Low-viscosity perfusion adhesive for repairing concrete crack and preparation method thereof

A crack repair and concrete technology, applied in the field of materials, can solve the problems of poor environmental protection of the slurry, short curing time, large exothermic temperature rise, etc., and achieve the effects of low production cost, excellent flexibility and excellent flexibility.

Active Publication Date: 2018-08-10
中冶武汉冶金建筑研究院有限公司
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the disadvantage of this type of glue is that it uses highly toxic furfural, the slurry is not environmentally friendly, and the environment is polluted by volatilization of the solvent, the heat of curing is large, and problems such as "explosion" are prone to occur; patents CN201110207935.3, CN201010219982. 5. CN201310106305.6 uses a low molecular weight glycidyl ether diluent, which has a very low viscosity and contains epoxy groups that can participate in the reaction of the curing agent. It is usually called a reactive diluent
In addition, although the traditional polyamine curing agent has low initial viscosity, it has the disadvantages of short curing time and large exothermic temperature rise. Before the glue penetrates into the depth of the crack, it will gradually cross-link and consolidate and lose its penetration ability. , often leads to incomplete filling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-viscosity perfusion adhesive for repairing concrete crack and preparation method thereof
  • Low-viscosity perfusion adhesive for repairing concrete crack and preparation method thereof
  • Low-viscosity perfusion adhesive for repairing concrete crack and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Put the cardanol epoxy resin in the baking workshop and heat it up to 80°C within 1 hour, and keep it warm for 8 hours; put the heated cardanol epoxy resin into the mixer, start the mixer, and add surfactant and defoamer in sequence and ester diluent, the feeding time is controlled to be 10 minutes to complete, and then mixed for 10 minutes until uniform, and the A component is prepared. Mixing of component B First mix the curing agent component evenly, then put in the accelerator and coupling agent in turn, and mix evenly.

[0031] Table 1 Example 1 perfusion glue ratio

[0032]

Embodiment 2

[0034] Put the cardanol epoxy resin in the baking workshop and heat it up to 80°C within 1 hour, and keep it warm for 8 hours; put the heated cardanol epoxy resin into the mixer, start the mixer, and add surfactant and defoamer in sequence and ester diluent, the feeding time is controlled to be 10 minutes to complete, and then mixed for 10 minutes until uniform, and the A component is prepared. Mixing of component B First mix the curing agent component evenly, then put in the accelerator and coupling agent in turn, and mix evenly.

[0035] Table 2 Example 2 perfusion glue ratio

[0036]

Embodiment 3

[0038] Put the cardanol epoxy resin in the baking workshop and heat it up to 80°C within 1 hour, and keep it warm for 8 hours; put the heated cardanol into the mixer, start the mixer, and add surfactants, defoamers and esters in sequence For the diluent, the feeding time is controlled to be 10 minutes to complete, and after the feeding is completed, mix for another 10 minutes until it is uniform, and the A component is prepared. Mixing of component B First mix the curing agent component evenly, then put in the accelerator and coupling agent in turn, and mix evenly.

[0039] Table 3 Example 3 perfusion glue ratio

[0040]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low-viscosity perfusion adhesive for repairing a concrete crack and a preparation method thereof. The low-viscosity perfusion adhesive for repairing the concrete crack is prepared from a component A and a component B in a mass ratio of 100 to 3, wherein, in parts by mass, the component A is prepared from 100 parts of cardanol epoxy resin, 1.2 to 9.7 parts of ester thinner, 0.5 to 1 part of surfactant and 1 to 1.5 parts of antifoaming agent; the component B is prepared from 25 to 37 parts of compound amine curing agent, 1 to 3 parts of coupling agent and 1 to 2 parts of accelerant. The cardanol epoxy resin of the low-viscosity perfusion adhesive is low in room-temperature viscosity; as the cardanol has a low-temperature-resistant characteristic, the cardanol epoxyresin is slightly influenced in viscosity by a temperature change, and is particularly suitable to use in a low-temperature environment; the excellent flexible performance is provided for the epoxy resin by the longer carbon chain of the cardanol; when a seam injection adhesive is confected, a flexibilizer can be allowed not to be extra added any more; in addition, a synthetic raw material cashewnut shell liquid of the low-viscosity perfusion adhesive is a potential renewable resource, and the production cost is enabled to tend to cheapness.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a low-viscosity concrete crack repair pouring glue and a preparation method thereof. Background technique [0002] Epoxy joint injection glue is a multi-component solution type pouring material mixed with epoxy resin as the main agent, supplemented with diluent, toughener, surfactant and curing agent. The cured epoxy joint glue has good bonding properties, excellent base adaptability and good mechanical strength, and is widely used in concrete structure crack filling repair and reinforcement projects. [0003] Under the action of external pressure, epoxy joint glue can penetrate and fill into the cracks of the structure, and its own viscosity will directly affect the filling depth and filling degree of the glue in the process of crack repair, and then affect the effect of repair . Usually, the effect of reducing the viscosity of the glue is achieved by adding a di...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J163/00C09J11/06C09J11/08C08G59/50
CPCC08G59/5006C08G59/5013C09J11/06C09J11/08C09J163/00C08L83/12C08K5/544
Inventor 周紫晨曾明张冰王智罗英杰
Owner 中冶武汉冶金建筑研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com