Modified similar material and preparation method thereof

A similar material and modified technology, which is applied in the field of geomechanical model similar materials and its preparation, can solve the problems of small adjustable range of elastic modulus, reduced volume, small ultimate compressive strength and tensile strength, and achieve physical The effect of maintaining stable mechanical properties

Inactive Publication Date: 2018-09-25
NORTH CHINA UNIVERSITY OF TECHNOLOGY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] At present, there are many kinds of similar materials used in similar tests, such as paraffin wax, pure gypsum, gypsum diatomite mixed simulation materials, cement pumice mixture, etc. Although these similar materials have played a certain role in specific tests, but, There are still many disadvantages, such as paraffin, which requires a certain temperature to be applied when making test pieces, and is inconvenient to operate, so it is not commonly used; the modulus of elasticity of gypsum can be adjusted in a small range, and the ratio of ultimate compressive strength to tensile strength It is too small, so its application range is limited; similar materials made of gypsum, diatomaceous earth and water will shrink in volume as the amount of diatomite added increases.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified similar material and preparation method thereof
  • Modified similar material and preparation method thereof
  • Modified similar material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] In the three-necked flask that stirrer is equipped with, add 500g formula Ia compound (AR, purchased from Dow-Corning Company) and 60g formula Ib (AR, purchased from Liaoning Province organosilicon resin factory) compound, inert gas protection, start stirring device And raise the temperature to 110°C. After the two are mixed evenly, add 3g of titanium tetrachloride-triethylaluminum, control the rotation speed at 600r / min, stir and react for 10 hours, stop stirring, and obtain R as a polymer of methyl Object Ic.

[0040]

[0041] Ia

[0042] +

[0043]

[0044] Ib

[0045] ↓

[0046]

[0047] IC

[0048] where M w 1.22×10 4 ,M n 4.52×10 3 , The molecular weight distribution index is 2.6.

Embodiment 2

[0050] First, mix 100 parts of barite powder with a particle size of 200 mesh and 0.015 parts of polymer of formula Ic evenly, then dry at 90°C for 3 hours to remove water, take it out and cool to room temperature; add 4 parts of No. 32 hydraulic machine oil to the dried Mix the barite powder and the polymer of formula Ic evenly, and then crush the mixed material until its particle size is ≤1mm; add 1.8 parts of cement marked 525 to the barite powder, the polymer of formula Ic and No. 32 hydraulic machine oil In the mixture, continue to mix evenly; finally add 2 parts of water to the above mixture, and mix evenly. The material has a compressive strength of 0.76 MPa and a modulus of deformation of 12.1 MPa.

Embodiment 3

[0052] First mix 100 parts of barite powder with a particle size of 200 mesh and 0.013 parts of polymer of formula Ic evenly, then dry at 90°C for 3 hours to remove water, take it out and cool to room temperature; add 4 parts of No. 32 hydraulic machine oil to the dried Mix the barite powder and the polymer mixture of formula Ic evenly, and then crush the mixed material to a particle size ≤ 1mm; add 1 part of cement marked 425 to the barite powder, polymer formula Ic and No. 32 hydraulic press In the oil mixture, continue to mix well; finally add 2.5 parts of water to the above mixture, and mix well. The material has a compressive strength of 0.98MPa and a modulus of deformation of 12.8MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
compressive strengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a modified similar material and a preparation method thereof, wherein the modified material comprises barite powder, cement, water, 32# hydraulic oil and a specific polymer represented by a formula I. According to the present invention, the modified similar material can simulate various rock bodies, and has characteristics of wide raw material source and no toxic-side effect, and the preparation method has characteristics of simple preparation process, low energy consumption, high preparation efficiency and low cost.

Description

technical field [0001] The invention relates to a similar material and a preparation method thereof, in particular to a geomechanical model similar material suitable for simulating rock masses and a preparation method thereof. Background technique [0002] The similar simulation test is a test method that uses a model instead of a prototype to conduct test research according to a certain geometric and physical relationship, and uses the research results for the prototype. It is an important scientific research method. It is to make a model similar to the prototype in the laboratory according to the similarity principle, observe the internal force parameters and their distribution laws of the model with the help of test instruments, and use the results of the research on the model to infer the possibility of the prototype. The mechanical phenomena that occur and the law of rock mass pressure distribution can solve practical problems in rock mass engineering production. This ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C08G81/00
CPCC04B28/04C08G81/00C04B24/42C04B14/368C04B22/002C04B24/00
Inventor 宋志飞秦金雷邹杰徐勇
Owner NORTH CHINA UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com