33/131C04B33/132C04B33/138C04B33/32C04B35/632C04B35/63408C04B35/63468C04B38/08C04B2235/3409C04B2235/3418C04B2235/96C04B38/067Y02P40/60
Inventor 余明友胡翠田
Owner DINGYUAN COUNTY MINGYOU WALL MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap