Efficient and short-process dyeing and finishing process of nylon knitted fabric in one bath

A short-process technology for knitted fabrics, which is applied in the field of one-bath high-efficiency short-process dyeing and finishing of nylon knitted fabrics, which can solve the problems of long processing process, time-consuming, elastic and strength damage of nylon fibers, etc.

Active Publication Date: 2020-10-27
ZHEJIANG YINGFENG TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The above-mentioned process is relatively long for nylon knitted fabrics, time-consuming, energy-consuming, and prone to problems such as nylon fiber elasticity and strength damage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Efficient and short-process dyeing and finishing process of nylon knitted fabric in one bath
  • Efficient and short-process dyeing and finishing process of nylon knitted fabric in one bath
  • Efficient and short-process dyeing and finishing process of nylon knitted fabric in one bath

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Preparation of functional finishing agent grafted with quaternary ammonium salt on the surface of nano-titanium dioxide:

[0035] Add 150mL acetone, 16 parts of nano-titanium dioxide, 3 parts of N,N-dimethyl-acryloyloxyethyl-propyltrimethoxysilane ammonium chloride into the stirrer, stir and react at 40°C for 24 hours, and centrifuge the mixture , washed twice with methanol, and dried at 70°C to obtain surface-modified nano-titanium dioxide for subsequent use;

[0036] Add 172 parts of water and 12 parts of surface-modified nano-titanium dioxide into the polymerization reactor, stir, raise the temperature of the water bath to 72 ° C, and drop 28 parts of N,N-dimethyl-acryloyloxyethyl-propyltrimethoxy The initiator solution of silane ammonium chloride, 0.6 parts of potassium persulfate and 14 parts of water is added dropwise after 2 hours, the temperature is raised to 80°C, the temperature is kept for 1 hour, and the temperature is lowered to below 50°C to obtain the nan...

Embodiment 2

[0043] One-bath high-efficiency and short-process dyeing and finishing process for nylon knitted fabrics, including the following steps:

[0044] (1), Pre-type

[0045] 180~190℃, time 30s, speed 40~45m / min;

[0046] (2), refining, dyeing

[0047] The one-step process of scouring and dyeing nylon knitted fabrics is as follows:

[0048]

[0049] In the dyeing bath, add one-bath degreaser for training and dyeing (one-bath degreaser for training and dyeing (DR-838 Wuxi Derong Chemical Co., Ltd.), chelating dispersant (polyacrylic acid), nylon leveling agent (nylon leveling agent TF- 217B Zhejiang Chuanhua Co., Ltd. Fine Chemical Co., Ltd.), run for 10 minutes, then add nylon knitted fabric and run for 15 minutes, then add dye, adjust the pH value to 5-6, heat up to 100°C and dye for 30-45 minutes.

[0050] (3), finishing

[0051]

[0052]Wherein, the preparation method of functional finishing agent is:

[0053] Add 150mL acetone, 16 parts of nano-titanium dioxide, 3 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a refining-dyeing one-bath process efficient short-process dyeing and finishing process for a chinlon knitted fabric. The process comprises the following steps: presetting for30 seconds at the temperature of 180-190 DEG C at the speed of 40-45 m / min, refining and dyeing for 30-45 minutes at the bath ratio of 1:8 at the temperature of 100 DEG C, and after-finishing for 30-45 seconds at the setting temperature of 190-200 DEG C at the speed of 30-40 m / min; the formula of refining and dyeing comprises 2-5 g / L of refining-dyeing one-bath degreaser, 2-3 g / L of chelated dispersing agent, 1-2 g / L of chinlon levelling agent, and 0.1-10 owf of weak acid dye; and the after-finishing needs 10-20 g.L<-1> of a functional finishing agent. According to the refining-dyeing one-bathprocess efficient short-process dyeing and finishing process for the chinlon knitted fabric, the chinlon knitted fabric is preprocessed and dyed in the short process through the refining-dyeing one-bath process, the size and morphological stability of the chinlon knitted fabric is guaranteed, and the problems of fabric wrinkling, bruising, dyeing effect, dyelot chromatism and the like in the conventional process are eliminated.

Description

technical field [0001] The invention relates to a textile dyeing and finishing technology, more specifically, it relates to a one-bath high-efficiency and short-process dyeing and finishing process for nylon knitted fabrics, belonging to the field of textile dyeing and finishing. Background technique [0002] Nylon is the trade name of synthetic polyamide fibers, commonly known as nylon, and its basic constituents are aliphatic polyamides linked by amide bonds -NHC0-. Nylon 6 macromolecules commonly used in textile fabrics are mainly composed of three parts, namely hydrophobicity The methylene moiety, the hydrophilic amide group and the amino and carboxyl groups at the chain ends. Although the amino group content of nylon is low, its molecular chain has a large number of methylene groups that can form van der Waals force and hydrogen bonds with dyes, so nylon can not only combine with anionic dyes through ionic bonds, but also through strong Van der Waals forces interact wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06P3/24D06C7/02D06M15/356C08F292/00C08F230/08D06M101/34
CPCC08F292/00D06C7/02D06M15/3568D06M16/00D06M2101/34D06M2200/25D06P3/24C08F230/08
Inventor 顾相军
Owner ZHEJIANG YINGFENG TECH CO LTD