Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Cationic self-matting resin, and preparation method and application thereof

A cationic, self-extinguishing technology, used in coatings, polyurea/polyurethane coatings, etc., to reduce crystallinity, improve film-forming properties, and reduce particle size fluctuations

Active Publication Date: 2018-09-18
WANHUA CHEM GRP CO LTD
View PDF18 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In view of the fact that there is no research report on cationic self-extinction resin, it is necessary to develop and prepare a cationic self-extinction resin, which can overcome the defects in the prior art and has excellent self-extinction effect. of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cationic self-matting resin, and preparation method and application thereof
  • Cationic self-matting resin, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0087] A kind of cationic self-dulling resin, the weight parts of raw materials are composed of:

[0088] 7.8 parts of isocyanate (the molar ratio of IPDI to HDI is 2:1),

[0089] Macromolecule polyol (PTMG1000) 14.0 parts,

[0090] 0.11 parts of monohydric alcohol and / or dihydric alcohol (MPEG1200) containing polyoxyethylene segment in main chain and / or side chain,

[0091] 0.37 parts of diamine cationic hydrophilic chain extender (HBAAP),

[0092] Small molecule diamine chain extender (EDA and EDA-OH) 1.73 parts,

[0093] Catalyst (organic bismuth 8108) 0.0022 parts,

[0094] 32.9 parts of solvent (acetone),

[0095] 56.0 parts of deionized water,

[0096] Neutralizing agent (acetic acid) 0.1 parts.

[0097] Above-mentioned cationic self-extinction resin, the preparation method is:

[0098] (1) Add 140 grams of PTMG1000 into a four-necked flask with a condenser and a stirrer, then add 31 grams of IPDI and 47 grams of HDI, 0.022g of organic bismuth 8108, 22 grams of ac...

Embodiment 2

[0104] 5.3 parts of isocyanate (IPDI, TDI, HDI),

[0105]Macromolecule polyol (PTMG1000) 11.7 parts,

[0106] 0.11 parts of monohydric alcohol and / or dihydric alcohol (MPEG1200) containing polyoxyethylene segment in main chain and / or side chain,

[0107] 0.37 parts of diamine cationic hydrophilic chain extender (HBAAP),

[0108] Small molecule diamine chain extender (EDA) 0.98 parts,

[0109] Catalyst (organic bismuth 8108) 0.00164 parts,

[0110] Solvent (acetone) 29.1 parts,

[0111] 43.1 parts of deionized water,

[0112] Neutralizing agent (acetic acid) 0.1 parts.

[0113] Above-mentioned cationic self-extinction resin, the preparation method is:

[0114] (1) Add 117 grams of PTMG1000 to a four-necked flask with a condenser and a stirrer, then add 23 grams of IPDI, 6 grams of TDI and 24 grams of HDI, 0.0164 grams of organic bismuth 8108, 17 grams of acetone, and heat at 85 ° C After reacting for 1.5 hours, the NCO value was 7.3% (theoretical value was 7.36%), and a ...

Embodiment 3

[0120] 10.2 parts of isocyanate (HMDI and HDI),

[0121] Macromolecule polyol (PTMG1000) 20.0 parts,

[0122] 0.33 parts of monohydric alcohols and / or dihydric alcohols (MPEG1200) containing polyoxyethylene segments in the main chain and / or side chains,

[0123] 0.93 part of dibasic amine cationic hydrophilic chain extender (HBAAP),

[0124] Small molecule diamine chain extender (IPDA and EDA-OH) 3.2 parts,

[0125] Catalyst (organic bismuth 8108) 0.003 part,

[0126] Solvent (acetone) 51.9 parts,

[0127] 80.9 parts of deionized water,

[0128] Neutralizing agent (acetic acid) 0.254 parts.

[0129] Above-mentioned cationic self-extinction resin, the preparation method is:

[0130] (1) Add 200 grams of PTMG1000 into a four-necked flask with a condenser and a stirrer, then add 31 grams of HMDI and 71 grams of HDI, 0.03 grams of organic bismuth 8108, 31 grams of acetone, and react at 85 ° C for 1.5 hours, The NCO value is 8.7% (theoretical value is 8.61%), resulting in di...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cationic self-matting resin, and a preparation method and application thereof. The cationic self-matting resin comprises isocyanate, a diamine cationic hydrophilic chain extender, macropolyol, monohydric alcohol and / or dihydric alcohol with the main chain and / or the side chain containing a polyoxyethylene chain, a small molecular diamine chain extender, a catalyst, a solvent and a neutralizing agent. The preparation method has the advantages of simple process, convenience in operation, safety and non-toxicity, and the obtained cationic self-matting resin has the advantages of small particle size fluctuation, good emulsion stability and resistance, good adhesion to anionic leather, glass and other substrates, and bringing of soft and smooth hand feeling and naturalrich appearance for leather, and can be widely applied to the fields of leather finishing, wood plastics, paper printing, printing and dying inks, printing coatings, packaging coatings and matt nailpolish.

Description

technical field [0001] The invention belongs to the technical field of cationic self-extinction resin preparation, and relates to a cationic self-extinction resin and its preparation method and application. Background technique [0002] Water-based polyurethane has the characteristics of non-toxicity, flexibility, environmental protection, and easy modification due to its use of water as the medium. Under the premise of today's increasingly high environmental protection requirements, water-based polyurethane is widely used in textile coatings, wood, architectural coatings, metals, adhesives and leather. With the development of society and the continuous improvement of aesthetics, the pursuit of self-extinction or matte is becoming more and more vigorous. At present, there are mainly two methods to achieve the effect of extinction: external addition method and self-extinction. Among them, the external addition method mainly achieves the matting effect by adding matting powd...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G18/66C08G18/32C08G18/48C09D175/08
CPCC08G18/3228C08G18/3271C08G18/3275C08G18/4833C08G18/4854C08G18/6674C08G18/6685C08G18/6688C09D175/08
Inventor 周操赵炳炎张洁韩克
Owner WANHUA CHEM GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com