Steel forging resistant to compression and corrosion, and machining method thereof
A corrosion-resistant steel and processing method technology, applied in the field of steel processing, can solve the problems of low comprehensive effect, low balance of yield strength, tensile strength and corrosion resistance of stainless steel forgings, low comprehensive performance of forgings, etc., to achieve balance High, low temperature resistance, strong weather resistance
Active Publication Date: 2018-07-20
TIANJIN RONGCHENG UNITED IRON & STEEL GRP CO LTD
View PDF6 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0005] The above improves the corrosion resistance of forgings, but the comprehensive performance of forgings is low; at the same time, from the perspective of current forging processing technology, stainless steel forgings in mechanical equipment such as oil mining machinery, rail transportation technology industry or military products, etc. The balance of yield strength, tensile strength and corrosion resistance is relatively low, the overall effect is not high, and there are improvements
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0031] Table 1 Mass percentage of each element in a kind of compression and corrosion resistant steel forging of Example 1
[0032]
[0033]
Embodiment 2
[0035] Table 2 Mass percentage of each element in a kind of compression and corrosion resistant steel forging of Example 2
[0036] components
Embodiment 3
[0038] Table 3 Mass percentage of each element in a kind of compression and corrosion resistant steel forging of embodiment 3
[0039] components
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more
Abstract
The invention discloses a steel forging resistant to compression and corrosion, and a machining method thereof. The problem of low comprehensive performance of austenitic stainless steel forgings manufactured with an existing machining method is solved. According to the technical scheme, the steel forging resistant to compression and corrosion comprises, by weight, no more than 0.08% of C, no morethan 0.50% of Mn, no more than 0.50% of Si, no more than 0.04% of P, no more than 0.03% of S, 11%-12.5% of Cr, 7.50%-9.50% of Ni, 0.40%-0.60% of Mo, 1.50%-2.50% of Cu, no more than 0.60% of Nb, no more than 0.25% of V and the balance Fe. The prepared steel forging has the advantages of high strength and toughness, corrosion and wear resistance, high weatherability, high and low temperature resistance, high stability, etc.
Description
technical field [0001] The invention relates to the technical field of steel processing, in particular to a compression-resistant and corrosion-resistant steel forging and a processing method thereof. Background technique [0002] At present, petrochemical and coal chemical industries are developing rapidly, and the scale of equipment tends to be larger. The weight of hydrogenation reactors in petroleum and coal-fired mining machinery and petrochemical core equipment has exceeded the kiloton level. Gradually, domestic mining machinery and reactors with plate-welded structures are being upgraded to forge-welded structures. [0003] The precipitation hardening treatment of stainless steel is generally described as three stages. The specific heat treatment steps are similar to martensitic steel, carbon steel and alloy steel. In fact, precipitation hardening stainless steel is improved on the basis of ordinary stainless steel, and its corrosion resistance, toughness and proces...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/44C22C38/42C22C38/46C22C38/48C21D6/00B22D11/124
CPCB22D11/124C21D6/004C22C38/02C22C38/04C22C38/42C22C38/44C22C38/46C22C38/48
Inventor 马丽娟利强
Owner TIANJIN RONGCHENG UNITED IRON & STEEL GRP CO LTD
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap