Papermaking coating granular superfine starch adhesive and preparation method thereof

A starch adhesive, granular technology, applied in the directions of adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of increased coating production cost, high price, insufficient paper strength, etc., and achieves easy operation. , uniform particle size, the effect of improving strength

Inactive Publication Date: 2018-06-29
枣庄市金科化工有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, carboxylated styrene-butadiene latex also has some defects: the paper still has the problem of insufficient strength; the higher price leads to the continuous increase of coating production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A granular superfine starch adhesive for papermaking coating, the starch adhesive includes the following components in parts by weight: 35 parts of potato starch, 12 parts of bamboo charcoal, 6 parts of sodium tetraborate, and 5 parts of ethyl acetate , 7 parts of sodium acrylate, 10 parts of polyvinyl alcohol, 7 parts of water glass, 6 parts of EDTA, 3 parts of dibutyl phosphate, 5 parts of zinc borate, and 5 parts of nano-scale silver oxide. The particle size of bamboo charcoal is 60 mesh.

[0016] A method for preparing a granular superfine starch adhesive for papermaking coating, comprising the following steps: adding potato starch into water to make a 35% dispersion, adding nanoscale silver oxide, bamboo charcoal, sodium tetraborate and sodium acrylate, Stir and mix evenly, then add a certain amount of pH regulator to adjust the pH to 8, and continuously stir and react in a constant temperature water bath at 55°C for 15 minutes; then add ethyl acetate, water glass,...

Embodiment 2

[0018] A granular superfine starch adhesive for papermaking coating, the starch adhesive includes the following components in parts by weight: 60 parts of potato starch, 17 parts of bamboo charcoal, 13 parts of sodium tetraborate, and 10 parts of ethyl acetate , 14 parts of sodium acrylate, 22 parts of polyvinyl alcohol, 13 parts of water glass, 10 parts of EDTA, 7 parts of dibutyl phosphate, 10 parts of zinc borate, and 9 parts of nano-scale silver oxide. The particle size of bamboo charcoal is 200 mesh.

[0019] A method for preparing a granular superfine starch adhesive for papermaking coating, comprising the following steps: adding potato starch into water to make a 50% dispersion, adding nanoscale silver oxide, bamboo charcoal, sodium tetraborate and sodium acrylate, Stir and mix evenly, then add a certain amount of pH regulator to adjust the pH to 10, and continuously stir and react in a constant temperature water bath at 65°C for 30 minutes; then add ethyl acetate, wate...

Embodiment 3

[0021] A granular superfine starch adhesive for papermaking coating, the starch adhesive includes the following components in parts by weight: 45 parts of potato starch, 15 parts of bamboo charcoal, 9 parts of sodium tetraborate, and 8 parts of ethyl acetate , 9 parts of sodium acrylate, 15 parts of polyvinyl alcohol, 10 parts of water glass, 9 parts of EDTA, 5 parts of dibutyl phosphate, 7 parts of zinc borate, and 7 parts of nano-scale silver oxide. The particle size of bamboo charcoal is 100 mesh.

[0022] A preparation method of granular superfine starch adhesive for papermaking coating, comprising the following steps: adding potato starch into water to make a 40% dispersion, adding nanoscale silver oxide, bamboo charcoal, sodium tetraborate and sodium acrylate, Stir and mix evenly, then add a certain amount of pH regulator to adjust the pH to 8.5, and continuously stir and react in a constant temperature water bath at 60°C for 20 minutes; then add ethyl acetate, water gla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a papermaking coating granular superfine starch adhesive and a preparation method thereof. The starch adhesive is prepared from the following ingredients in parts by weight: 35to 60 parts of potato starch, 12 to 17 parts of bamboo carbon, 6 to 13 parts of sodium tetraborate, 5 to 10 parts of ethyl acetate, 7 to 14 parts of sodium acrylate, 10 to 22 parts of polyvinyl akohol, 7 to 13 parts of water glass, 6 to 10 parts of EDTA, 3 to 7 parts of dibutyl phosphate, 5 to 10 parts of zinc borate and 5 to 9 parts of nanoscale silver oxide. The starch adhesive disclosed by theinvention has the advantages of high stability, uniform particle size, good physical and chemical performance, ability in improving paper strength, simpleness and convenience in operation and abilityin reducing cost and reducing carbon emission; furthermore, the raw materials have wide source and can be generated again, and the particle size of an obtained product is small.

Description

technical field [0001] The invention relates to the technical field of starch adhesives, in particular to a granular superfine starch adhesive for papermaking coating and a preparation method thereof. Background technique [0002] Adhesives are the most important component of paper coating raw materials. It plays a decisive role in determining the viscosity, rheology, water retention and curing time of the coating, and has an important influence on the printing performance of coated paper. With the continuous development of paper coating technology, the types of coating adhesives are gradually changing. Synthetic latex adhesives are petrochemical products with non-renewable resources. They are high-carbon emission products with high cost. The starch used for coating comes from raw materials such as crop corn or potato starch. Its resources are widely renewable and have low carbon emission characteristics. The cost is low; therefore, in recent years, starch has been used mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/02C09J4/06C09J11/04C09J11/06
CPCC09J4/06C09J11/04C09J11/06
Inventor 黄崇君
Owner 枣庄市金科化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com