Wrought magnesium alloy material with low cost, high performance and heat resistance, and preparation method thereof
A deformed magnesium alloy and heat-resistant deformation technology, applied in the field of metal materials, can solve the problems of high cost of raw materials and limited application range, and achieve the effects of high commercial value, simple preparation and processing technology, and low cost
Inactive Publication Date: 2018-08-10
XIANGTAN UNIV
View PDF3 Cites 15 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, these newly developed alloy systems are generally constrained by practical problems such as high cost of raw materials, preparation and processing, and plastic deformation, which greatly limits the scope of application.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0054] Embodiment 1: The alloy composition (mass percentage) is: Zn is 6.5%, Sn is 4.0%, Mn is 1.0%, and the remainder is magnesium and unavoidable impurities.
Embodiment 2
[0055] Embodiment 2: The alloy composition (mass percentage) is: Zn is 6.5%, Sn is 4.0%, Cu is 0.5%, Mn is 1.0%, and the remainder is magnesium and unavoidable impurities.
Embodiment 3
[0056] Embodiment 3: The alloy composition (mass percentage) is: Zn is 6.5%, Sn is 4.0%, Cu is 1%, Mn is 0.75%, and the remainder is magnesium and unavoidable impurities.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Property | Measurement | Unit |
---|---|---|
tensile strength | aaaaa | aaaaa |
elongation | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
Login to view more
Abstract
The invention provides a wrought magnesium alloy material with low cost, a high performance and heat resistance, and a preparation method thereof. The wrought magnesium alloy material is prepared fromthe chemical components in percentage by weight: 4.0 to 9.0 percent of Zn, 0.5 to 8 percent of Sn, 0.1 to 5 percent of Cu, 0.5 to 2 percent of Mn, and the balance magnesium and inevitable impurities.According to the wrought magnesium alloy material with the low cost, the high performance and the heat resistance, and the preparation method thereof provided by the invention, the problems that an existing high-strength heat-resistant wrought magnesium alloy material uses a rare earth element and a high-price alloy material, so that complicated processes such as large plastic deformation (rapidsolidification, powder metallurgy and the like) are higher in cost and the like are solved; and the element components of the alloy are reasonably blended, a conventional smelting and casting processis adopted, and reasonable heat treatment process conditions are selected after conventional plastic deformation and forming, so that the wrought magnesium alloy material with an excellent mechanicalproperty and a performance being remarkably superior to a high-strength ZK60 wrought magnesium alloy can be obtained. The wrought magnesium alloy material provided by the invention has the characteristics of low cost, high performance, no rare earth, and excellent high temperature and room temperature properties, and has a great application prospect.
Description
technical field [0001] The invention relates to a metal material, which belongs to the field of magnesium alloy production in nonferrous metals, in particular to a high-performance heat-resistant deformation magnesium alloy material. Background technique [0002] As the lightest metal structural material, magnesium alloy has the advantages of high specific strength, high specific stiffness, high damping and vibration reduction, thermal and electrical conductivity, and excellent electromagnetic shielding performance. It has become an important research direction for an economical society. Magnesium alloys are divided into cast magnesium alloys and wrought magnesium alloys. The currently used magnesium alloy products are mainly cast magnesium alloys. However, magnesium alloy casting products have many defects, low mechanical properties, poor reliability and other shortcomings, which limit its application range. Compared with cast magnesium alloys, wrought magnesium alloys hav...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C23/04C22C1/03C22F1/06
CPCC22C1/03C22C23/04C22F1/002C22F1/06
Inventor 齐福刚罗文忠叶芝松赵镍史子一曹红帅刘应都欧阳晓平
Owner XIANGTAN UNIV
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap