A kind of putty powder, an environmentally friendly technology, applied in the direction of filling slurry, etc., can solve the problems of water resistance, poor adhesion, peeling, etc., and achieve the effects of reduced usage, strong adhesion, and short growth period

Inactive Publication Date: 2018-07-03
城步天元农业开发有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the usual putty on the market is Shuangfei powder plus glue, and the purchased glue is added to Shuangfei powder and stirred into a paste. This method can save money, but it has low transparency, water resistance, poor hardness, no elasticity, and poor adhesion. , the surface of the object to be coated will crack and peel after a long time; in addition, due to the poor quality of Shuangfei powder, the surface of the object will be rough; in addition, the ingredients in the current glue often contain toxic substances such as formaldehyde, benzene, toluene, xylene, VOC, etc. , can cause damage to the human nervous system, and can cause poisoning and cancer in severe cases, especially for infants and the elderly and infirm.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] 1. Crush the bamboo flesh after peeling off the bamboo bark and inner pith ring tissue into 80-mesh bamboo powder for later use.

[0015] 2. Take 50kg of heavy calcium powder, 25kg of ash calcium, 20kg of bamboo powder and 3kg of plant glue and mix them into putty powder.

[0016] 3. Roughly level the base to be scraped without clear water. The base with strong water absorption should be wetted with water or sprayed with glue for back-sealing treatment before scraping putty. The newly plastered cement wall should be scraped after the curing period putty.

[0017] 4. Stir evenly according to the ratio of putty powder: water = 1:0.5, let it stand for about 10 minutes and then stir evenly before use.

[0018] 5. Use a steel scraper or spatula to scrape as usual, usually twice, and the second coating can be applied only when the previous coating is completely dry. Batch scraping thickness 0.8m, dosage 1kg / m 2 , generally survive twice. In the case of a flat base, about ...

Embodiment 2

[0021] 1. Crush the bamboo flesh after peeling off the bamboo bark and inner pith ring tissue into 150-mesh bamboo powder for later use.

[0022] 2. Take 60kg of talcum powder, 35kg of lime powder, 25kg of bamboo powder and 5kg of vegetable glue and mix them into putty powder.

[0023] 3. Roughly level the base to be scraped without clear water. The base with strong water absorption should be wetted with water or sprayed with glue for back-sealing treatment before scraping putty. The newly plastered cement wall should be scraped after the curing period putty.

[0024] 4. Stir evenly according to the ratio of putty powder: water = 1:0.5, let it stand for about 10 minutes and then stir evenly before use.

[0025] 5. Use a steel scraper or spatula to scrape as usual, usually twice, and the second coating can be applied only when the previous coating is completely dry. Batch scraping thickness 1.5mm, dosage 1.2kg / m 2 , generally survive twice. In the case of flat base, about 1...

Embodiment 3

[0028] 1. Crush the bamboo flesh after peeling off the bamboo bark and inner pith ring tissue into 100-mesh bamboo powder for later use.

[0029] 2. Take 55kg of heavy calcium powder, 30kg of lime powder, 25kg of bamboo powder and 4kg of vegetable glue and mix them into putty powder.

[0030] 3. Roughly level the base to be scraped without clear water. The base with strong water absorption should be wetted with water or sprayed with glue for back-sealing treatment before scraping putty. The newly plastered cement wall should be scraped after the curing period putty.

[0031] 4. Stir evenly according to the ratio of putty powder: water = 1:0.5, let it stand for about 10 minutes and then stir evenly before use.

[0032] 5. Use a steel scraper or spatula to scrape as usual, usually twice, and the second coating can be applied only when the previous coating is completely dry. Batch scraping thickness 1.0mm, dosage 1.1kg / m 2 , generally survive twice. In the case of flat base, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to environmentally-friendly putty powder, which is prepared from the following raw materials by weight: 50-60 parts of heavy calcium powder or talc powder, 25-35 parts of ash calcium or lime powder, 20-25 parts of bamboo powder, and 3-5 parts of a glue. According to the present invention, the environmentally-friendly putty powder is the interior wall putty, is added with thenatural bamboo powder, and further comprises other raw materials, such that the obtained environmentally-friendly putty powder can effectively inhibit bacteria and sterilize, and the current situationthat the wall easily produces mildew after wetting; bamboo has a short growth period, can grow in 2-3 years, and can be operated for a long time after one planting so as to provide advantages of wideresource and environment protection; the glue consumption is reduced while the plant glue is used, and formaldehyde and other harmful substances are not used; the use operation of the product is simple, wherein the product can be used only by adding water and stirring during the construction; the polished putty surface has advantages of smoothness, crack resistance, good water resistance and goodalkali resistance; the product has strong adhesion, and can effectively fill the substrate; and no odor is generated during the coating and the scraping so as to achieve the advantages of environmentprotection, safety and reliability.

Description

technical field [0001] The invention relates to decorative materials, in particular to an environment-friendly putty powder. Background technique [0002] Putty is a kind of decorative coagulation material to level the surface of the object to be painted, and it is an indispensable product before painting. A layer of white on the surface of the blank room is putty. Usually the whiteness of the putty is above 90 and the fineness is above 330. Putty is a kind of base material for leveling the wall, which lays a good foundation for future decoration (painting and wallpaper). Putty is divided into two kinds: putty inside wall and putty on exterior wall. External wall putty can resist wind and sun, so it has good gelation, high strength and low environmental index. The comprehensive index of putty in the inner wall is good, and it is hygienic and environmentally friendly. Therefore, the inner wall is not for external use and the outer wall is not for internal use. Putties are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 肖布闻
Owner 城步天元农业开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap