Glass stone manufacturing process

A manufacturing process and technology of glass stone, applied in the field of glass stone manufacturing process, can solve the problems of rough surface, poor weather resistance, low color saturation, etc., achieve high production efficiency and yield, meet diversified needs, and high degree of automation Effect

Pending Publication Date: 2018-06-15
东莞市尚艺玻璃制品有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are similar products in the market. One kind of stickers and silk screens are made on the bottom of the glass. This kind of glass makes the pattern lose its original texture, and its weather resistance is poor, so it is not easy to use for a long time. The other is to spray high-temperature inorganic coating glass. The surface, its disadvantage is that the surface is rough, not anti-fouling, low color saturation, and distorted patterns
And above-mentioned two kinds of techniques can't make pattern pattern on the four sides of glass, can't form complete natural stone effect, the present invention overcomes above-mentioned all defects very well

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The manufacturing method of described glass stone manufacturing process:

[0020] One: The required polymer material is configured according to the weight of the following components: polyamide resin 43%, silicone modified acrylic resin 57%, leveling agent 4%, surfactant 3%, filler 29% %, an appropriate amount of diluent, with glass as the base material, processed into the required specifications and shapes;

[0021] Two: Processing, high temperature ink required for screen printing or roll printing on the glass, entering the glass tempering furnace for tempering and forming;

[0022] Three: Use the burned ink as the bottom layer and the ink color as the base color, spray a layer of polymer paint on the periphery of the glass and the ink surface, then bake in an oven at 110-200 degrees for 10 minutes, and place it for 24 hours to dry;

[0023] Four: Select the required pattern and print it on the copy paper or copy film with special sublimation ink inkjet or printing p...

Embodiment 2

[0027] One: The required polymer material is configured according to the weight of the following components: polyamide resin 42%, silicone modified acrylic resin 55%, leveling agent 3%, surfactant 4%, filler 30% %, an appropriate amount of diluent, with glass as the base material, processed into the required specifications and shapes;

[0028] Two: Processing, high temperature ink required for screen printing or roll printing on the glass, entering the glass tempering furnace for tempering and forming;

[0029] Three: Use the burned ink as the bottom layer and the ink color as the base color, spray a layer of polymer paint on the periphery of the glass and the ink surface, then bake in an oven at 110-200 degrees for 10 minutes, and place it for 24 hours to dry;

[0030] Four: Select the required pattern and print it on the copy paper or copy film with special sublimation ink inkjet or printing process;

[0031] Five: Paste the ink surface of the printed transfer paper or tran...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glass stone manufacturing process. A high polymer material needed for manufacturing a glass stone in the glass stone manufacturing process is prepared from the following components by weight: 40%-45% of polyamide resin, 56%-60% of organosilicone modified acrylate resin, 2%-5% of a flatting agent, 2%-4% of a surfactant, 27%-31% of filling material, and proper amount of diluent; the filling material comprises 15%-17% of pigment in a main agent and 12%-14% of aluminum chloride, the diluent is absolute ethyl alcohol, and the organosilicone modified acrylate resin is a material prepared from a polyacrylic resin and chlorotrimethoxysilane. The effect of the stone is achieved by taking the industrial glass as a base material, and the high strength, the wear resistance, the antifouling property and the index are better than those of the natural stone.

Description

technical field [0001] The invention relates to a method for manufacturing decorative materials, in particular to a glass stone manufacturing process. Background technique [0002] Natural stone is a non-renewable raw material, and it will cause damage to the environment when it is mined. This invention is directly made on the surface of the glass and its surroundings, and has excellent wear resistance and scratch resistance, particularly good weather resistance, and high color saturation. The pattern is delicate and beautiful. [0003] At present, there are similar products in the market. One kind of stickers and silk screens are made on the bottom of the glass. This kind of glass makes the pattern lose its original texture, and its weather resistance is poor, so it is not easy to use for a long time. The other is to spray high-temperature inorganic coating glass. Surface, its disadvantage is that the surface is rough, not anti-fouling, low color saturation, and distorted ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C17/34C09D133/04C09D177/00
CPCC03C17/007C03C17/009C03C17/34C03C2217/445C09D143/04C08L77/00
Inventor 陈国祥
Owner 东莞市尚艺玻璃制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com