Light-weight heat insulation plate prepared from waste and old glass

A technology of waste glass and thermal insulation boards, which is applied in the field of thermal insulation materials, can solve the problems of increased building load, thermal insulation material falling off, and high density of thermal insulation boards, so as to reduce transportation costs, prevent cracking, and have outstanding flame retardancy and high temperature resistance. Effect

Inactive Publication Date: 2018-08-03
HEFEI JINTONGWEI LOW TEMPERATURE TECH CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the density of the cement foam insulation board is relatively high, which increases the load of the building after construction, and there may be a risk that the insulation material will fall off after long-term use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A light insulation board prepared from waste glass. According to the mass parts, the insulation board contains the following raw materials: 40 parts of cement, 15 parts of high-strength gypsum, 5 parts of polystyrene foam, 17 parts of perlite, and 15 parts of glass beads 5 parts of sodium silicate water glass, 2 parts of chopped fiber, 35 parts of water, 1 part of retarder and 3 parts of foaming agent.

[0026] In this embodiment, the preparation method of glass microspheres is as follows: grinding waste glass into glass micropowder with a particle size of 10-15 μm, sending the sieved glass micropowder into a bead forming furnace for spheroidization treatment, and the spheroidized micropowder The beads are bleached to obtain hollow microspheres, and the hollow microspheres are sent to a tempering furnace for tempering treatment, and the required glass microspheres are obtained after the tempering treatment is completed.

[0027] Wherein, the modulus of sodium silicate w...

Embodiment 2

[0034] A light insulation board prepared from waste glass. According to the mass parts, the insulation board contains the following raw materials: 50 parts of cement, 20 parts of high-strength gypsum, 8 parts of polystyrene foam, 25 parts of perlite, and 25 parts of glass beads 7 parts of sodium silicate water glass, 4 parts of chopped fiber, 40 parts of water, 3 parts of retarder, and 5 parts of foaming agent.

[0035] In this embodiment, the preparation method of glass microspheres is as follows: grinding waste glass into glass micropowder with a particle size of 10-15 μm, sending the sieved glass micropowder into a bead forming furnace for spheroidization treatment, and the spheroidized micropowder The beads are bleached to obtain hollow microspheres, and the hollow microspheres are sent to a tempering furnace for tempering treatment, and the required glass microspheres are obtained after the tempering treatment is completed.

[0036] Wherein, the modulus of sodium silicate...

Embodiment 3

[0043] A light insulation board prepared from waste glass. According to the mass parts, the insulation board contains the following raw materials: 45 parts of cement, 17 parts of high-strength gypsum, 6 parts of polystyrene foam, 20 parts of perlite, and 18 parts of glass beads 6 parts of sodium silicate water glass, 3 parts of chopped fiber, 38 parts of water, 2 parts of retarder and 4 parts of foaming agent.

[0044] In this embodiment, the preparation method of glass microspheres is as follows: grinding waste glass into glass micropowder with a particle size of 10-15 μm, sending the sieved glass micropowder into a bead forming furnace for spheroidization treatment, and the spheroidized micropowder The beads are bleached to obtain hollow microspheres, and the hollow microspheres are sent to a tempering furnace for tempering treatment, and the required glass microspheres are obtained after the tempering treatment is completed.

[0045] Wherein, the modulus of sodium silicate ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
modulusaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of a heat insulation material, in particular to a light-weight heat insulation plate prepared from waste and old glass. The heat insulation plate is prepared from the following raw materials of cement, high-intensity gypsum, polystyrene foam, perlite, glass micro beads, sodium silicate water glass, chopped fiber, water, retarding agents and foaming agents, wherein the glass micro beads are toughened hollow micro beads produced from waste and old glass; the used sodium silicate water glass has the modulus being 1.0 to 1.4 and the Baume degree being 45 to 50 degree Be; the chopped fiber is chopped polypropylene fiber; the length of the fiber is 13 to 15 mm; the retarding agents are one kind of protein type retarding agents special for sodium polyphosphate, sodium hexametaphosphate and gypsum; the foaming agents select oxydol. The heat insulation plate ensures the heat insulation and thermal isolation performance; meanwhile, the density of theheat insulation plate is greatly reduced, so that the heat insulation plate has lower transportation cost and construction difficulty. The glass waste materials are used; the advantage of better greeneffect and environment protection are realized.

Description

technical field [0001] The invention relates to the technical field of thermal insulation materials, in particular to a lightweight thermal insulation board prepared from waste glass. Background technique [0002] Thermal insulation board is a kind of building material used in building thermal insulation engineering construction. Compared with ordinary building structural materials, thermal insulation board has better thermal insulation performance, and can play a good role in thermal insulation in the building interior, thereby reducing the energy-saving characteristics of the building. , to reduce the energy consumption of temperature control equipment such as air conditioners and heating; when the insulation board is used for exterior wall construction, it can also improve the waterproof and moisture-proof performance of the building. [0003] Conventional insulation boards include XPS insulation boards, polyurethane insulation boards, cement foam insulation boards, expan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/26C04B14/22C04B111/40
CPCC04B28/26C04B14/22C04B2111/40C04B7/00C04B22/143C04B16/08C04B14/18C04B16/0633C04B22/002C04B22/16C04B22/068C04B24/14
Inventor 武行峰
Owner HEFEI JINTONGWEI LOW TEMPERATURE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com