Fertilizer synergist
A fertilizer synergist and raw material technology, applied in organic fertilizers, inorganic fertilizers, ammonium salt fertilizers, etc., can solve problems such as poor plant growth, achieve the effect of promoting plant growth and enhancing chelation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0021] Example 1
[0022] Add chitosan to water at a mass ratio of 1:100 into the No. 1 beaker, stir and mix with a glass rod for 30 minutes, then let it stand and swell for 4 hours, and then move the No. 1 beaker into a digital speed-measuring constant-temperature magnetic stirrer at a temperature of 100℃ , Under the condition of 500r / min, heating and stirring to dissolve for 50min, the chitosan liquid is obtained; adding polyvinyl alcohol and water according to the mass ratio of 1:100 into the No. 2 beaker, stirring and mixing with a glass rod for 30min, then standing for swelling 4h, then move the No. 2 beaker into the digital display speed measuring constant temperature magnetic stirrer, at a temperature of 100 ℃, rotating speed 500r / min, heating and stirring to dissolve for 50 minutes, then the polyvinyl alcohol liquid is obtained; the sepiolite and organic acid The mass ratio of 1:100 is placed in a single-necked flask, and the single-necked flask is placed in a digital spe...
Example Embodiment
[0023] Example 2
[0024] Add chitosan to water at a mass ratio of 1:100 into the No. 1 beaker, stir and mix with a glass rod for 30 minutes, then let it stand and swell for 4 hours, and then move the No. 1 beaker into a digital speed-measuring constant-temperature magnetic stirrer at a temperature of 100℃ , Under the condition of 500r / min, heating and stirring to dissolve for 50min, the chitosan liquid is obtained; adding polyvinyl alcohol and water according to the mass ratio of 1:100 into the No. 2 beaker, stirring and mixing with a glass rod for 30min, then standing for swelling 4h, then move the No. 2 beaker into the digital display speed measuring constant temperature magnetic stirrer, at a temperature of 100 ℃, rotating speed 500r / min, heating and stirring to dissolve for 50 minutes, then the polyvinyl alcohol liquid is obtained; the sepiolite and organic acid The mass ratio of 1:100 is placed in a single-necked flask, and the single-necked flask is placed in a digital spe...
Example Embodiment
[0025] Example 3
[0026] Add chitosan to water at a mass ratio of 1:100 into the No. 1 beaker, stir and mix with a glass rod for 30 minutes, then let it stand and swell for 4 hours, and then move the No. 1 beaker into a digital speed-measuring constant-temperature magnetic stirrer at a temperature of 100℃ , Under the condition of 500r / min, heating and stirring to dissolve for 50min, the chitosan liquid is obtained; adding polyvinyl alcohol and water according to the mass ratio of 1:100 into the No. 2 beaker, stirring and mixing with a glass rod for 30min, then standing for swelling 4h, then move the No. 2 beaker into the digital display speed measuring constant temperature magnetic stirrer, at a temperature of 100 ℃, rotating speed 500r / min, heating and stirring to dissolve for 50 minutes, then the polyvinyl alcohol liquid is obtained; the sepiolite and organic acid The mass ratio of 1:100 is placed in a single-necked flask, and the single-necked flask is placed in a digital spe...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap