A kind of tea dregs permeable brick and preparation method thereof

A technology for permeable bricks and tea residues, applied in the field of tea residue permeable bricks and the preparation thereof, can solve the problems of unsatisfactory service life, heavy weight and high cost of permeable bricks, overcome the reduction of brick body friction, improve water permeability, reduce The effect of preparation cost

Active Publication Date: 2020-12-22
贵州省凤冈县浪竹有机茶业有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] There are ceramic and non-ceramic permeable bricks that are impervious to water. Their permeable function is realized by the joints between bricks when they are paved or patched together. The single impermeable ceramic permeable bricks are ceramic bricks of different colors. The blocks are combined and pasted on a special resin board according to certain specifications. Like a mosaic, there are supporting feet under the resin board so that the water leaking from the joints of the bricks can seep into the ground to achieve the purpose of water permeability. Bricks are convenient to lay and replace, and pattern combinations are easier to realize, but the permeable bricks are heavy in weight, high in cost and unsatisfactory in service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of tea dregs permeable brick and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of tea dregs permeable brick, with tea dregs A, coal gangue, halloysite, acrylic resin, carboxymethyl cellulose, water reducing agent, water as the base material, and tea dregs B, waste glass, acrylic resin, carboxymethyl Base cellulose, water reducing agent and water are the fabric; the weight percentages of the base material and the fabric are respectively: 90% and 10%.

[0027] The raw materials of the base material are calculated in parts by weight: 20 kg of tea residue A, 14 kg of coal gangue, 11 kg of halloysite, 3 kg of acrylic resin, 1 kg of carboxymethyl cellulose, 1 kg of water reducing agent, and 5 kg of water.

[0028] The raw materials of the fabric are calculated in parts by weight: 10 kg of tea residue B, 15 kg of waste glass, 1 kg of acrylic resin, 0.5 kg of carboxymethyl cellulose, 0.5 kg of water reducer, and 5 kg of water.

[0029] The particle diameter of the base material is 0.1mm, and the particle diameter of the fabric is 0.5mm.

[0030] T...

Embodiment 2

[0041] A kind of tea dregs permeable brick, with tea dregs A, coal gangue, halloysite, acrylic resin, carboxymethyl cellulose, water reducing agent, water as the base material, and tea dregs B, waste glass, acrylic resin, carboxymethyl Base cellulose, water reducing agent and water are the fabric; the weight percentages of the base material and the fabric are respectively: 70% and 30%.

[0042] The raw materials of the base material are calculated in parts by weight: 40 kg of tea residue A, 19 kg of coal gangue, 16 kg of halloysite, 7 kg of acrylic resin, 2 kg of carboxymethyl cellulose, 2 kg of water reducer, and 10 kg of water.

[0043] The fabric raw materials are calculated in parts by weight: 20 kg of tea residue B, 25 kg of waste glass, 3 kg of acrylic resin, 1 kg of carboxymethyl cellulose, 1 kg of water reducing agent, and 10 kg of water.

[0044] The particle diameter of the base material is 1 mm, and the particle diameter of the fabric is 2 mm.

[0045] The particle...

Embodiment 3

[0055] A kind of tea dregs permeable brick, with tea dregs A, coal gangue, halloysite, acrylic resin, carboxymethyl cellulose, water reducing agent, water as the base material, and tea dregs B, waste glass, acrylic resin, carboxymethyl Base cellulose, water reducing agent and water are fabrics; the weight percentages of the bottom material and fabric are respectively: 84%, 16%.

[0056] The base material raw materials are calculated in parts by weight: 25 kg of tea residue A, 18 kg of coal gangue, 14 kg of halloysite, 6 kg of acrylic resin, 2 kg of carboxymethyl cellulose, 1.5 kg of water reducer, and 7 kg of water.

[0057] The raw materials of the fabric are calculated in parts by weight: 18 kg of tea residue B, 20 kg of waste glass, 2 kg of acrylic resin, 0.8 kg of carboxymethyl cellulose, 0.7 kg of water reducer, and 9 kg of water.

[0058] The particle diameter of the base material is 0.5 mm, and the particle diameter of the fabric is 1 mm.

[0059] The weight percentage...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The present invention belongs to the technical field of water-permeable bricks, and more particularly relates to a tea residue based water-permeable brick and a preparation method thereof. Tea residue, coal gangue, halloysite, acrylic resin, carboxymethyl cellulose, a water reducer and water as prime materials are mixed with tea residue, waste glass, acrylic resin and carboxymethyl cellulose, a water reducer and water as coating materials in a particular ratio and stirred uniformly. The mixture is placed in a forming mold, subjected to steam curing and then prepared into a water-permeable brick with good water permeability, high strength and low shrinkage. Meanwhile, the water-permeable brick also has excellent wear resistance and crack resistance with prolonged product service life.

Description

technical field [0001] The invention belongs to the technical field of permeable bricks, in particular to a tea dregs permeable brick and a preparation method thereof. Background technique [0002] At present, the permeable bricks seen on the market can be divided into two categories in terms of materials and production processes. One is made of solid industrial waste, domestic waste and construction waste as the main raw materials through crushing, molding and high-temperature refining. The building decoration materials that have the performance of permeable bricks and meet the standards of permeable bricks are called ceramic permeable bricks; the other type is made of inorganic non-metallic materials as the main raw material, and is made by forming and curing with organic or inorganic binders. , because it does not need to be fired, it is called non-ceramic permeable brick. [0003] There are ceramic and non-ceramic permeable bricks that are impervious to water. Their per...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/28C04B38/00C04B40/02C04B111/20C04B111/60
CPCC04B26/285C04B2111/00017C04B2111/00284C04B2111/20C04B2111/2038C04B2111/60C04B2201/50C04B18/248C04B18/12C04B24/2641C04B14/10C04B2103/302C04B38/0041C04B40/0245C04B18/0427
Inventor 陈其波
Owner 贵州省凤冈县浪竹有机茶业有限公司